Search

Copper extraction from primary copper sulfide ore from a typical porphyry copper deposit from Antofagasta, Chile, was investigated after leaching with a chloride-ferrous media at two temperatures. The study focused on whether this chemical leaching system could be applied at an industrial scale. Leaching tests were conducted in columns loaded with approximately 50 kg of agglomerated ore; the ore was first cured for 14 days and then leached for 90 days. The highest copper extraction, 50.23%, was achieved at 32.9 °C with the addition of 0.6 kg of H2SO4 per ton of ore, 0.525 kg of NaCl per ton of ore, and 0.5 kg of FeSO4 per ton of ore. In respect to copper extraction, the most effective variables were temperature and the addition of NaCl. [ABSTRACT FROM AUTHOR]

In this paper, the effect of the cupric and chloride ions concentrations on copper dissolution from chalcopyrite concentrate was studied in acidified media. Variables included three different concentrations of Cu2+ (0.5, 1.5, and 2.5 g L−1), four different concentrations of Cl− (0, 5, 7, and 10 g L−1), two different pH values of 1 and 2, and a constant temperature of 60 °C. Results indicated that addition of Cl− to the system improves copper extractions, especially at higher concentrations of Cu2+. Initial copper concentrations in the leaching solution did not significantly affect the copper extraction when Cl− was not present. Better copper extractions were obtained at pH 1 as compared with pH 2. As the Cu2+ and Cl− concentrations were increased, higher values of redox potential were obtained. According to the formation constants of the chloro-complexes, the predominant species in the Cu2+/Cl− system in the studied interval were CuCl+ and Cu2+. Using a model of copper speciation in the experimental range predicted for a single copper concentration with increasing Cl− concentration, the Cu2+ concentration decreased significantly while the concentration of the chloro-complex species CuCl+ increased. In the leached residue, evidence of sulfur formation was found using SEM and corroborated by XRD analysis. When chloride is present in the medium, the amounts of copper and iron in the residue decrease, confirming a positive effect of chloride on the extraction of copper from concentrate for the studied conditions. [ABSTRACT FROM AUTHOR]

This work investigates the effect of an agglomeration and curing pretreatment on leaching of a copper sulfide ore, mainly chalcopyrite, using mini-columns in acid-nitrate-chloride media. Ten pretreatment tests were conducted to evaluate different variables, namely the addition of nitrate as NaNO3 (11.7 and 23.3 kg/ton), chloride as NaCl (2.1 and 19.8 kg/ton), curing time (20 and 30 days) and repose temperature (25 and 45 °C). The optimum copper extraction of 58.6% was achieved with the addition of 23.3 kg of NaNO3/ton, 19.8 kg of NaCl/ton, and after 30 days of curing at 45 °C. Under these pretreatment conditions, three samples of ore were leached in mini-columns. The studied parameters were temperature (25 and 45 °C) and chloride concentration (20 and 40 g/L). The optimum copper extraction of 63.9% was obtained in the mini-column leaching test at 25 °C, with the use of 20 g/L of chloride. A higher temperature (45 °C) and a higher chloride concentration (40 g/L) negatively affected the extraction. The pretreatment stage had favorable effects, in terms of accelerating copper dissolution and improving leaching of copper sulfide ore in acid-nitrate-chloride media. Waste salts from caliche industry and waste brine from reverse osmosis can be used for providing the nitrate and chloride media. [ABSTRACT FROM AUTHOR]

In this study, the surface optimization methodology was used to assess the effect of three independent variables—time, particle size and sulfuric acid concentration—on Mn extraction from marine nodules during leaching with H2SO4 in the presence of foundry slag. The effect of the MnO2/Fe ratio and particle size (MnO2) was also investigated. The maximum Mn extraction rate was obtained when a MnO2 to Fe molar ratio of 0.5, 1 M of H2SO4, −320 + 400 Tyler mesh (−47 + 38 μm) nodule particle size and a leaching time of 30 min were used. [ABSTRACT FROM AUTHOR]

This document presents a proposal for designing an expert system in the Gabriela Mistral Division's crushing plant belonging to Codelco (Chile) with the objective of maximizing stacked tonnage, allowing the improvement of operational variables that directly interact with the crushing process. In addition, this study considers the impact that occurs in both the process and operational continuity regarding the standardization of the system. In the first stage, a survey and analysis of historic operation data was carried out, which allowed the definition of benchmarking indicators. Subsequently, both modalities of operation were compared, monitoring processed tonnage and detentions related to operational failures. As a result, significant differences were observed in the performance of the critical line operating with expert control, with a 55% reduction in the detentions referred to operational failures. Added to this is the benefit of low cost and improved quality as the control provides an analysis of the variables in reduced time intervals, which is superior to human control. [ABSTRACT FROM AUTHOR]