Search

Magnesium-based alloys hold potential for medical applications, but face challenges like rapid bioresorption and limited mechanical strength during early bone healing. In our study, we present a novel Mg–Zn–Zr–Ce alloy with low cerium content (up to 0.1 wt.% Ce) processed using two severe plastic deformation (SPD) techniques. Through an innovative combination of multiaxial forging and multipass rolling, we have achieved a fine-grained structure with an average grain size of the primary α-Mg phase of 1.0 μm. This refined microstructure exhibits improved mechanical properties, including a substantial increase in yield strength (σYS) from 130 to 240 MPa, while preserving ductility. The alloy’s composition includes α-Mg grains, cerium and zinc hydrides, and intermetallic phases with cerium and zinc elements. Tensile testing of the fine-grained alloy demonstrates an enhancement in yield strength (σYS) to 250 MPa, marking a 2.8-fold improvement over the conventional state (σYS = 90 MPa), with a modest 2-fold reduction in ductility. Crucially, electrochemical tests conducted in physiological solutions highlight substantial advancements in corrosion resistance. The corrosion current was reduced from 14 to 2 μA/cm2, while polarization resistance decreased from 3.1 to 8.1 kΩ∙cm2, underlining the alloy’s enhanced resistance to biodegradation. Our results show that the novel Mg–Zn–Zr–Ce alloy, after combined SPD, demonstrates mitigated bioresorption and enhanced mechanical properties. Our findings highlight the fact that the introduction of this innovative alloy and the application of SPD represent significant steps towards addressing the limitations of magnesium-based alloys for medical implants, offering potential improvements in safety and effectiveness.

The microstructural investigation, mechanical properties, and accumulation and dissipation of energies of the magnesium alloy Mg-2.9Y-1.3Nd in the recrystallized state and after severe plastic deformation (SPD) by extrusion are presented. The use of SPD provides the formation of a bimodal structure consisting of grains with an average size 15 µm and of ultrafine-grained grains with sizes less than 1 µm and volume fractions up to 50%, as well as of the fine particles of the second Mg24Y5 phases. It is established that grain refinement during extrusion is accompanied by an increase of the yield strength, increase of the tensile strength by 1.5 times, and increase of the plasticity by 1.8 times, all of which are due to substructural hardening, redistribution of the phase composition, and texture formation. Using infrared thermography, it was revealed that before the destruction of Mg-2.9Y-1.3Nd in the recrystallized state, there is a sharp jump of temperature by 10 °C, and the strain hardening coefficient becomes negative and amounts to (−6) GPa. SPD leads to a redistribution of thermal energy over the sample during deformation, does not cause a sharp increase in temperature, and reduces the strain hardening coefficient by 2.5 times.

For this paper, studies of the microstructure as well as the mechanical and biological properties of bioinert titanium, zirconium, and niobium alloys in their nanostructured (NS) and ultrafine-grained (UFG) states have been completed. The NS and UFG states were formed by a combined two-step method of severe plastic deformation (SPD), first with multidirectional forging (MDF) or pressing into a symmetrical channel (PSC) at a given temperature regime, and then subsequent multi-pass groove rolling (MPGR) at room temperature, with pre-recrystallization annealing. Annealing increased the plasticity of the alloys in the NS and UFG states without changing the grain size. The UFG structure, with an average size of structural elements of no more than 0.3 μm, was formed as a result of applying two-step SPD and annealing. This structure presented significant improvement in the mechanical characteristics of the alloys, in comparison with the alloys in the coarse-grained (CG) or small-grained (SG) states. At the same time, although the formation of the UFG structure leads to a significant increase in the yield strength and tensile strength of the alloys, their elastic modulus did not change. In terms of biocompatibility, the cultivation of MG-63 osteosarcoma cells on the polished and sandblasted substrates demonstrated high cell viability after 10 days and good cell adhesion to the surface.

Bioinert metals are used for medical implants and in some industrial applications. This study was performed to detect and analyze peculiarities that appear in the temperature distributions during quasi-static tensile testing of bioinert alloys. These alloys include VT1-0 titanium, Zr-1%Nb and Ti-45%Nb in both coarse-grain (CG) and ultrafine-grain (UFG) states. The crystal structure, as well as the crystal domain and grain sizes of these alloys in the UFG state, may be different from the CG versions and identifying the thermal signatures that occur during their deformation and fracture is of interest, as it may lead to an understanding of physical processes that occur during loading. By comparing the surface temperature distributions of specimens undergoing deformation under tensile loading to the distributions at maximum temperatures it was found that the observed differences depend on the alloy type, the alloy structural state and the thermal properties of structural defects in the specimen. Macro-defects were found in some specimens of VT1-0 titanium, Zr-1Nb and Ti-45Nb alloys in both the CG and UFG states. The average tensile strength of specimens containing defects was lower than that of specimens with no defects. Infrared thermography documents change in the thermal patterns of specimens as they are deformed under tensile loading and when the load stops changing or the specimen breaks.