Te4+-doped Cs2ZrCl6 vacancy-ordered perovskites with excitation wavelength-dependent tunable color have been synthesised by a simple precipitation method at room temperature, with two luminescent centres originating from the Te4+ and the STE (self-trapping exciton) of the Cs2ZrCl6 itself, respectively. They exhibit two different emission characteristics at 254 nm and 365 nm excitation wavelengths. At an excitation wavelength of 254 nm, the emission characteristics allow Te4+-doped Cs2ZrCl6 to exhibit tunable emission from blue to white to yellow under the control of Te4+ doping. And the excitation wavelength of 365 nm shows yellow emission. Te4+ doped Cs2ZrCl6 phosphors were used for optical anti-counterfeiting, and the anti-counterfeiting patterns were well distinguished under 254 nm and 365 nm UV lamps, demonstrating the potential of this excitation wavelength-dependent tunable color material for optical anti-counterfeiting applications. [ABSTRACT FROM AUTHOR]

The optical properties of Mn4+-activated phosphors are heavily affected by the host and the related data are difficult to obtain, which makes quantitative design of novel phosphors with required wavelength particularly challenging. In the era of big data, computation is emerging as a vital complement to materials development. Compared with traditional calculation routes, machine learning (ML) models provide better solutions for the problems wherein understanding the underlying physics is complicated with sparse data. In this study, we developed six ML models based on a sparse and small data set to rapidly predict the peak emission wavelength of novel phosphors and use Recursive Feature Elimination (RFE) to select the best features. Among them, the K-nearest neighbors regression (KNN.r) algorithm using non-parametric regression technology can predict the value of the target variable based on the similarity between the target value and its spatial neighbors, which can tackle sparse data sets with no obvious linear relationship well and has the best prediction accuracy. These models were then used to predict 278 potential Mn4+-activated phosphor hosts extracted from the inorganic crystal structure database (ICSD), and 19 samples were selected to validate these methods. In order to overcome the lack of physical and chemical insight of KNN, a visual data analysis was carried out based on hierarchical clustering analysis (HCA), and the rule between the peak emission wavelength and the structure of host was proposed. Guided by the results of KNN and HCA, six samples were selected for the synthesis and characterization to verify our conclusions. The measured values of all these phosphors exhibit good agreement with the predicted results, suggesting the success of our methodology. Thus, the model established and the rule proposed in this paper provide a new pathway for the rapid discovery of novel phosphors. [ABSTRACT FROM AUTHOR]