Search

Magnesium matrix composites are essential lightweight metal matrix composites, following aluminum matrix composites, with outstanding application prospects in automotive, aerospace lightweight and biomedical materials because of their high specific strength, low density and specific stiffness, good casting performance and rich resources. However, the inherent low plasticity and poor fatigue resistance of magnesium hamper its further application to a certain extent. Many researchers have tried many strengthening methods to improve the properties of magnesium alloys, while the relationship between wear resistance and plasticity still needs to be further improved. The nanoparticles added exhibit a good strengthening effect, especially the ceramic nanoparticles. Nanoparticle-reinforced magnesium matrix composites not only exhibit a high impact toughness, but also maintain the high strength and wear resistance of ceramic materials, effectively balancing the restriction between the strength and toughness. Therefore, this work aims to provide a review of the state of the art of research on the matrix, reinforcement, design, properties and potential applications of nano-reinforced phase-reinforced magnesium matrix composites (especially ceramic nanoparticle-reinforced ones). The conventional and potential matrices for the fabrication of magnesium matrix composites are introduced. The classification and influence of ceramic reinforcements are assessed, and the factors influencing interface bonding strength between reinforcements and matrix, regulation and design, performance and application are analyzed. Finally, the scope of future research in this field is discussed. [ABSTRACT FROM AUTHOR]

In the general environment of lightweight automobiles, the integrated die-casting technology proposed by Tesla has become the general mode to better achieve weight reduction in automobiles. The die-casting mold required by integrated die-casting technology has the characteristics of large scale and complexity. Hence, higher requirements are put forward for the comprehensive performance of the die steel. Despite the stagnation in the progress of conventional strengthening methods, enhancing the performance of die steel has become increasingly challenging. Indeed, it necessitates exploring novel die steel and optimizing heat treatment and reinforcement technologies. This article summarizes and analyzes the development status of die steel and corresponding heat treatment and microstructure manipulation as well as strengthening methods and elaborates on an excellent nano-strengthening technology. Furthermore, this review will aid researchers in establishing a comprehensive understanding of the development status of die steel and the processes utilized for its strengthening. It will also assist them in developing die steel with improved comprehensive performance to meet the high demand for mold steel in the integrated die-casting technology of the new era. [ABSTRACT FROM AUTHOR]

It is well known that the development of lightweight alloys with improved comprehensive performance and application value are the future development directions for the ultra-high-strength 7xxx series Al-Zn-Mg-Cu alloys used in the aircraft field. As the lightest metal element in nature, lithium (Li) has outstanding advantages in reducing the density and increasing the elastic modulus in aluminum alloys, so Al-Zn-Mg-Cu alloys containing Li have gained widespread attention. Furthermore, since the Al-Zn-Mg-Cu alloy is usually strengthened by aging treatment, it is crucial to understand how Li addition affects its aging precipitation process. As such, in this article, the effects and mechanism of Li on the aging precipitation behavior and the impact of Li content on the aging precipitation phase of Al-Zn-Mg-Cu alloys are briefly reviewed, and the influence of Li on the service properties, including mechanical properties, wear resistance, and fatigue resistance, of Al-Zn-Mg-Cu alloys are explained. In addition, the corresponding development prospects and challenges of the Al-Zn-Mg-Cu-Li alloy are also proposed. This review is helpful to further understand the role of Li in Al-Zn-Mg-Cu alloys and provides a reference for the development of high-strength aluminum alloys containing Li with good comprehensive properties. [ABSTRACT FROM AUTHOR]

Bimodal hybrid in-situ nano-/micro-size TiC/Al composites were prepared with combustion synthesis of Al-Ti-C system and hot press consolidation. Attempt was made to obtain in-situ bimodal-size TiC particle reinforced dense Al matrix composites by using different carbon sources in the reaction process of hot pressing forming. Microstructure showed that the obtained composites exhibited reasonable bimodal-sized TiC distribution in the matrix and low porosity. With the increasing of the carbon nano tube (CNT) content from 0 to 100 wt. %, the average size of the TiC particles decreases and the compressive strength of the composite increase; while the fracture strain increases first and then decreases. The compressive properties of the bimodal-sized TiC/Al composites, especially the bimodal-sized composite synthesized by Al-Ti-C with 50 wt. % CNTs as carbon source, were improved compared with the composites reinforced with single sized TiC. The strengthening mechanism of the in-situ bimodal-sized particle reinforced aluminum matrix composites was revealed. [ABSTRACT FROM AUTHOR]

A high extrusion ratio of 166:1 was applied to commercial AZ61 alloy in one step with an extrusion speed of 2.1 m·min−1. The effects of DA (direct aging) treatment on the microstructure and tensile properties of extruded alloy were investigated. The extruded alloy exhibits fine DRXed grains and the average grain size is ~11 μm. After DA treatment at 170 °C, the tensile strength and 0.2% offset yield strength is enhanced from 314 to 336 MPa and from 169 to 191 MPa respectively, sacrificing elongation from 26.5% to 23.3%. The grain size and texture distribution of extruded AZ61 scarcely evolve during the post aging treatment. However, the enhanced strength in peak-aged alloy is mainly caused by the high-density elliptical Mg17Al12 precipitates distributing uniformly along the grain boundaries or within the grains, by precipitation and dispersion hardening. Furthermore, the nano-sized precipitates effectively inhibit grains from coarsening by triggering pinning effects along the grain boundaries at elevated temperature. As a result, the peak-aged alloy exhibits a better superplasticity of 306.5% compared with that of 231.8% of extruded sample. This work provides a practical one-step method for mass-producing Mg alloy sheets with excellent tensile strength and ductility compared with those fabricated by conventional extrusion methods. [ABSTRACT FROM AUTHOR]