Search

Due to its service background, the thermal behavior of Ta films is substantially concerning to researchers, especially the heat-induced β-Ta to α-Ta phase transformation. In this work, the nanocrystalline Ta films with varying β/α phase ratios (0.85–0) were deposited and vacuum annealed at 200–800 °C to study the phase transformation behavior and mechanical properties. Partial phase transformation of β-Ta to α-Ta occurred at low temperature (200 °C) and complete transformation when the annealing temperature was raised to 800 °C. Moreover, an orientation relationship of β-<110>//α-<111> and β-{330}//α-{110} was concluded, and a hypothesis theory about the low-temperature phase transformation was proposed. Annealing hardening took place at 200–600 °C and softening at 800 °C in all the samples. The hardening is mostly due to the ordering of intergranular amorphous phases with the temperature increased, simultaneously bringing the increase of modulus. The annealing softening is governed by both grain coarsening and phase transformation, where the latter is dominated in high β fraction samples. • High-temperature induced grain boundary structure ordering promotes the hardening of Ta films at 200 °C–600 °C. • β-Ta to α-Ta phase transformation was found at a wide temperature range, which partially governs the softening of Ta at 800 °C. • A preferred orientation relationship of β-<110>{330}//α-<111>{110} was concluded • The influence of phase transformation on mechanical properties was independently quantified using a simple comparative method. [ABSTRACT FROM AUTHOR]

The high Mn steel (Mn ≥ 20 wt.%) is widely applied because of excellent cryogenic properties. In the fusion-welded high-Mn steel joint, the Mn vapor and segregation degrade the joint quality. Friction stir welding (FSW) produces a high-Mn steel joint without defect, but the nugget zone (NZ) exhibits a poor plasticity. In this work, the preheating was subjected to FSW high-Mn steel to improve the plasticity of the NZ. Compared with the as-welded NZ, the as-preheated NZ contained slightly coarser austenite with lower density of dislocations (6.7 × 1014 m−2), and had a lower stacking fault energy (SFE) (47.18 mJ m−2) at room temperature. The lower SFE caused the deformation mechanism of dislocation slip and active twinning-induced plasticity (TWIP) in the as-preheated NZ owing to the lower back stress and critical twinning stress. Subsequently, a high strength and plasticity product of 62 GPa% was achieved in the as-preheated NZ, which was consistent with high strain hardening rate. At cryogenic temperature of −196 °C, the SFE of the as-preheated NZ decreased to 35.66 mJ m−2, but more active TWIP besides dislocation slip was found during tension. Therefore, the as-preheated NZ exhibited excellent strength and plasticity product of 91.9 GPa%. Furthermore, the yield strength of the as-preheated NZ was slightly reduced, which was attributed to the decreased of dislocation density and grain growth. • The preheating was introduced into the friction stir welded high Mn steel. • The SFE of austenite in the as-welded and as-preheated NZs at room and cryogenic temperature was calculated. • The deformation behavior of the as-welded and as-preheated NZs at room and cryogenic temperature was studied. • The contribution of various strengthening mechanisms to yield strength was evaluated. • The as-preheated-320 NZ presented excellent strength and plasticity product at room and cryogenic temperature. [ABSTRACT FROM AUTHOR]

Ti alloy clad plate is of great interest for marine and petrochemical industry applications. However, high interfacial bonding is hardly obtained in the Ti alloy clad plate due to the brittle intermetallic compounds (IMCs) forming at the interface. In this study, a Ti-6Al-4V alloy/EH690 steel clad plate was fabricated by vacuum rolling and subsequently tempered to control the mechanical property of the steel substrate. The tempered sorbite appeared in the EH690 steel after quenching and tempering (QT). A decarburized zone, Fe 2 Ti + TiC mixed phases layer, and β-Ti layer were formed at the interface between steel and Ti. The brittle IMCs with high lattice mismatch resulted in a low interfacial strength of 108 MPa. To improve bonding strength, Nb was inserted between Ti and steel as an interlayer, which effectively inhibited the inter-diffusion of Ti, Fe, and C without brittle TiC or Fe-Ti IMCs. A (Ti, Nb) solid solution layer with high plasticity was present at the Nb/Ti interface. Fe 2 Nb and Fe 7 Nb 6 phases were detected at the steel/Nb interface, exhibiting less brittleness and hardness compared to Fe-Ti IMCs. The interfacial shear strength was up to 265 MPa after adding the Nb interlayer, showing a mixed fracture mode of brittleness and ductility. [ABSTRACT FROM AUTHOR]

Ti/Al clad plate is a highly promising material due to its low cost, lightweight nature, high strength, and excellent corrosion resistance. However, the deformation coordination between Ti and Al is very poor, and both metals easily are oxidated, resulting in a weak interfacial bonding. In this study, Ti/Al clad plate was fabricated by vacuum rolling, obtaining a clear interface without oxidation and compound. The as-rolled Ti/Al clad plate had a shear strength of 76 MPa with the fracture being at the Al substrate due to the solution of Mg 2 Si precipitates in the Al substrate during rolling. As a result, the solution and aging is necessary to enhance interfacial bonding. There were fine and dispersed Mg 2 Si precipitates in the as-treated Al substrate, and an (Al, Si) 3 Ti layer with ∼300 nm thickness appeared at the interface. Besides, the interfacial shear strength was up to 140 MPa, and the fracture still was at the Al side. The as-treated clad plate had an elongation of 33.5% which exceeded that of 25.8% calculated by the mixed rule. Obviously, the thin (Al, Si) 3 Ti layer is helpful to improve interfacial shear strength and plasticity of the Ti/Al clad plate. [ABSTRACT FROM AUTHOR]

The precipitate evolution, strength and corrosion resistance of an Al–Zn–Mg–Cu alloy processed by cryorolling, warm rolling and final aging have been investigated. A large number of spherical Zn-rich GP zones formed after warm rolling. In-situ transmission electron microscopy (TEM) observation indicated that the GP zones are stable during aging treatment and can serve as nuclei for subsequent precipitates, leading to homogeneous distribution of precipitates in the matrix after aging. TEM results also showed that ultrafine subgrains were developed in the deformed microstructure during aging. The high density of precipitates and dislocations combined with grain refinement contribute to the higher strength of the thermo-mechanically treated alloy compared with the peak-aged alloy. On the other hand, the η phase with C15 cubic structure having ‧‧‧RR‧‧‧ stacking is found in the thermo-mechanically treated alloy and is different from one with C14 hexagonal structure having ‧‧‧RR−1‧‧‧ stacking that is commonly observed in conventionally aged alloys, where R and R−1 represent rhombic layer and the relatively 180°-rotated rhombic layer, respectively. The transition from ill-defined stacking to C15 stacking and further to C14 stacking is observed in the structure of a η phase. Besides, the combination of warm rolling and aging can avoid the formation of continuous grain boundary precipitates, which is beneficial to the corrosion resistance of the alloy. [ABSTRACT FROM AUTHOR]

The effect of grain boundary character distribution (GBCD) on hydrogen-induced cracks (HICs) initiation and propagation in nickel-saving austenitic stainless steel was investigated at different strain rates with electrochemical hydrogen charging. The fracture strength and elongation of specimens decreased as the strain rates decreased due to more hydrogen atoms being transported by mobile dislocations. HICs are more likely to initiate at random grain boundaries (RGBs) because of poor deformation coordination of adjacent grains at RGBs after hydrogen charging. Special boundaries (SBs) deflected HICs and hindered the propagation of HICs owing to a more stable boundary structure and less strain localization during slow strain rate tensile (SSRT) deformation with hydrogen charging. Furthermore, highly efficient distributions of SBs contribute to great resistance to hydrogen embrittlement. • Higher content of SBs reduced the elongation and strength degeneration of material after H-charging. • With the increase of SB, the fracture mode changes from intergranular to quasi-cleavage. • SBs are beneficial to delay hydrogen permeation. • HICs prefer to initiate on RGBs due to poor deformation coordination after H-charging. • HICs are deflected and terminated by special boundaries, a higher fraction of f J2 /(1-f J3) effectively inhibit HICs propagation. [ABSTRACT FROM AUTHOR]