The main task of this work is to study the tribological performance of nanolubricants formed by trimethylolpropane trioleate (TMPTO) base oil with magnetic nanoparticles coated with oleic acid: Fe3O4 of two sizes 6.3 nm and 10 nm, and Nd alloy compound of 19 nm. Coated nanoparticles (NPs) were synthesized via chemical co-precipitation or thermal decomposition by adsorption with oleic acid in the same step. Three nanodispersions of TMPTO of 0.015 wt% of each NP were prepared, which were stable for at least 11 months. Two different types of tribological tests were carried out: pure sliding conditions and rolling conditions (5% slide to roll ratio). With the aim of analyzing the wear by means of the wear scar diameter (WSD), the wear track depth and the volume of the wear track produced after the first type of the tribological tests, a 3D optical profiler was used. The best tribological performance was found for the Nd alloy compound nanodispersion, with reductions of 29% and 67% in friction and WSD, respectively, in comparison with TMPTO. On the other hand, rolling conditions tests were utilized to study friction and film thickness of nanolubricants, determining that Fe3O4 (6.3 nm) nanolubricant reduces friction in comparison to TMPTO. [ABSTRACT FROM AUTHOR]

This study presents an effective magnetic separation method for cadmium removal, based on the use of a novel nanostructured material as an adsorbent. This adsorbent involves the incorporation of magnetite nanoparticles (Fe3O4-NPs), synthesized by the reverse coprecipitation method, into sodium alginate and activated carbon to form spherical structures by crosslinking Ca2+ ions with the charged alginate chains, referred to as magnetic alginate activated carbon (MAAC) beads. The effect of the experimental parameters, such as pH, contacting time, adsorbent dosage, agitation type, and rotating speed were investigated and optimized for an efficient removal of Cd(II) ions at an initial concentration of 250 mg/L. The amount of adsorbed Cd(II) by MAAC beads increased at a pH of 6 with a removal efficiency over 90%. The maximum adsorption capacity reached was 70 mg/g of adsorbent at an initial Cd(II) concentration of 150 mg/L, whereas at 250 mg/L the adsorption capacity lowered until 60 mg/g. Sorption isotherms were calculated using Langmuir, Freundlich, Temkin, and Dubinin–Radushkevich equations, and were better described by the Freundlich and Temkin models. These results proved the removal efficiency and the potential use under real environmental conditions of the MAAC beads, due to their easy recovery from contaminated aqueous solutions. [ABSTRACT FROM AUTHOR]