Search

Preparing electrode materials plays an essential role in the fabrication of high-performance supercapacitors. In general, heteroatom doping in carbon-based electrode materials enhances the electrochemical properties. Herein, nitrogen, oxygen, and sulfur co-doped porous carbon (PC) materials were prepared by direct pyrolysis of Anacardium occidentale (AO) nut-skin waste for high-performance supercapacitor applications. The as-prepared AO-PC material possessed interconnected micropore/mesopore structures and exhibited a high specific surface area of 615 m2 g−1. The Raman spectrum revealed a moderate degree of graphitization of AO-PC materials. These superior properties of the as-prepared AO-PC material help to deliver high specific capacitance. After fabricating the working electrode, the electrochemical performances including cyclic voltammetry, galvanostatic charge–discharge, and electrochemical impedance spectroscopy measurements were conducted in 1 M H2SO4 aqueous solution using a three-electrode configuration for supercapacitor applications. The AO-PC material delivered a high specific capacitance of 193 F g−1 at a current density of 0.5 A g−1. The AO-PC material demonstrated −1. All the above outcomes confirmed that the as-prepared AO-PC from AO nut-skin waste via simple pyrolysis is an ideal electrode material for fabricating high-performance supercapacitors. Moreover, this work provides a cost-effective and environmentally friendly strategy for adding value to biomass waste by a simple pyrolysis route.

In this study, calcium carbonate nanoparticles (CCNPs) and calcium oxide nanoparticles (CONPs) are synthesized by the carbonization/calcination of calcium oleate. CONPs are an essential inorganic material, and they are used as catalysts and as effective chemisorbents for toxic gases. CCNPs are widely used in plastics, printing ink, and medicines. Here, calcium oleate is used as a starting material for the preparation of CCNPs and CONPs. This calcium oleate is prepared from calcium hydroxide and oleic acid in ethanol under mild reflux conditions. The effect of the calcination temperature of calcium oleate is examined during the synthesis of CCNPs and CONPs. By simple carbonization/calcination, calcite-type CCNPs and CONPs are prepared at 600 °C, respectively. The synthesized nanomaterials are analyzed by various physicochemical characterization techniques such as X-ray diffraction (XRD), Fourier transform infrared spectroscopy, thermogravimetric analysis (TGA) with derivative thermogravimetry (DTG), and scanning electron microscopy (SEM) with energy dispersive X-ray analysis. An X-ray diffractometer and the Scherrer formula are used to analyze the crystalline phase and crystallite size of prepared nanoparticles. TGA techniques confirm the thermal stability of the calcium oleate, CCNPs, and CONPs. The SEM analysis illustrates the dispersive behavior and cubic/spherical morphologies of CCNPs/CONPs. Furthermore, the obtained results are compared to the CCNP and CONP samples prepared using calcium hydroxide. As a result, the carbonization/calcination of calcium oleate produces monodispersed CONPs, which are then compared to the CONPs from calcium hydroxide. Additionally, from calcium oleate, CONPs can be prepared on a large scale in a cheap, convenient way, using simple equipment which can be applied in various applications.

Here, the controlled formation of platinum nanoparticles (PtNPs) and silver nanoparticles (AgNPs) using amine-functionalized multivalent ligands are reported. The effects of reaction temperature and ligand multivalency on the growth kinetics, size, and shape of PtNPs and AgNPs were systematically studied by performing a stepwise and a one-step process. PtNPs and AgNPs were prepared in the presence of amine ligands using platinum (II) acetylacetonate and silver (I) acetylacetonate, respectively. The effects of ligands and temperature on the formation of PtNPs were studied using a transmission electron microscope (TEM). For the characterization of AgNPs, additionally, ultraviolet-visible (UV-Vis) absorption was employed. The TEM measurements revealed that PtNPs prepared at different temperatures (160–200 °C, in a stepwise process) are monodispersed and of spherical shape regardless of the ligand multivalency or reaction temperature. In the preparation of PtNPs by the one-step process, ligands affect the shape of the PtNPs, which can be explained by the affinity of the ligands. The TEM and UV-Vis absorption studies on the formation of AgNPs with mono-, di-, and trivalent ligands showed narrower size distributions, while increasing the temperature from 80 °C to 120 °C and with a trivalent ligand in a one-step process.