Search

Hf0.5Zr0.5O2 (HZO) thin films are promising candidates for non-volatile memory and other related applications due to their demonstrated ferroelectricity at the nanoscale and compatibility with Si processing. However, one reason that HZO has not been fully scaled into industrial applications is due to its deleterious wake-up and fatigue behavior which leads to an inconsistent remanent polarization during cycling. In this study, we explore an interfacial engineering strategy in which we insert 1 nm Al2O3 interlayers at either the top or bottom HZO/TiN interface of sequentially deposited metal-ferroelectric-metal capacitors. By inserting an interfacial layer while limiting exposure to the ambient environment, we successfully introduce a protective passivating layer of Al2O3 that provides excess oxygen to mitigate vacancy formation at the interface. We report that TiN/HZO/TiN capacitors with a 1 nm Al2O3 at the top interface demonstrate a higher remanent polarization (2Pr ∼ 42 μC cm−2) and endurance limit beyond 108 cycles at a cycling field amplitude of 3.5 MV cm−1. We use time-of-flight secondary ion mass spectrometry, energy dispersive spectroscopy, and grazing incidence x-ray diffraction to elucidate the origin of enhanced endurance and leakage properties in capacitors with an inserted 1 nm Al2O3 layer. We demonstrate that the use of Al2O3 as a passivating dielectric, coupled with sequential ALD fabrication, is an effective means of interfacial engineering and enhances the performance of ferroelectric HZO devices.

Ferroelectric random-access memory (FRAM) based on conventional ferroelectric materials is a non-volatile memory with fast read/write operations, high endurance, and 10 years of data retention time. However, it suffers from destructive read-out operation and lack of CMOS compatibility. HfO

Ferroelectric random-access memory (FRAM) based on conventional ferroelectric materials is a non-volatile memory with fast read/write operations, high endurance, and 10 years of data retention time. However, it suffers from destructive read-out operation and lack of CMOS compatibility. HfO2-based ferroelectric tunnel junctions (FTJ) may compensate for the shortcomings of FRAM by its CMOS compatibility, fast operation speed, and non-destructive readout operation. In this study, we investigate the effect of ferroelectric and interface film thickness on the tunneling electroresistance or ON/OFF current ratio of the Hf0.5Zr0.5O2/Al2O3based FTJ device. Integrating a thick ferroelectric layer (i.e. 12 nm Hf0.5Zr0.5O2) with a thin interface layer (i.e. 1 nm Al2O3) resulted in an ON/OFF current ratio of 78. Furthermore, to elucidate the relationship between ON/OFF current ratio and interfacial properties, the Hf0.5Zr0.5O2-Al2O3films and Ge-Al2O3interfaces are examined via time-of-flight secondary ion mass spectrometry depth profiling mode. A bilayer oxide heterostructure (Hf0.5Zr0.5O2/Al2O3) is deposited by atomic layer deposition (ALD) on the Ge substrate. The ON/OFF current ratio is enhanced by an order of magnitude when the Hf0.5Zr0.5O2film deposition mode is changed from exposure (H2O) ALD to sequential plasma (sequential O2-H2) ALD. Moreover, the interfacial engineering approach based on thein situALD H2-plasma surface pre-treatment of Ge increases the ON/OFF current ratio from 9 to 38 by reducing the interfacial trap density state at the Ge-Al2O3interface and producing Al2O3with fewer oxygen vacancies as compared to the wet etch (HF + H2O rinse) treatment of the Ge substrate. This study provides evidence of strong coupling between Hf0.5Zr0.5O2and Al2O3films in controlling the ON/OFF current ratio of the FTJ.