A new nano-silica/chitosan (SiO2/CS) sorbent was created using a wet process to eliminate uranium(VI) from its solution. Measurements using BET, XRD, EDX, SEM, and FTIR were utilized to analyze the production of SiO2/CS. The adsorption progressions were carried out by pH, SiO2/CS dose, temperature, sorbing time, and U(VI) concentration measurements. The optimal condition for U(VI) sorption (165 mg/g) was found to be pH 3.5, 60 mg SiO2/CS, for 50 min of sorbing time, and 200 mg/L U(VI). Both the second-order sorption kinetics and Langmuir adsorption model were observed to be obeyed by the ability of SiO2/CS to eradicate U(VI). Thermodynamically, the sorption strategy was a spontaneous reaction and exothermic. According to the findings, SiO2/CS had the potential to serve as an effectual sorbent for U(VI) displacement. [ABSTRACT FROM AUTHOR]

Considering how important rare earth elements (REEs) are for many different industries, it is important to separate them from other elements. An extractant that binds to REEs inexpensively and selectively even in the presence of interfering ions can be used to develop a useful separation method. This work was designed to recover REEs from spent nickel–metal hydride batteries using ammonium sulfate. The chemical composition of the Ni–MH batteries was examined. The operating leaching conditions of REE extraction from black powder were experimentally optimized. The optimal conditions for the dissolution of approximately 99.98% of REEs and almost all zinc were attained through use of a 300 g/L (NH4)2SO4 concentration after 180 min of leaching time and a 1:3 solid/liquid phase ratio at 120 °C. The kinetic data fit the chemical control model. The separation of total REEs and zinc was conducted under traditional conditions to produce both metal values in marketable forms. The work then shifted to separate cerium as an individual REE through acid baking with HCl, thus leaving pure cerium behind. [ABSTRACT FROM AUTHOR]

The W–Cu composites with nanosized grain boundaries and high effective density were fabricated using a new fast isostatic hot pressing method. A significantly faster method was proposed for the formation of W–Cu composites in comparison to the traditional ones. The influence of both the high temperature and pressure conditions on the microstructure, structure, chemical composition, and density values were observed. It has been shown that W–Cu samples have a polycrystalline well-packed microstructure. The copper performs the function of a matrix that surrounds the tungsten grains. The W–Cu composites have mixed bcc-W (sp. gr. Im 3 ¯ m) and fcc-Cu (sp. gr. Fm 3 ¯ m) phases. The W crystallite sizes vary from 107 to 175 nm depending on the sintering conditions. The optimal sintering regimes of the W–Cu composites with the highest density value of 16.37 g/cm3 were determined. Tungsten–copper composites with thicknesses of 0.06–0.27 cm have been fabricated for the radiation protection efficiency investigation against gamma rays. It has been shown that W–Cu samples have a high shielding efficiency from gamma radiation in the 0.276–1.25 MeV range of energies, which makes them excellent candidates as materials for radiation protection. [ABSTRACT FROM AUTHOR]