Elastic knitted fabrics find numerous applications in the industry for compression stockings, sports and leisure wear, swimwear, ballet wear, etc. During its use, knitwear is subjected to dynamic loading due to body movements. The loading and unloading of the knitted fabric affect the size of the elastic region in which unrecovered deformation completely disappears. This paper deals with the influence of the elastane percentage in the knitted fabric on the elastic properties of the knitted fabric under dynamic loading. For this experiment, three types of yarn were used in different combinations: polyamide (PA), wrapped elastane yarn and bare elastane. The mentioned yarns were used to knit three different groups of plated weft-knitted fabrics (two yarns in a knitted fabric row): without elastane, knitted fabric with a percentage of wrapped elastane, and knitted fabric with a percentage of bare elastane. The percentage of elastane ranged between 0% and 43%. First, standard uniaxial tensile tests were performed on knitted fabric samples until breakage under static load. The force–elongation diagrams obtained are used to determine the elastic limit up to which Hook's law applies. All knitted fabrics were cyclically tested to the elastic limit. From the obtained loading and unloading curves, unrecovered deformation (unrecovered elongation), elastic elongation and hysteresis index were determined and calculated. The results showed that the percentage of elastane significantly affects the size of the elastic region of the knitted fabric and has no effect on the hysteresis index. Therefore, it is necessary to optimize the elastane percentage for different knitted fabric designs to achieve the best dynamic recovery of the knitted fabric and to design a more stretchable knitted garment that fits the body as well as possible. [ABSTRACT FROM AUTHOR]

This paper lays out standards of compression stockings and their classification into classes. The analysis of knitted fabric structure parameters, elongation and compression of moderate- and high-compression stockings was conducted. Stocking compression on specific parts of the stocking leg was measured on three sizes of a wooden leg model. For moderate-compression stockings, compression above the ankle was 32 hPa. For high-compression stockings, compression above the ankle was 60 hPa. Both groups of the analyzed compression stockings were made on modern one-cylinder hosiery automats. The legs of the stockings were made in single inlaid jersey 1 + 1. Both yarns were elastane covered. The finer yarn formed loops and its knitting into a course was significantly larger than in the other yarn, which was much coarser and does not form loops but "lay the weft in a bent way". The smallest elongation of knitted fabric was above the ankle, where the highest compression was achieved, while the largest elongation was under the crotch, where the stocking leg exerted the smallest compression on the surface. The leg of the compression stocking acted as a casing that imposed compression on the leg and often reinforced it to be able to sustain compression loads. [ABSTRACT FROM AUTHOR]