Search

In the present paper, the designed thermomechanical process was applied to prepare ferrite/bainite multiphase microstructures in Si-rich low-alloy steel with a carbon content of 0.33 wt.% (0.33C) and 0.21 wt.% (0.21C). The microstructures were analyzed by scanning electron microscope, transmission electron microscope, and electron backscatter diffraction, and the mechanical properties (tensile and impact properties) were tested. The results showed that, on the premise of obtaining 15 vol.% ferrite in both steels, the ferrite grains in the 0.33C steel were polygonal with an average grain size of 2.2 μm, recrystallized more completely. However, the ferrite grains in the 0.21C steel were mainly long strip-shaped with a width of 2–4 μm, and the recrystallization degree was poor. In addition, upon increasing the austempering temperature, bainite ferrite laths were formed in the 0.33C steel, and the thickness was in the range of 81–123 nm. The morphology of bainite ferrite in the 0.21C steel gradually changed from lath to granular. Upon increasing the austempering temperature, the tensile strength and yield strength of both steels increased and the elongation decreased slightly. The impact energy of the two steels showed different trends upon increasing the austempering temperature, in which the impact energy of the 0.33C steel increased, while that of the 0.21C steel decreased. This is due to the difference size of the martensite-austenite constituents in the two steels. [ABSTRACT FROM AUTHOR]

The effect of the Zn/Mg ratio on microstructures, mechanical properties and corrosion performances of Al-Zn-Mg alloys was studied. Microstructures were characterized using the optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). Tensile tests, intergranular corrosion (IGC) and stress corrosion cracking (SCC) tests were conducted to study the properties. Microstructures results indicated that with the decrease of the Zn/Mg ratio, the recrystallization proportion and the fraction of second phase decreased, while the size of η' (MgZn2) phases in grain interior also significantly decreased. The number density of η' phases in grain interior increased and grain boundary precipitates developed discontinuous distribution with the decrease of the Zn/Mg ratio. These microstructures contributed to the significant improvement of the strength and corrosion resistance. The tensile strength and yield strength increased by 34.1% and 47.4%, respectively, with the Zn/Mg ratio decreased from 11.4 to 6.1. Calculating results indicated that the enhancement of strength mainly contributed from the solid-solution strengthening, grain-boundary strengthening and precipitation strengthening. The intergranular corrosion degree was greatly relieved and the stress corrosion sensitivity index decreased from 0.031 to 0.007 with the Zn/Mg ratio decreased from 11.4 to 6.1. [ABSTRACT FROM AUTHOR]

In this work, a biomedical Ti-6Al-4V (TC4)/Zn composite with gradient microstructures was successfully prepared by friction stir processing (FSP). The microstructures and mechanical properties of the composite were systematically studied using scanning electron microscope (SEM), X-ray diffractometer (XRD), transmission electron microscope (TEM), atom probe tomography (APT), and microhardness test. The results show that TC4/Zn composite can be successfully prepared, and gradient microstructures varying from coarse grain to nanocrystalline is formed from the bottom to the upper surface. During FSP, adding Zn can accelerate the growth of β phase region, and the grain size significantly increases with the increasing rotation rate. The grain combination is the main mechanism for grain growth of β phase region. The deformation mechanisms gradually change from dislocation accumulations and rearrangement to dynamic recrystallization from the bottom to the upper surface (1.5 mm–150 μm from the upper surface). The composite exhibits slightly higher microhardness compared with the matrix. This paper provides a new method to obtain a TC4/Zn composite with gradient surface microstructures for potential applications in the biomedical field. [ABSTRACT FROM AUTHOR]