The development of strain sensors with high sensitivity and stretchability is essential for health monitoring, electronic skin, wearable devices, and human-computer interactions. However, sensors that combine high sensitivity and ultra-wide detection generally require complex preparation processes. Here, a novel flexible strain sensor with high sensitivity and transparency was proposed by filling a multiwalled carbon nanotube (MWCNT) solution into polydimethylsiloxane (PDMS) channel films fabricated via an electric field-driven (EFD) 3D printing and molding hybrid process. The fabricated flexible strain sensor with embedded MWCNT networks had superior gauge factors of 90, 285, and 1500 at strains of 6.6%, 14%, and 20%, respectively. In addition, the flexible strain sensors with an optical transparency of 84% offered good stability and durability with no significant change in resistance after 8000 stretch-release cycles. Finally, the fabricated flexible strain sensors with embedded MWCNT networks showed good practical performance and could be attached to the skin to monitor various human movements such as wrist flexion, finger flexion, neck flexion, blinking activity, food swallowing, and facial expression recognition. These are good application strategies for wearable devices and health monitoring.

Nano-silver paste, as an important basic material for manufacturing thick film components, ultra-fine circuits, and transparent conductive films, has been widely used in various fields of electronics. Here, aiming at the shortcomings of the existing nano-silver paste in printing technology and the problem that the existing printing technology cannot achieve the printing of high viscosity, high solid content nano-silver paste, a nano-silver paste suitable for electric-field-driven (EFD) micro-scale 3D printing is developed. The result shows that there is no oxidation and settlement agglomeration of nano-silver paste with a storage time of over six months, which indicates that it has good dispersibility. We focus on the printing process parameters, sintering process, and electrical conductivity of nano-silver paste. The properties of the nano-silver paste were analyzed and the feasibility and practicability of the prepared nano-silver paste in EFD micro-scale 3D printing technology were verified. The experiment results indicate that the printed silver mesh which can act as transparent electrodes shows high conductivity (1.48 Ω/sq) and excellent transmittance (82.88%). The practical viability of the prepared nano-silver paste is successfully demonstrated with a deicing test. Additionally, the experimental results show that the prepared silver mesh has excellent heating properties, which can be used as transparent heaters.