Search

The current work investigates the possibility of fabricating additive manufacturing products in solid-state form, from AA2011-T6 of 40 mm diameter rods as a feedstock, using an additive friction stir deposition (A-FSD) technique. The use of large diameter feedstocks, especially high-strength aluminum alloys (2XXX series), is a challenge, as it necessitates high power and the critical selection of the optimal A-FSD parameters, such as feed rate and spindle rotation speed. The study included applying a wide range of spindle rotation speeds, ranging from 400 to 1200 rpm, at three levels of feeding rates of 1, 3, and 5 mm/min. The AA2011-T6 friction stir deposited parts (FSDPs) were visually evaluated. This was followed by an examination of macrostructures through the thickness of the fabricated specimens. The characterization of microstructures was also carried out using optical microscopy and a scanning electron microscope equipped with advanced EDS analysis. Furthermore, the mechanical properties in terms of hardness and compressive strength of the AA2011-T6 base material (BM) and deposited materials were evaluated. Sound, additively manufactured products were successfully fabricated from 40 mm diameter AA2011-T6 feedstocks using the suggested deposition variables of 600 and 800 rpm spindle speeds and feeding rates of 1, 3, and 5 mm/min. The results indicated that the spindle speed and feeding rate govern the quality of the FSDPs. Furthermore, the axial load during the A-FSD process increased with increasing these parameters. In comparison to the AA2011-T6 BM, the additively deposited materials showed a refined grain structure and uniform dispersion of the fragment precipitates in their continuous multi-layers. The reduction ratio in grain size attains 71.56%, 76%, and 81.31% for the FSDPs processed at 800 rpm spindle speed and feeding rates of 1, 3 and 5 mm/min, respectively, compared to the grain size of BM. The Al2Cu and Al7Cu2Fe intermetallics are detected in the AA2011-T6 BM, and their deposited parts are in different shapes of spherical, almost spherical, irregular, and rod-like shapes. The compressive strength and hardness of the deposited parts increased with increasing spindle speed and feeding speeds. At a spindle speed of 800 rpm and a 5 mm/min feeding rate, the higher hardness and compressive strength gained were 85% and 93%, respectively, from that of the AA2011-T6 feedstock. [ABSTRACT FROM AUTHOR]

The paper deals with research related to the production of metal cellular aluminium systems, in which production is based on the application of sodium chloride particles. In this paper, the properties of porous aluminium materials that were produced by an unconventional method—by pressing salt particles into the melt of aluminium alloy—are described. The new methodology was developed and verified for the production of these materials. The main feature of this methodology is a hydraulic forming press and a simple-shaped foundry mould. For these purposes, four different groups of sodium chloride particle sizes (1 to 3, 3 to 5, 5 to 7 and 8 to 10 mm) were applied. The preferred aluminium foundry alloy (AlSi12) was used to produce the porous aluminium samples. Based upon this developed methodology, samples of porous aluminium materials were produced and analysed. Their weight and volume were monitored, their density and relative density were calculated, and their porosity was determined. In addition, the porosity of samples and continuity of their air cells were monitored as well. An industrial computed tomograph and a scanning electron microscope were applied for these purposes. [ABSTRACT FROM AUTHOR]

In this paper, Al-Fe-Si-Zn-Cu (AA8079) matrix composites with several weight percentages of B4C (0, 5, 10, and 15) were synthesized by powder metallurgy (PM). The essential amount of powders was milled to yield different compositions such as AA8079, AA8079-5 wt.%B4C, AA8079-10 wt.%B4C, and AA8079-15 wt.%B4C. The influence of powder metallurgy parameters on properties' density, hardness, and compressive strength was examined. The green compacts were produced at three various pressures: 300 MPa, 400 MPa, and 500 MPa. The fabricated green compacts were sintered at 375 °C, 475 °C, and 575 °C for the time period of 1, 2 and 3 h, respectively. Furthermore, the sintered samples were subjected to X-ray diffraction (XRD) analysis, Energy Dispersive Analysis (EDAX), and Scanning Electron Microscope (SEM) examinations. The SEM examination confirmed the uniform dispersal of B4C reinforcement with AA8079 matrix. Corrosion behavior of the composites samples was explored. From the studies, it is witnessed that the rise in PM process parameters enhances the density, hardness, compressive strength, and corrosion resistance. [ABSTRACT FROM AUTHOR]