β – SiC powder mixed with 10 wt.% Al 2 O 3 and Y 2 O 3 powder in a molar ratio of 2: 3 was consolidated by spark plasma sintering (SPS) at 1700–1900 °C. Three SPS routes were designed to contrast the effects of passing a strong direct current (DC) on the densification behavior of the SiC materials. The wetting of the Y – Al – Si – O liquid to the SiC particles was increased by the DC, hence better densification. The resultant SiC ceramic had a finer uniform microstructure and high flexural strength. [ABSTRACT FROM AUTHOR]

Abstract: Porous silicon nitride/silicon oxynitride composite ceramics were fabricated by silica sol infiltration of aqueous gelcasting prefabricated Si3N4 green compact. Silica was introduced by infiltration to increase the green density of specimens, so suitable properties with low shrinkage of ceramics were achieved during sintering at low temperature. Si2N2O was formed through reaction between Si3N4 and silica sol at a temperature above 1550°C. Si3N4/Si2N2O composite ceramics with a low linear shrinkage of 1.3–5.7%, a superior strength of 95–180MPa and a moderate dielectric constant of 4.0–5.0 (at 21–39GHz) were obtained by varying infiltration cycle and sintering temperature. [Copyright &y& Elsevier]