Search

The development of accident-tolerant materials is of great significance for preventing the zirconium–water reactions and improving the inherent safety of nuclear reactors. In this study, ZrC/Ni multilayers with average layer thicknesses of 5, 10, 20, 50, and 100 nm were designed and successfully fabricated by magnetron sputtering. The characterization results of GIXRD, SEM, AFM, TEM, etc., show that the series of films are mainly composed of alternately deposited Ni crystalline layers and ZrC amorphous layers, and the interface is clear. The films were irradiated with 50 keV He+ with a fluence of 1.0 × 1017 ions/cm2 at room temperature, and the films with different layer thicknesses kept the original phase composition. It was found that an amorphous transition layer with a thickness of about 30 nm appeared between the amorphous and crystalline interface of the 100 nm film by TEM characterization. The analysis shows that this layer is formed by the mixing of Ni and Zr elements induced by irradiation, which is not conducive to He+ migration and produces large-sized helium bubbles. The appearance of the transition layer improves the irradiation stability of the amorphous/crystalline composite film, thus providing a theoretical basis for the application of this type of material in fuel cladding. [ABSTRACT FROM AUTHOR]

In this work, the epitaxial semipolar (11–22) AlN was prepared on nonpolar m-sapphire substrate by combining sputtering and high-temperature annealing. According to our systematic measurements and analysis from XRD, Raman spectra, and AFM, the evolution of crystalline structure and morphology was investigated upon increasing AlN thickness and annealing duration. The annealing operation intensively resets the lattice and improves the crystalline quality. By varying the film thickness, the contribution from the AlN-sapphire interface on crystalline quality and lattice parameters during the annealing process was investigated, and its contribution was found to be not so obvious when the thickness increased from 300 nm to 1000 nm. When the annealing was performed under durations from 1 to 5 h, the crystalline quality was found unchanged; meanwhile, the evolution of morphology was pronounced, and it means the crystalline reorganization happens prior to morphology reset. Finally, the annealing treatment enabled a zig-zag morphology on the AlN template along the sapphire [0001] direction in the plane, which potentially affects the subsequent device epitaxy process. Therefore, our results act as important experience for the semipolar nitride semiconductor laser device preparation, particularly for the epitaxy of microcavity structure through providing the crystalline evolution. [ABSTRACT FROM AUTHOR]

The aim of this review is to summarize studies conducted by temperature-modulated differential scanning calorimetry (TMDSC) on polymer crystallization. This technique can provide several advantages for the analysis of polymers with respect to conventional differential scanning calorimetry. Crystallizations conducted by TMDSC in different experimental conditions are analysed and discussed, in order to illustrate the type of information that can be deduced. Isothermal and non-isothermal crystallizations upon heating and cooling are examined separately, together with the relevant mathematical treatments that allow the evolution of the crystalline, mobile amorphous and rigid amorphous fractions to be determined. The phenomena of 'reversing' and 'reversible' melting are explicated through the analysis of the thermal response of various semi-crystalline polymers to temperature modulation. [ABSTRACT FROM AUTHOR]

Titanium-based alloys are widely used in aerospace engineering. They have good mechanical and corrosion properties but, in some cases, the material itself or the coating should meet some additional requirements. For example, it may be a requirement of high reflectance to provide effective temperature control. Wollastonite is a promising component for reflective coatings because it improves both their whiteness and mechanical properties. This paper presents the results of studying the composition, the structure and the adhesive strength of wollastonite-containing silicate coatings to titanium substrate. The surface of titanium samples was pre-treated by laser cladding with TiC and etching to provide surface porosity. It has been shown that such treatment allows a significantly increase in the adhesive strength of the coating to the substrate. A decrease in the adhesive strength was observed on titanium samples with an excess of TiO2 on the surface. This is caused by the formation of crystalline PbTiO3 at the interface. [ABSTRACT FROM AUTHOR]