This study focuses on examining the influence of bast fibers on the flammability and thermal properties of the polylactide matrix (PLA). For this purpose, Urtica dioica and Vitis vinifera fibers were subjected to two types of modifications: mercerization in NaOH solution (M1 route) and encapsulation in an organic PLA solution (M2 route). In a further step, PLA composites containing 5, 10, and 15 wt% of unmodified and chemically treated fibers were obtained. The results of the tests show that only biocomposites containing mercerized fibers had a nearly 20% reduced flammability compared to that of PLA. Moreover, the biofiller obtained in this way belongs to the group of flame retardants that generate char residue during combustion, which was also confirmed by TGA tests. The M2 modification route allowed to achieve higher mass viscosity than the addition of unmodified and M1-modified fibers. The reason is that fibers additionally encapsulated in a polymer layer impede the mobility of the chain segments. The inferior homogenization of the M2-modified fibers in the PLA matrix translated into a longer combustion time and only a 15% reduction in flammability. [ABSTRACT FROM AUTHOR]

Despite a recent sustained preoccupation for developing biobased epoxies with enhanced applicability, such products have not been widely accepted for industry because of their inferior characteristics compared to classic petroleum-based epoxy thermosets. Therefore, significant effort is being made to improve the flame retardance of the most commonly used epoxies, such as diglycidyl ether-based bisphenol A (DGEBA), bisphenol F (DGEBF), novalac epoxy, and others, while continuously avoiding the use of hazardous halogen-containing flame retardants. Herein, a phosphorus-containing bisphenol, bis(4-(((4-hydroxyphenyl)amino)(6-oxido-6H-dibenzo[c,e][1,2]oxaphosphinin-6-yl)methyl)phenyl) phenylphosphonate (BPH), was synthesized by reacting bis(4-formylphenyl)phenylphosphonate with 4-hydroxybenzaldehyde followed by the addition of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) to the resulting azomethine groups. Environmentally friendly epoxy-based polymer thermosets were prepared by using epoxy resin as polymer matrix and a mixture of BPH and 4,4′-diaminodiphenylsulfone (DDS) as hardeners. A hyperbranched phthalocyanine polymer (HPc) and BaTiO3 nanoparticles were incorporated into epoxy resin to improve the characteristics of the final products. The structure and morphology of epoxy thermosets were evaluated by infrared spectroscopy and scanning electron microscopy (SEM), while the flammability characteristics were evaluated by microscale combustion calorimetry. Thermal properties were determined by thermogravimetric analysis and differential scanning calorimetry. The surface morphology of the char residues obtained by pyrolysis was studied by SEM analysis. [ABSTRACT FROM AUTHOR]