Search

We elucidate here the significance of cold rolling reduction on Luders band formation and mechanical behavior in cold-rolled intercritically annealed medium-Mn steel. The study indicated that Luders strain can be decreased by decreasing cold rolling reduction. Moreover, inactive recovery and recrystallization of ferrite consisting of a high dislocation density was responsible for the presence of low Luders strain.

Thin-gauge non-oriented silicon steel with high strength was successfully processed using strip casting. Texture evolution and strengthening mechanism via nanoscale Cu-rich precipitates were studied to fundamentally understand the balanced combination of magnetic properties and mechanical properties. Coarse equiaxed grains with average size of ∼190 μm and relatively random texture were formed in the as-cast strip, which contributed to the inhomogeneous deformation, resulting in high density of shear bands. Exact Cube was retained from the initial Cube texture and new Goss was formed during the heavy rolling process in the 0.20 mm cold rolled sheet, which promoted relatively strong Cube and Goss texture after recrystallization annealing. The 0.20 mm annealed sheet exhibited high magnetic induction of 1.709 T, which corresponds to the high texture factor of 0.5. The total iron losses were significantly reduced with decrease in thickness, and the P1.5/50, P1.0/400, and P1.0/1000 in 0.20 mm sheet were as low as 2.63, 15.17 and 55.63 W/kg, respectively, which showed a good match between magnetic induction and iron loss. During the aging process, both the magnetic induction and total iron loss exhibited relatively good stability. With increase in aging time, the yield strength first rapidly increased and then slightly decreased. In 0.20 mm sheet, peak yield strength of ∼630 MPa was obtained on aging at 550 °C for 90–120 min. The key mechanism of precipitation strengthening was attributed to the difference in modulus and coherency strain associated with high density of nanoscale precipitates of ∼5 nm. The study revealed that the nanoscale Cu-rich precipitates can be adopted as effective approach to increase the yield strength over ∼100 MPa without deteriorating iron loss in thin-gauge non-oriented silicon steel by strip casting, which guaranteed the balance of magnetic properties and mechanical properties to meet the requirements of high-speed motor.

The short communication presents a welding behavior of a dual-phase Mg alloy under different friction stir processes. Growing weld speed obtained different microstructures and ripple spacing of weld joint, and with which the mechanical properties of weld joint generally decreased. Butt-welding joint was more tenacious than lap-welding one.

In the present study, a hot-rolled and heat-treated TRIP steel (Fe-0.25C-1.23Si-2.09Mn-2.92Al wt%) was successfully produced by a simple process that involved intercritical heat treatment (IHT) followed by direct quenching without bainite reaction step. The microstructure of the as-cast ingot, as-hot-rolled sheet and heat-treated sheet was studied and related to mechanical properties of the heat-treated sheet. It was observed that δ-ferrite was retained from the solidification stage and remained as a stable phase during different stages of processing because of the alloy design that included ~ 3 wt% Al. Banded structure was obtained in both as-hot-rolled sheet and heat-treated sheet. The microstructure of 770–820 °C heat-treated sheet consisted of δ-ferrite, retained austenite (RA), α-ferrite and martensite. Based on the alloy design and direct quenching process, ~ 20–30% volume fraction of RA was obtained in the heat-treated sheet. The 780 °C heat-treated sheet exhibited an excellent combination of tensile strength and total elongation of 880 MPa and 28%, respectively.

In order to improve the mechanical properties of Inconel 718 alloy produced by sub-rapid solidification, the yttrium (Y) element was added during casting. One alloy with 0.1% weight Y content (0.1Y) and a reference alloy without Y addition (0Y) were produced, which involved homogenization, cold rolling, intermediate annealing, and aging treatment. The influences of Y addition on the microstructure and mechanical properties of Inconel 718 alloy were examined. Due to the precipitation of Ni3Y and Ni17Y2 particles, 0.1Y alloy exhibited a refined grain size and a lower recrystallization fraction. The average grain size of 0Y homogenized sample and 0.1Y homogenized sample were about 50.8 μm and 29.5 μm, respectively. Besides, a higher fraction of δ phase precipitated in the 0.1Y annealed sample, including a large amount of granular or short-rod shape δ phases and a small amount of needle-like δ phases. The area fraction of δ phase in the 0.1Y annealed sample was ~10.45%. However, the area fraction of δ phase in the 0Y annealed sample was lower (~7.93%), and needle-like δ phase was hardly observed under this condition. Compared with 0Y alloy, 0.1Y alloy showed better tensile properties. The 0.1Y alloy after aging treatment exhibited an excellent combination of ultimate tensile strength (~1400 MPa), and total elongation (~20%) when deformed at room temperature.

Low mismatch and low energy interface between precipitates and ferrite matrix was adopted to promote the precipitation of high density of uniformly dispersed coherent NiAl phase in the silicon steel, aiming to improve strength to meet the requirement of drive motor. The precipitation mechanism of NiAl and its influence on magnetic and mechanical properties of silicon steel were studied. The theoretical lattice mismatch between precipitation and matrix was 0.72%, and a new high strength non-oriented silicon steel reinforced by B2 structure NiAl precipitation with a volume content of 1.73% and an average size of 15 nm was prepared. The uniformity of precipitation size and minimization of interface energy remarkably reduced the driving force for NiAl precipitation and hindered the Ostwald ripening. The texture of annealed silicon steel was characterized by strong α* fiber with a peak at {411} and a moderate γ fiber texture with a peak at {111} . With increase in aging time (from 0 h to 16 h), the strength of silicon steel increased to peak values then decreased and the magnetic properties decreased slightly. The nano-scale NiAl precipitation had little effect on coercivity and hysteresis loss of silicon steel while improving the strength of silicon steel, P10/400 and P10/1000, of silicon steel was as low as 21.7 W/kg and 93.3 W/kg, respectively in the peak-aged condition (at 550 °C for 4 h), and the yield strength was 802 MPa. Thus, it is underscored that using NiAl precipitation as strengthening phase improves the mechanical properties of silicon steel without excessively deteriorating the magnetic properties.