Search

The physicochemical properties of binary systems are of great importance for the application of the latter. We report on the investigation of an ammonium sulfamate–urea binary system with different component ratios using a combination of experimental (FTIR, XRD, TGA/DSC, and melting point) and theoretical (DFT, QTAIM, ELF, RDG, ADMP, etc.) techniques. It is shown that, at a temperature of 100 °C, the system under study remains thermally and chemically stable for up to 30 min. It was established using X-ray diffraction analysis that the heating time barely affects the X-ray characteristics of the system. Data on the aggregate states in specified temperature ranges were obtained with thermal analysis and determination of the melting point. The structures of the ammonium sulfamate–urea system with different component ratios were optimized within the density functional theory. The atom-centered density matrix propagation calculation of the ammonium sulfamate–urea system with different component ratios was performed at temperatures of 100, 300, and 500 K. Regardless of the component ratio, a regular increase in the potential energy variation (curve amplitude) with an increase in temperature from 100 to 500 K was found.

Spruce (Piceaabies) wood hemicelluloses have been obtained by the noncatalytic and catalytic oxidative delignification in the acetic acid-water-hydrogen peroxide medium in a processing time of 3–4 h and temperatures of 90–100 °C. In the catalytic process, the H2SO4, MnSO4, TiO2, and (NH4)6Mo7O24 catalysts have been used. A polysaccharide yield of up to 11.7 wt% has been found. The hemicellulose composition and structure have been studied by a complex of physicochemical methods, including gas and gel permeation chromatography, Fourier-transform infrared spectroscopy, and thermogravimetric analysis. The galactose:mannose:glucose:arabinose:xylose monomeric units in a ratio of 5:3:2:1:1 have been identified in the hemicelluloses by gas chromatography. Using gel permeation chromatography, the weight average molar mass Mw of hemicelluloses has been found to attain 47,654 g/mol in noncatalytic delignification and up to 42,793 g/mol in catalytic delignification. Based on the same technique, a method for determining the α and k parameters of the Mark–Kuhn–Houwink equation for hemicelluloses has been developed; it has been established that these parameters change between 0.33–1.01 and 1.57–472.17, respectively, depending on the catalyst concentration and process temperature and time. Moreover, the FTIR spectra of the hemicellulose samples contain all the bands characteristic of heteropolysaccharides, specifically, 1069 cm−1 (C–O–C and C–O–H), 1738 cm−1 (ester C=O), 1375 cm−1 (–C–CH3), 1243 cm−1 (–C–O–), etc. It has been determined by the thermogravimetric analysis that the hemicelluloses isolated from spruce wood are resistant to heating to temperatures of up to ~100 °C and, upon further heating, start destructing at an increasing rate. The antioxidant activity of the hemicelluloses has been examined using the compounds simulating the 2,2-diphenyl-2-picrylhydrazyl free radicals.

The process of sulfation of arabinogalactan—a natural polysaccharide from Larix sibirica Ledeb.—with sulfamic acid in 1,4-dioxane using different activators has been studied for the first time. The dynamics of the molecular weight of sulfated arabinogalactan upon variation in the temperature and time of sulfation of arabinogalactan with sulfamic acid in 1,4-dioxane has been investigated. It has been found that, as the sulfation time increases from 10 to 90 min, the molecular weights of the reaction products grow due to the introduction of sulfate groups without significant destruction of the initial polymer and sulfation products. Sulfation at 95 °C for 20 min yields the products with a higher molecular weight than in the case of sulfation at 85 °C, which is related to an increase in the sulfation rate; however, during the further process occurring under these conditions, sulfation is accompanied by the destruction and the molecular weight of the sulfated polymer decreases. The numerical optimization of arabinogalactan sulfation process has been performed. It has been shown that the optimal parameters for obtaining a product with a high sulfur content are a sulfamic acid amount of 20 mmol per 1 g of arabinogalactan, a process temperature of 85 °C, and a process time of 2.5 h.