Search

The effects of La and Y on the microstructure and mechanical properties of cast Al-Si-Cu alloys were investigated by X-ray diffractometer (XRD), optical microscope (OM), and scanning electron microscope (SEM). The results indicated that the addition of La and Y had a great effect on the refinement of α-Al grains, the modification of eutectic Si phase, and the reduction of β-Al5FeSi length in Al-Si-Cu alloys. The A380 + 0.6 wt.% La/Y alloy exhibited the best microstructure and mechanical properties. The UTS and EI of the A380 + 0.6 wt.% La/Y alloy were 215.3 MPa and 5.1%, which were 22.9% and 37.8% higher than those of the matrix alloy, respectively. In addition, neither Al11La3 nor Al3Y generated by the addition of La and Y could not serve as the nucleation core of α-Al grains, so the grain refinement of α-Al originated from the growth limitation and constitutional supercooling. Since La and Y promote twinning generation and constitutional supercooling, the eutectic Si phase also changed from stripe-like to short fibrous or even granular and was significantly refined. Furthermore, thermodynamic calculations indicated that the Al11La3 phase was formed first and the Al3Y phase was generated on the Al11La3 phase. [ABSTRACT FROM AUTHOR]

To enhance the mechanical properties (e.g., strength and elongation) of the face-centered cubic (fcc) α-phase in the Au-Cu-Al system, this study focused on the introduction of the martensite phase (doubled B19 (DB19) crystal structure of Au2CuAl) via the manipulation of alloy compositions. Fundamental evaluations, such as microstructure observations, phase identifications, thermal analysis, tensile behavior examinations, and reflectance analysis, have been conducted. The presence of fcc annealing twins was observed in both the optical microscope (OM) and the scanning electron microscope (SEM) images. Both strength and elongation of the alloys were greatly promoted while the DB19 martensite phase was introduced into the alloys. Amongst all the prepared specimens, the 47Au41Cu12Al and the 44Au44Cu12Al alloys performed the optimized mechanical properties. The enhancement of strength and ductility in these two alloys was achieved while the stress plateau was observed during the tensile deformation. A plot of the ultimate tensile strength (UTS) against fracture strain was constructed to illustrate the effects of the introduction of the DB19 martensite phase on the mechanical properties of the alloys. Regardless of the manipulation of the alloy compositions and the introduction of the DB19 martensite phase, the reflectance stayed almost identical to pure Au. [ABSTRACT FROM AUTHOR]

High-strength aluminum alloy (mainly refers to the 7xxx series) is the optimum material for lightweight military equipment. However, this type of aluminum alloy is a wrought aluminum alloy. If it is directly formed by traditional casting methods, there will inevitably be problems such as coarseness, unevenness, looseness, and hot cracking in the structure, which will greatly affect the final performance of the part. Based on the internal cooling with annular electromagnetic stirring (IC-AEMS) method, a new technology of rheological die forging is developed in this paper, and the scale-reduced parts of a brake hub of Al-6.54Zn-2.40Cu-2.35Mg-0.10Zr aluminum alloy were prepared. The influence of IC-AEMS and the addition of rare element Sc on the structure and mechanical properties of the parts was studied. An optical microscope and scanning electron microscope (SEM) were used to observe the microstructure evolution, energy dispersive spectroscopy (EDS) was used to analyze the phase distribution and composition, and the mechanical properties of the parts were tested by uniaxial tensile tests. The results show that the addition of Sc element can effectively refine the grains and improve the strength and elongation of the material; the application of IC-AEMS improves the cooling rate of the melt, increases the effective nucleation rate, and the grains are further refined. Through process optimization, scale-reduced parts of a brake hub with good formability and mechanical properties can be obtained, the ultimate tensile strength is 597.2 ± 3.1 MPa, the yield strength is 517.8 ± 4.3 MPa, and the elongation is 13.7 ± 1.3%. [ABSTRACT FROM AUTHOR]

Serration behavior is a kind of plastic instability phenomenon of materials, which widely exists in the high-entropy alloys and has influence on microstructure and mechanical properties. In this work, the microstructure and mechanical properties of a NiCrFeCoMn high-entropy alloy (HEA) were studied under high-speed impact. The microstructure of a NiCrFeCoMn HEA were investigated by optical microscope (OM), scanning electron microscope (SEM), electron backscatter diffraction (EBSD), and transmission electron microscope (TEM). The dislocation density increased with the true strain at high-strain-rate deformation, and the dislocations can be hindered and released continually by the twin layers, resulting in serration on the true stress—true strain curve. When values of the strain rates are 1250, 2000 and 4800 s−1, the yield strength of the deformed NiCrFeCoMn HEA are 510, 525 and 680 MPa, respectively. Moreover, the fluctuation of the serration became more serious with the increasing of the strain rate. Compared with the as-cast NiCrFeCoMn HEA, the true stress—true strain curve of the deformed NiCrFeCoMn HEAwas smoother. [ABSTRACT FROM AUTHOR]