1. The diffusion path in Ti-Ni70Cu30 diffusion couple at 850 °C for different annealing times.
- Author
-
Serafin, Daria, Nowak, Wojciech Jerzy, Wierzba, Patrycja, Albrecht, Robert, and Wierzba, Bartek
- Subjects
- *
COUPLES , *DIFFUSION , *FLUX (Energy) , *ANNEALING of metals - Abstract
The interdiffusion in Ti-Ni70Cu30 diffusion couple was studied at 850 °C at times varied between 10 and 300 min. The diffusion paths for the samples were determined and the order of intermetallic phases occurring in the diffusion zone was established. It was concluded that after 10 and 30 min of diffusion annealing, four intermetallic phases formed, namely: Ti 2 Ni, TiNi, τ 1 and TiNi 3. Between 30 and 60 min, also the Ti 2 Cu phase appeared next to Ti 2 Ni phase forming the multi-zone region, which thickness almost doubled between 60 and 300 min of diffusion annealing at 850 °C. The formation of Ti 2 Cu and the multi-zone region was explained by the enrichment of Cu at the Ti 2 Ni/Ti boundary and connected with the increase in its diffusion flux. • Ti-Ni70Cu30 couple was annealed at 850 °C at times between 10 and 300 min. • after 10 and 30 min of annealing of Ti-Ni70Cu30 at 850 °C four phases formed. • between 30 and 60 min, the Ti 2 Cu appeared next to Ti 2 Ni forming two-phase region. • enrichment in Cu at the Ti 2 Ni/Ti boundary caused the formation of two-phase region. [ABSTRACT FROM AUTHOR]
- Published
- 2021
- Full Text
- View/download PDF