Search

The building and construction industry consumes a significant amount of virgin resources and minimizing the demand with alternative waste materials can provide a contemporary solution. In this study, thermal components of kraft fibres (KFs) derived from waste cardboard are investigated. The mechanical properties containing KFs within concrete composites are evaluated. Metakaolin (MK) and KFs were integrated into concrete samples as a partial substitute for cement. Silica Fume (SF) was applied to the KF (SFKFs) with a view to enhancing the fibre durability. The results indicated that there was a reduction in compressive strength of 44 and 56% when 10% raw and modified KFs were integrated, respectively. Raw, fibre and matrix-modified samples demonstrated a 35, 4 and 24% flexural strength reduction, respectively; however, the tensile strength improved by 8% when the matrix was modified using MK and SFKF. The morphology of the fibres was illustrated using a scanning electron microscope (SEM), with an energy dispersion X-ray spectroscopy (EDS) provision and Fourier transform infrared spectroscopy (FT-IR) employed to gain insights into their chemical nature. The thermal, calorimetric and combustion attributes of the fibres were measured using thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and pyrolysis combustion flow calorimetry (PCFC). SFKFs showed a lower heat release capacity (HRC), demonstrating a lower combustion propensity compared to raw KFs. Furthermore, the 45% decreased peak heat release rate (pHRR) of SFKFs highlighted the overall reduction in the fire hazards associated with these materials. TGA results also confirmed a lower mass weight loss of SFKFs at elevated temperatures, thus corroborating the results from the PCFC runs. [ABSTRACT FROM AUTHOR]

There is a need to develop new construction materials with improved mechanical performance and durability that are low-priced and have environmental benefits at the same time. This paper focuses on the rheological, mechanical, morphological, and durability properties of synthetic and steel fiber reinforced self-compacting concrete (SCC) containing 5–15% metakaolin (M) by mass as a green replacement for Portland cement. Testing of the fresh mixes included a slump-flow test, density, and porosity tests. Mechanical properties were determined through compression and flexural strength. A rapid chloride penetrability test (RCPT) and the chloride migration coefficient were used to assess the durability of the samples. A scanning electron microscope (SEM) with energy dispersion spectrometry (EDS) was used to study the concrete microstructure and the interfacial transition zone (ITZ). The results show that a combination of metakaolin and hybrid fibers has a negative effect on the flowability of SCC. In contrast, the inclusion of M and hybrid fibers has a positive effect on the compressive and flexural strength of SCC. The fracture of SCC samples without fibers was brittle and sudden, unlike the fiber-reinforced SCC samples, which could still transfer a considerable load with increasing crack mouth opening deflection. Overall, the chloride migration coefficients were reduced by up to 71% compared to the control mix. The chloride reduction is consistent with the resulting compact concrete microstructure, which exhibits a strong bond between fibers and the concrete matrix. [ABSTRACT FROM AUTHOR]