Search

The objective of this research was to quantify the effect of surface degradation and abrasion separately and in combination on the flexural strength of lithia disilicate ceramics. Lithia disilicate disks were fabricated using the lost wax technique and pressing in vacuum. The eight groups in this pilot experiment were (i) reference, hydrated in distilled water for 24 h prior to fracture; (ii) reference, non-hydrated group; (iii) 28-day pH cycling group; (iv) 125K chewing cycle group; (v) combined pH cycling + 125K chewing cycle; (vi) constant pH 2 solution for 28 days; (vii) constant pH 7 solution for 28 days; and (viii) constant pH 10 solution for 28 days. pH cycling is a method that alternates between pH 2, 7 and 10 over 28 days. A total of 15 disks were used for each group. All the groups were tested using the biaxial piston and a three-ball flexural strength test to obtain their biaxial flexural strength. pH 2 constant immersion demonstrated the highest fracture strength and was significantly greater than all other groups (p < 0.0001). Chewing and pH cycling + chewing groups exhibited the lowest fracture strengths and were significantly lower than all other groups (p < 0.0001). The damage observed from the chewing simulator does not represent apparent clinical fractures. [ABSTRACT FROM AUTHOR]

The aim of this work is to investigate the effects produced by polymicrobial biofilm (Porphyromonas gingivalis, Streptococcus mutans, Streptococcus sanguinis, and Streptococcus salivarius) on the corrosion behavior of titanium dental implants. Pure titanium disks were polished and coated with titanium nitride (TiN) and silicon carbide (SiC) along with their quarternized versions. Next, the disks were cultivated in culture medium (BHI) with P. gingivalis, S. mutans, S. sanguinis, and S. salivarius and incubated anaerobically at 37 °C for 30 days. Titanium corrosion was evaluated through surface observation using Scanning Electron Microscope (SEM) and Atomic Force Microscopy (AFM). Furthermore, the Ti release in the medium was evaluated by Inductively Coupled Plasma Mass Spectrometry (ICP-MS). SEM images showed that coated Ti disks exhibited lower corrosion compared to non-coated disks, except for the quartenized TiN. This was confirmed by AFM, where the roughness was higher in non-coated Ti disks. ICP showed that Ti levels were low in all coating disks. These results indicate that these SiC and TiN-based coatings could be a useful tool to reduce surface corrosion on titanium implant surfaces. [ABSTRACT FROM AUTHOR]

Titanium (Ti) corrodes clinically in the presence of bacteria. We investigated this phenomenon as a function of Ti particles found in biopsied tissues around peri-implantitis sites and surface roughness of failed Ti implants. Tissue biopsies were surgically collected from peri-implantitis sites, processed, and embedded in resin. The resin-embedded samples were hand trimmed to the region of interest and semi-thick (500 nm) sections were collected onto coverslips. One section was toluidine blue post-stained as a reference. The remainder sections were left unstained for energy-dispersive X-ray spectroscopy (EDX) analysis. Processed samples were examined under scanning electron microscopy (SEM) and EDX. Corresponding failed implants were also removed and examined under SEM and EDX. Five out of eight biopsied samples demonstrated the presence of Ti particles in the soft tissue, suggesting the true rate among all failures was between 24.5% and 91.5% (the lower bound of a 95% confidence interval for the true rate of Ti presence). SEM analysis of failed implant bodies also indicated changes in surface morphology and appeared less detailed with decreased weight percent of Ti on the surface of the failed implants. In conclusion, Ti particles were noted in 5/8 biopsied samples. Surface morphologies were smoother in failed implants compared with the reference implant. [ABSTRACT FROM AUTHOR]

The effect of pH changes on the chemical durability of dental glass–ceramic materials was evaluated using weight loss and ion release levels. The hypothesis that increased pH changes will exhibit greater corrosion was investigated. The ion concentration was analyzed using inductively coupled plasma atomic emission spectrometer (ICP). The surface compositions were investigated using X-ray photoelectron spectroscopy (XPS). The surface morphologies were examined using scanning electron microscopy (SEM). Dental glass–ceramics were tested in constant immersion, 3-day cycling, and 1-day cycling with pH 10, pH 2, and pH 7 for 3, 15, and 30 days. The 1-d cycling group demonstrated the highest levels of weight loss compared with 3-d cycling and constant immersion. For the ion release, Si4+ and Ca2+ had the highest rates of release in 1-d cycling, whereas the Al3+ release rate with constant pH 2 was highest. The alteration/passivation layer that was formed on the surface of disks possibly prevented further dissolution of pH 10 corroded disks. XPS analysis demonstrated different surface compositions of corroded disks in pH 10 and pH 2. Si4+, K+, Na+, Al3+, and Ca2+ were detected on the surface of corroded pH 10 disks, whereas a Si4+ and P5+-rich surface formed on corroded pH 2 disks. SEM results demonstrated rougher surfaces for corroded disks in cycling conditions and pH 2 constant immersion. In conclusion, increased pH changes significantly promote the corrosion of dental glass–ceramic materials. [ABSTRACT FROM AUTHOR]

The effect of a novel silicon carbide (SiC) coating on the chemical durability of a fluorapatite glass-ceramic veneer was investigated by examining weight loss and ion release levels. The hypothesis that this novel coating will exhibit significant corrosion resistance was tested. Inductively coupled plasma atomic emission spectrometer (ICP) was used for ion concentration determination and scanning electron microscopy (SEM) for surface morphology analyses. Samples were immersed in pH 10 and pH 2 buffer solutions to represent extreme conditions in the oral cavity. Analyses were done at 15 and 30 days. The SiC coated group demonstrated significant reduction in weight loss across all solutions and time points (p < 0.0001). Ion release analyses demonstrated either a marginally lower or a significantly lower release of ions for the SiC-coated disks. SEM analysis reveals planarization of surfaces by the SiC-coated group. The surfaces of coated samples were not as corroded as the non-coated samples, which is indicative of the protective nature of these coatings. In conclusion, SiC is a novel coating that holds promise for improving the performance of ceramic materials used for dental applications. [ABSTRACT FROM AUTHOR]