Search

The effects of La and Y on the microstructure and mechanical properties of cast Al-Si-Cu alloys were investigated by X-ray diffractometer (XRD), optical microscope (OM), and scanning electron microscope (SEM). The results indicated that the addition of La and Y had a great effect on the refinement of α-Al grains, the modification of eutectic Si phase, and the reduction of β-Al5FeSi length in Al-Si-Cu alloys. The A380 + 0.6 wt.% La/Y alloy exhibited the best microstructure and mechanical properties. The UTS and EI of the A380 + 0.6 wt.% La/Y alloy were 215.3 MPa and 5.1%, which were 22.9% and 37.8% higher than those of the matrix alloy, respectively. In addition, neither Al11La3 nor Al3Y generated by the addition of La and Y could not serve as the nucleation core of α-Al grains, so the grain refinement of α-Al originated from the growth limitation and constitutional supercooling. Since La and Y promote twinning generation and constitutional supercooling, the eutectic Si phase also changed from stripe-like to short fibrous or even granular and was significantly refined. Furthermore, thermodynamic calculations indicated that the Al11La3 phase was formed first and the Al3Y phase was generated on the Al11La3 phase. [ABSTRACT FROM AUTHOR]

In the present paper, the Mg-11Gd-2Y-1Zn alloys with different Al addition were fabricated by the gravity permanent mold method. The effect of Al content on microstructure evolution and mechanical properties of as-cast Mg-11Gd-2Y-1Zn alloy was studied by metallographic microscope, scanning electron microscope, XRD and tensile testing. The experimental results showed that the microstructure of as-cast Mg-11Gd-2Y-1Zn alloy consisted of α-Mg phase and island-shaped Mg3 (RE, Zn) phase. When Al element was added, Al2RE phase and lamellar Mg12REZn (LPSO) phase were formed in the Mg-11Gd-2Y-1Zn alloy. With increasing Al content, LPSO phase and Mg3 (RE, Zn) phase gradually decreased, while Al2RE phase gradually increased. There were only α-Mg and Al2RE phases in the Mg-11Gd-2Y-1Zn-5Al alloy. With the increase of Al content, the grain size decreased firstly and then increased. When the Al content was 1 wt.%, the grain size of the alloy was the minimum value (28.9 μm). The ultimate tensile strength and elongation increased firstly and then decreased with increasing Al addition. And the fracture mode changed from intergranular fracture to transgranular fracture with increasing addition. When Al addition was 1 wt.%, the maximum ultimate tensile strength reached 225.6 MPa, and the elongation was 7.8%. When the content of Al element was 3 wt.%, the maximum elongation reached 10.2% and the ultimate tensile strength was 207.7 MPa. [ABSTRACT FROM AUTHOR]

To enhance the mechanical properties (e.g., strength and elongation) of the face-centered cubic (fcc) α-phase in the Au-Cu-Al system, this study focused on the introduction of the martensite phase (doubled B19 (DB19) crystal structure of Au2CuAl) via the manipulation of alloy compositions. Fundamental evaluations, such as microstructure observations, phase identifications, thermal analysis, tensile behavior examinations, and reflectance analysis, have been conducted. The presence of fcc annealing twins was observed in both the optical microscope (OM) and the scanning electron microscope (SEM) images. Both strength and elongation of the alloys were greatly promoted while the DB19 martensite phase was introduced into the alloys. Amongst all the prepared specimens, the 47Au41Cu12Al and the 44Au44Cu12Al alloys performed the optimized mechanical properties. The enhancement of strength and ductility in these two alloys was achieved while the stress plateau was observed during the tensile deformation. A plot of the ultimate tensile strength (UTS) against fracture strain was constructed to illustrate the effects of the introduction of the DB19 martensite phase on the mechanical properties of the alloys. Regardless of the manipulation of the alloy compositions and the introduction of the DB19 martensite phase, the reflectance stayed almost identical to pure Au. [ABSTRACT FROM AUTHOR]

Serration behavior is a kind of plastic instability phenomenon of materials, which widely exists in the high-entropy alloys and has influence on microstructure and mechanical properties. In this work, the microstructure and mechanical properties of a NiCrFeCoMn high-entropy alloy (HEA) were studied under high-speed impact. The microstructure of a NiCrFeCoMn HEA were investigated by optical microscope (OM), scanning electron microscope (SEM), electron backscatter diffraction (EBSD), and transmission electron microscope (TEM). The dislocation density increased with the true strain at high-strain-rate deformation, and the dislocations can be hindered and released continually by the twin layers, resulting in serration on the true stress—true strain curve. When values of the strain rates are 1250, 2000 and 4800 s−1, the yield strength of the deformed NiCrFeCoMn HEA are 510, 525 and 680 MPa, respectively. Moreover, the fluctuation of the serration became more serious with the increasing of the strain rate. Compared with the as-cast NiCrFeCoMn HEA, the true stress—true strain curve of the deformed NiCrFeCoMn HEAwas smoother. [ABSTRACT FROM AUTHOR]