The microstructural evolution of unpatterned Al-2wt.%Cu thin films has been examined to elucidate the mechanism by which copper improves electromigration resistance. After annealing at 425°C and cooling to room temperature at a rate of approximately 1°C/min., the microstructure of the Al-Cu films consisted of 1 μm aluminum grains with θ-phase Al2Cu precipitates at grain boundaries and triple points. The grain size and precipitation distribution did not change with subsequent isothermal heat treatments in the temperature range of 200° to 400°C. Al-Cu thin films annealed at 400°C, a temperature just below the Al/Al+θ solvus, exhibited microstructures in which the aluminum grain boundaries were depleted in copper except for the presence of the pre-existing large, widely dispersed AI2Cu precipitates. Al-Cu thin films annealed at 200° to 300°C were enriched with copper at the aluminum grain boundaries. The large, widely dispersed Al2Cu precipitates remained after the lower temperature anneals. From these results, it is proposed that the presence of copper in aluminum thin films improves electromigration resistance due to the precipitation of a thin film of Al2Cu, or a substoichiometric precursor, along the grain boundaries. The grain boundary phase retards grain boundary diffusion in the thin films, thereby reducing total mass transport and improving electromigration resistance.

Al with additions of Cu is commonly used as the conductor metallizations for integrated circuits (ICs). As the packing density of ICs increases, interconnect lines are required to carry ever higher current densities. Consequently, reliability due to electromigration failure becomes an increasing concern. Cu has been found to increase the lifetimes of these conductors, but the mechanism by which electromigration is improved is not yet fully understood. In order to evaluate certain theories of electromigration it is necessary to have a detailed description of the Cu distribution in the Al microstructure, with emphasis on the distribution of Cu at the grain boundaries. In this study analytical electron microscopy (AEM) has been used to characterize grain boundary regions in an Al-2 wt.% Cu thin film metallization on Si after a variety of thermal treatments. The results of this study indicate that the Cu distribution is dependent on the thermal annealing conditions. At temperatures near the θ phase (CuAl2) solvus, the Cu distribution may be modelled by the collector plate mechanism, in which the grain boundary is depleted in Cu relative to the matrix. At lower temperatures, Cu enrichment of the boundaries occurs, perhaps as a precursor to second phase formation. Natural cooling from the single phase field produces only grain boundary depletion of Cu consistent with the collector-plate mechanism. The kinetic details of the elemental segregation behavior derived from this study can be used to describe microstructural evolution in actual interconnect alloys.