Search

Piezoelectric fibers have an important role in wearable technology as energy generators and sensors. A series of hybrid nanocomposite piezoelectric fibers of polyinylidene fluoride (PVDF) loaded with barium-titanium oxide (BT) and reduced graphene oxide (rGO) were prepared via the melt spinning method. Our previous studies show that high-performance fibers with 84% of the electroactive β-phase in the PVDF generated a peak output voltage up to 1.3 V and a power density of 3 W kg -1 . Herein, the dynamic mechanical and creep behavior of these fibers were investigated to evaluate their durability and piezoelectric performance. Dynamic mechanical analysis (DMA) was used to provide phenomenological information regarding the viscoelastic properties of the fibers in the longitudinal direction. DSC and SEM were employed to characterize the crystalline structure of the samples. The storage modulus and the loss tangent increased by increasing the frequency over the temperature range (-50 to 150 °C) for all of the fibers. The storage modulus of the PVDF/rGO nanocomposite fibers had a higher value (7.5 GPa) in comparison with other fibers. The creep and creep recovery behavior of the PVDF/nanofillers in the nanocomposite fibers have been explored in the linear viscoelastic region at three different temperatures (10-130 °C). In the PVDF/rGO nanocomposite fibers, strong sheet/matrix interfacial interaction restricted the mobility of the polymer chains, which led to a higher modulus at temperatures 60 and 130 °C.

The ubiquity of wearables, coupled with the increasing demand for power, presents a unique opportunity for nanostructured fiber-based mobile energy storage systems. When designing wearable electronic textiles, there is a need for mechanically flexible, low-cost and light-weight components. To meet this demand, we have developed an all-in-one fiber supercapacitor with a total thickness of less than 100 μm using a novel facile coaxial wet-spinning approach followed by a fiber wrapping step. The formed triaxial fiber nanostructure consisted of an inner poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) core coated with an ionically conducting chitosan sheath, subsequently wrapped with a carbon nanotube (CNT) fiber. The resulting supercapacitor is highly flexible, delivers a maximum energy density 5.83 Wh kg -1 and an extremely high power of 1399 W kg -1 along with remarkable cyclic stability and specific capacitance. This asymmetric all-in-one fiber supercapacitor may pave the way to a future generation of wearable energy storage devices.

Novel nanostructured hybrid electrospun polyacrylonitrile (PAN) yarns with different graphene ratios were prepared using liquid crystal graphene oxide (LCGO) and PAN. It was found that the well-dispersed LCGO were oriented along the fiber axis in an electrified thin liquid jet during electrospinning. The graphene oxide sheets were well dispersed in the polar organic solvent, forming nematic liquid crystals upon increasing concentration. Twisted nanofibers were produced from aligned nanofibrous mats prepared by conventional electrospinning. It was found that the mechanical properties of the twisted nanofiber yarns increased even at very low LCGO loading. This research offers a new approach for the fabrication of continuous, strong, and uniform twisted nanofibers which could show promise in developing a novel carbon fiber precursor., Competing Interests: The authors declare no conflict of interest.