Search

This study aims to determine the effect of the heat treatment process and pressing on hardness, density, and morphological changes in the microstructure of Al-Si alloys. In this study, the medium used was coconut shell charcoal with a mesh size of 80 at a heat treatment process of 400 °C and a holding time of 75 minutes. The pressing was carried out with a load of 150 N. The result of this research is an increase in the hardness of the Al-Si alloy with an average value of 133 VHN after the Heat Treatment and pressing process. In the microstructure, there is a morphological change in the Al-Si alloy with the reduction of Si elements and also an increase in the density value after the heat treatment process.

Logam akan mengalami perubahan fasa selama proses pengecoran, baik perubahan sifat fisis maupun mekanik yang disebabkan oleh proses pembekuan. Perubahan sifat ini antara lain dipengaruhi media pendingin yang digunakan pada saat proses pendinginan. Tujuan penelitian ini adalah untuk membandingkan variasi temperatur pendinginan terhadap kekerasan hasil coran aluminium karena sifat fisis dan mekanis suatu logam sangat penting dalam kontruksi permesinan. Maka dalam penelitian ini digunakan media pendinginan yang berbeda yaitu : Air dengan suhu 15°C, Air dengan suhu 27°C dan Air dengan suhu 55°C. Dari pengujian kekerasan benda uji dengan media pendinginan air suhu 15°C mempunyai nilai kekerasan yang lebih baik dibanding air dengan suhu 27°C dan 55°C. Dari hasil pengujian komposisi kimia terdapat 17 unsur, tetapi hanya 4 unsur yang paling berpengaruh pada aluminium cor yaitu Si, Fe, Cu, dan Zn yang paling dominan. Dilihat dari unsur yang ada pada material ini dapat digolongkan logam aluminium paduan seng (Al-Zn).

Penelitian ini bertujuan untuk mengetahui kualitas bahan yang digunakan pada empat merk bearing (SKF, FMB, NKK, dan JAL) berdasarkan data-data pengujian sifat- sifat mekanik serta struktur intern (struktur mikro) pada benda uji tersebut dan dapat membandingkan ketahanan dan kekuatan keempat merk bearing tersebut berdasarkan analisis pengujian terhadap kegunaannya. Pengujian yang dilakukan meliputi pengujian kekerasan menggunakan alat Micro Vickers Hardness Tester, pengamatan struktur mikro menggunakan alat Olympus Metallurgical Microscope dan Olympus Phtomicrographics Systems, serta pengujian kekasaran permukaan menggunakan alat Surfcorder. Pengujian kekerasan maupun struktur mikro dilakukan pada bagian cincin luar bantalan (outer bearing) dan ball bearing. Sedangkan pengujian kekasaran permukaan hanya pada bagian outer bearing. Setelah dilakukan semua pengujian dapat disimpulkan bahwa berdasarkan kekuatan, kekerasan (ketahanan aus) serta kekasaran permukaan pada bagian outer bearing dan ball bearing maka merk yang memenuhi kualitas optimum adalah merk FMB karena sudah mencukupi dengan parameter kerja bantalan sehingga membuat umur pakai lebih panjang pada aspek penggunaan yang sama. Kata kunci: bearing, kekerasan, struktur mikro, kekasaran permukaan ABSTRACT This study aims to determine the quality of materials used in four bearing brands (SKF, FMB, NKK, and JAL) based on data testing of mechanical properties as well as internal structure (micro structure) on the specimens and can compare the endurance and the strength of the four brands bearings based on the test analysis of its usefulness. The tests include hardness testing using the Micro Vickers Hardness Tester tool, microstructure observation using Olympus Metallurgical Microscope and Olympus Phtomicrographics Systems, and surface roughness testing using Surfcorder tool. Hardness testing and microstructure are performed on outer bearing and ball bearing parts. While the surface roughness testing only on the outer bearing. After all tests, it can be concluded that based on strength, hardness (wear resistance) and surface roughness on outer bearing and ball bearings, the brand that meets the optimum quality is the FMB brand because it is sufficient with the bearing working parameters that make longer life on the same aspect of use. Keywords: bearing, strengthness, microstructure, surface roughness

Elekroplating merupakan proses pelapisan logam dengan logam lain dalam satu larutan elektrolit dimana arus searah yang dialirkan melalui anoda dan katoda akan menimbulkan rekasi reduksi dan oksidasi sehingga bahan anoda akan tergerus dan melapisi bahan katoda. Kualitas produk elektroplating sangat dipengaruh oleh beberapa faktor antara lain jenin bahan yang digunakan dan pemilihan parameter celup terhadap kilap dan ketebalan lapisan. Penelitian ini dilakukan dengan menggunakan material plat baja karbon tinggi sebagai katoda dan tembaga sebagai anoda. Persiapan bahan katoda dilakukan mulai dari memotong bahan, meratakan dan pemolesan permukaan dengan mesin dan kertas gerinda. Proses plating dilakukan dengan voltase 7 volt, dan menggunakan variasi waktu tahan celup selama 5, 7 dan 9 detik. Benda hasil elektroplating kemudian diuji nilai kilap lapisannya dengan gloss meter dan ketebalan lapisannya dengan thickness gauge. Hasil pengujian kilap menunjukkan bahwa dengan waktu plating 5 detik diperoleh nilai kilap sebesar 134,7 GU, waktu plating 7 detik diperoleh nilai kilap 133,7 GU dan waktu plating 9 detik diperoleh nilai kilap sebesar 129,5 GU. Sedangkan pengujian ketebalan menunjukkan bahwa dengan waktu plating 5 detik diperoleh ketebalan lapisan sebesar 0202 μm, waktu plating 7 detik diperoleh ketebalan sebesar 0,270 μm dan waktu plating 9 detik diperoleh ketebalan sebesar 0,294 μm.