Search

SUMMARY Purpose: This study aimed to characterize and analyze the number of voids and the percentage of void volume within and between the layers of class II composite restorations made using the bulk fill technique or the incremental technique by optical coherence tomography (OCT). Methods and Materials: Class II cavities (4×4×2 mm) were prepared in 48 human third molars (n=24 restorations per group, two class II cavities per tooth). Teeth were divided into four groups and restored as follows: group 1 (FOB), bulk filled in a single increment using Filtek One Bulk Fill (3M Oral Care); group 2 (FXT), incrementally filled using four oblique layers of Filtek Z350 XT (3M Oral Care); group 3 (FBF+FXT), bulk filled in a single increment using Filtek Bulk Fill Flowable Restorative (3M Oral Care) covered with two oblique layers of Filtek Z350 XT (3M Oral Care), and group 4 (FF+FXT), incrementally filled using Filtek Z350 XT Flow (3M Oral Care) covered with two oblique layers of Filtek Z350 XT (3M Oral Care). After the restorative procedure, specimens were immersed into distilled water and stored in a hot-air oven at 37°C. Forty-eight hours later, thermal cycling was conducted (5000 cycles, 5°C to 55°C). Afterward, OCT was used to detect the existence of voids and to calculate the number of voids and percentage of voids volume within each restoration. Data were submitted to chi-square and Kruskal-Wallis tests (α=0.05). Comparisons were made using the Dunn method. Results: Voids were detected in all groups, ranging from 0.000002 (FBF+FXT and FF+FXT) to 0.32 mm3 (FBF+FXT). FF + FXT presented voids in all of the restorations and had a significantly higher number of voids per restoration when compared to the other groups (p Conclusions: The use of flowable resin-based composites can result in an increased number of voids and percentage of voids volume in restorations, and this appears to be more related to voids present inside the syringe of the material than to the use of incremental or bulk fill restorative techniques.

SUMMARY Objectives: This study evaluated the effect of toothbrushing with a dentifrice on gloss, roughness profile, surface roughness, and wear of conventional and bulk-fill resin-based composites. Methods and Materials: Gloss and surface roughness of resin-based composites (RBCs; Admira Fusion X-tra, Aura Bulk Fill, Filtek Bulk Fill Flowable, Filtek Bulk Fill Posterior Restorative, Filtek Supreme Ultra, Herculite Ultra, Mosaic Enamel, SDR flow+, Sonic Fill 2, Tetric EvoFlow Bulk Fill and Tetric EvoCeram Bulk Fill) were analyzed before and after brushing; the roughness profile and wear were also determined after toothbrushing. Representative three-dimensional images of the surface loss and images comparing the unbrushed and brushed surfaces were also compared. Analysis of variance and Tukey post hoc tests were applied (α=0.05) to the gloss, surface roughness, roughness profile, and surface loss data. Pearson's correlation test was used to determine the correlation between gloss and surface roughness, surface loss and percentage of gloss decrease after brushing, and surface loss and surface roughness after brushing. Results: For all RBCs tested after 20,000 brushing cycles, the gloss was reduced and the surface roughness increased (p Conclusions: Toothbrushing with a dentifrice reduced the gloss, increased the surface roughness, and caused loss at the surface of all the RBCs tested. Considering all the properties tested, Mosaic Enamel exhibited excellent gloss retention and a low roughness profile and wear, while Admira Fusion X-tra exhibited the greatest decrease in gloss, the highest roughness profile, and the most wear.