The catalytic properties of modified Au/TiO2 catalysts for low-temperature CO oxidation are affected by deactivation and reactivation after long-term storage and by redox treatments. The effect of these phenomena on the catalysts was studied by HRTEM, BET, SEM, FTIR CO, XPS and H2 TPR methods. The main cause for the deactivation and reactivation of catalytic properties is the variation in the electronic state of the supported gold, mainly, the proportion of singly charged ions Au+. The most active samples are those with the highest proportion of singly charged gold ions, while catalysts with a high content of trivalent gold ions are inactive at low-temperatures. Active states of gold, resistant to changes caused by the reaction process and storage conditions, can be stabilized by modification of the titanium oxide support with transition metals oxides. The catalyst modified with lanthanum oxide shows the highest stability and activity.

The nature and size of the real active species of nanoparticulated metal supported catalysts is still an unresolved question. The technique of choice to measure particle sizes at the nanoscale, HRTEM, has a practical limit of 1 nm. This work is aimed to identify the catalytic role of subnanometer species and methods to detect and characterize them. In this frame, we investigated the sensitivity to redox pretreatments of Ag/Fe/TiO2, Ag/Mg/TiO2 and Ag/Ce/TiO2 catalysts in CO oxidation. The joint application of HRTEM, SR-XRD, DRS, XPS, EXAFS and XANES methods indicated that most of the silver in all samples is in the form of Ag species with size

In this paper, the effect of modifiers and pretreatments on the electronic states of 1 nm gold nanoparticles (AuNPs) supported on silica was systematically studied. AuNPs deposited on silica (particle size of 2–4 nm) modified with Ce, La and Fe oxides, were studied by FTIR of adsorbed CO after different redox treatments at 100, 300 and 500 °C. This study was conducted at room temperature to allow detecting the electronic states of gold, which is more likely involved in CO oxidation at the same temperature. AuNP size distribution was measured by HRTEM. It is shown that the electronic state of gold species (Aunδ−, Au0, Aunδ+, Au+) in 1 nm AuNPs is sensitive to the modifier as well as to the temperatures of redox pretreatments. Supports modified with the same additives but containing larger AuNPs (~3, 4, 5, and 7 nm) were also studied. They showed that Au0 remains stable irrespective of additives and redox pretreatments, indicating no significant effect of such treatments on the electronic properties of larger AuNPs. Samples with a predominant AuNP size of 2 nm are an intermediate case between these two groups of materials.