Search

Abstract: The effect of Si content on low frequency damping capacities and mechanical properties of as-cast Mg–Si alloys were investigated. Both hypoeutectic alloys with 0.3wt.%Si, 0.8wt.%Si and hypereutectic alloy with 2.3wt.%Si exhibit high damping capacities since these Mg–Si alloys possess large size α-Mg phase with very small amount of soluble atoms in it. The amount of the in situ formed Mg2Si determines the dislocation density and then influences the damping capacity of these Mg–Si alloys. The Mg–0.3wt.%Si alloy exhibits the lowest damping value at small strain region but the highest damping value at large strain region among these Mg–Si alloys. Two damping peaks were found in Mg–Si alloys at 80 and 230°C, respectively. But the addition of Al in Mg–Si alloy impeded the appearance of these two damping peaks since the soluble Al atoms hindered the movement of dislocations and the slide of grain boundaries. The presence of large size, brittle primary Mg2Si particles decreases the tensile strength and ductility of the hypereutectic Mg–Si alloy. [Copyright &y& Elsevier]

Abstract: Carbon nanotube (CNTs) reinforced Mg matrix composites were successfully fabricated by a novel approach. After hot extrusion, the influence of CNTs on microstructure and mechanical properties of Mg–6Zn matrix was investigated. The results showed that most CNTs distributed uniformly and individually in the composites, and good interfacial bonding was achieved. CNTs significantly refined the grains of Mg–6Zn matrix, and the CNTs evidently improved the ultimate tensile strength (UTS), yield strength (YS) and Young's modulus. Grain refinement, load transfer mechanism and Orowan strengthening mechanism play important roles on the increase of the yield strength. [Copyright &y& Elsevier]

Abstract: In this paper, 0.2μm SiCp/AZ91 composite was fabricated by stir casting technology. The influence of fine (<1μm) particles on the dynamic recrystallization (DRX) behavior of AZ91 matrix was investigated by researching the microstructure evolution of 0.2μm 1vol% SiCp/AZ91 composite during the hot extrusion process. Results showed that the DRXed ratio of AZ91 matrix increased as well as the average size of DRXed grains reduced due to the addition of fine particles. The SiCp could not only pin dislocation, but also was helpful to generate dislocations owing to the deformation mismatch between matrix and particles, thus causing the increase of dislocation density around SiCp, which was benefit to stimulate DRX nucleation. Meanwhile, the growth of DRXed grains was suppressed in the following deformation process due to the pinning effect of fine particles on grain boundaries. Thus, the fine particles had significant effect on stimulating DRXed nucleation and refining grain size. The yield strength and ultimate tensile strength of the as-deformed 0.2μm 1vol% SiCp/AZ91 composite are 275 and 335MPa, respectively, which are mainly attributed to the grain refinement, basal plane texture and uniform particle distribution induced by hot deformation. [Copyright &y& Elsevier]

sAbstract: The Mg/Al laminated composites were fabricated by the accumulative roll bonding (ARB) at ambient temperature using the pure magnesium and commercial pure Al sheets. Mg grains were refined after the primary sandwich preparation and then homogenized during the following ARB process while the grain size of Al layer decreased with increasing of the accumulated strains. Both the yield strength and ultimate strength along rolling direction and transverse direction increased gradually while the elongation to failure along both directions decreased with increasing of the ARB cycles. Formation of the Mg17Al12 phase indicated that the ARB process at ambient temperature could lead to a metallurgic bonding of the Mg/Al interface. [Copyright &y& Elsevier]

Abstract: In this paper, three kinds of magnesium matrix composites reinforced by SiCp with the sizes of 0.2, 5 and 10μm, respectively, were fabricated by stir casting technology. Then the as-cast ingots were deformed by the combination of forging and extrusion process. Typical microstructures were obtained in the composites reinforced by different particle sizes. For the composites with lower volume fraction of particles (2%), submicron SiCp had significant influence on grain refinement and strengthening effect, which resulted in better mechanical properties of submicron SiCp/AZ91 composite. However, mechanical properties reduced owing to the obvious agglomerated submicron SiC particles as the volume fraction increased to 5% and 10%. On the contrary, for micron SiCp/AZ91 composite, the grain size was refined and the strengthening effect was enhanced with the increasing of volume fraction. Although particle size has no influence on the texture type, it has different effects on weakening the intensity of texture. [Copyright &y& Elsevier]