Search

Single-electron transistors (SETs) represent a new generation of electronic devices with high charge sensitivity, high switching speed, and low power consumption. Here a simple and controlled fabrication of graphene quantum dot (GQD)-based SETs for photon detectors has been demonstrated. The plasma-synthesized GQDs exhibit stable photoluminescence and are successfully used as the Coulomb islands between heteroepitaxial spherical-gold/platinum (HS-Au/Pt) nanogap electrodes. The as-fabricated GQD-SETs enable photon detection with 410 nm excitation owing to the ability of GQDs to generate photoluminescence emission.

We show the control of a charging energy in chemically assembled nanoparticle single-electron transistors (SETs) by altering the core diameter of Au nanoparticles. The charging energy is a fundamental parameter that decides the operating temperature of SETs. Practical application of SETs requires us to regulate the value of the charging energy by tuning the diameter of quantum dots. In this study, we used 3.0, 5.0 and 6.2 nm diameter synthesized Au nanoparticles as a quantum dot in the SETs. The total capacitances and charging energy of the SETs were evaluated from the rhombic Coulomb diamonds attributed to a single Coulomb island. The capacitance and charging energy matched with a concentric sphere model much better than with a simple sphere model. The operating temperatures of the SETs suggested that a charging energy 2.2 times greater than the thermal energy was required for stable operation, in theory. These results will help us to select an appropriate core diameter for the Au nanoparticles in practical SETs.

Coulomb blockade behaviors in individual Au nanoparticles of 2 nm core diameter in double-barrier structures have been studied by means of noncontact atomic force spectroscopy (NC-AFS) at room temperature. The Au nanoparticles with a 1-decanethiol ligand were chemisorbed by 1,10-decanedithiol molecules of a mixed 1-octanethiol/1,10-decanedithiol self-assembled monolayer coated on a Au(111) surface; these particles were observed through NC-AFS. NC-AFS measurements of the cantilever frequency shift-sample voltage (Δf-V(S)) curves were sequentially conducted on three Au nanoparticles under the same experimental conditions; the Δf-V(S) curves were found to deviate from the parabolic (Δf(N)) curve in the cases where no extra charge existed on the Au core. The experimental Δf(CB)(=Δf-Δf(N)) and Δf(CB)/V curves agree well with the theoretical curves obtained using a golden-rule calculation and the same parabolic parameters. All the results, through NC-AFS, suggest Coulomb blockade behaviors in the Au nanoparticles at room temperature.

We report the fabrication of nickel nanospaced electrodes by electroplating and electromigration for nanoelectronic devices. Using a conventional electrochemical cell, nanogaps can be obtained by controlling the plating time alone and after a careful optimization of electrodeposition parameters such as electrolyte bath, applied potential, cleaning, etc. During the process, the gap width decreases exponentially with time until the electrode gaps are completely bridged. Once the bridge is formed, the ex situ electromigration technique can reopen the nanogap. When the gap is ∼1 nm, tunneling current–voltage characterization shows asymmetry which can be corrected by an external magnetic field. This suggests that charge transfer in the nickel electrodes depends on the orientation of magnetic moments. (Some figures in this article are in colour only in the electronic version)