Search

MWCNTs modified Si 2 BC 3 N ceramics were prepared through SPS sintering mechanically alloyed amorphous Si 2 BC 3 N powder and MWCNTs at 1900 °C in N 2 atmosphere. The phase evolutions, microstructures and mechanical properties of the prepared ceramic were characterized by XRD, SEM and TEM (SAED and HRTEM), as well as the properties testing. The results show that the Si 2 BC 3 N ceramics are mainly composed of β-SiC, α-SiC and BN(C) phases. The introduction of MWCNTs can stimulate the formation of β-SiC in comparison with the pure Si 2 BC 3 N ceramics. Meanwhile, the particle sizes of BN(C) and SiC are reduced with the introduction of MWCNTs. Furthermore, the MWCNTs are mainly embedded in the Si 2 BC 3 N matrixes, contributing to enhanced bonding. Judging from the interfacial characteristic, the strengthening and toughening mechanisms of MWCNTs in Si 2 BC 3 N ceramics can be classified as “crack bridging”, “pull-out” and “crack deflection”. Based on these effects, the 1 vol% MWCNTs incorporated Si 2 BC 3 N ceramics have much higher flexural strength and fracture toughness of 462.1 MPa and 5.54 MPa·m 1/2 , respectively. [ABSTRACT FROM AUTHOR]

A novel composite ceramics with excellent mechanical properties was fabricated by means of low temperature hot-pressing using hexagonal boron nitride ( h -BN) and magnesium aluminum silicate (MAS) as raw materials. The influences of starting MAS content on the microstructural evolution and mechanical properties of the composites were investigated. The results indicate that the effective enhancement of relative density of composites has been achieved, which shows that MAS is an effective liquid-phase sintering aid during the hot-pressing. MAS also can improve the structural ordering of h- BN flakes. On the other hand, h- BN exhibits significant inhibiting effect on the crystallization of α-Cordierite. Furthermore, h -BN flakes with layered structure can play a role in strengthening the MAS matrix. So h -BN and MAS are considered to be co-enhanced by each other, resulting in better sintering ability and the mechanical properties of composite ceramics are better than that of both h -BN and MAS. Composite ceramics incorporated with 50 wt% MAS exhibits the highest bending strength and fracture toughness of 213±25 MPa and 2.49±0.35 MPa m 1/2 , respectively. [ABSTRACT FROM AUTHOR]

BN/Si 3 N 4 composite ceramics with different BN content were prepared by water-based gel casting process with raw and Y–Al-oxides-coated BN powder, separately. A Y–Al oxides layer with the thickness ranging from dozens to hundreds of nanometers, serving as sintering additives, was coated on the surface of BN particles with the method of precipitation of inorganic salts. As a result, the fluidity of BN/Si 3 N 4 slurry with Y–Al-oxides-coated BN powder was much improved compared to that with raw BN. SEM examination showed the Y–Al-oxides-coated BN particles were homogeneously distributed within the Si 3 N 4 grain boundaries, and BN aggregation was barely detected. The BN/Si 3 N 4 composite ceramic prepared by Y–Al-oxides-coated BN powder showed a better sintering behavior than those prepared by raw BN due to the formation of fine and homogeneous microstructure in it. Compared to the BN/Si 3 N 4 ceramic with 15 vol% raw BN, the density and flexural strength of the ceramic with the same content of surface-coated BN were significantly improved to 8.5% and 67.2%, respectively. [ABSTRACT FROM AUTHOR]