Considering the high demand for innovative solutions in medicine, a major increase in interest in biomaterials research has been noticed, with the most significant advancements in metals and their alloys. Titanium-based alloys are one of the most recognised in the scientific community but do not represent the only way to achieve optimal results. Zirconium alloys for medical applications are a novelty with significant research potential based on their outstanding properties, which may be of value for medicine. The aim of the present study was to obtain new biomedical Zr-Nb-Mo alloys with varying ratios of their respective elements—Zr and Mo—using combined powder metallurgy (PM) and arc melting (VAM) methods. The obtained samples underwent microstructure analysis using an optical microscope (OM) and a scanning electron microscope (SEM). The study of element distribution was conducted with energy dispersive spectroscopy (EDS), whereas the phase composition was determined using X-ray diffraction (XRD). Mechanical properties were examined with a Micro Combi Tester MCT3, whereas tribological properties were assessed with a TRN Tribometer, and Ringer's solution was used as a lubricant. Additionally, the wear tracks of the studied samples were observed using the SEM. The research results indicated that increased Mo content conduced to microstructure refinement and homogeneity. Furthermore, the higher content of this element contributed to the growth of the HVIT, HIT, and EIT parameters, together with the improvement in the tribological performance of the alloys. XRD analysis revealed that the obtained samples were multiphase, and raising the Mo addition promoted the formation of new phases, including a ternary phase—Zr0.9Nb0.66Mo1.44 (Fd 3 ¯ m). The chemical composition study showed uneven distribution of niobium and areas of uneven mutual distribution of zirconium and molybdenum. [ABSTRACT FROM AUTHOR]

This paper reports the results of our study on electrochemical polishing of titanium and a Ti-based alloy using non-aqueous electrolyte. It was shown that electropolishing ensured the removal of surface defects, thereby providing surface smoothing and decreasing surface roughness. The research was conducted using samples made of titanium and Ti6Al4V alloy, as well as implant system elements: implant analog, multiunit, and healing screw. Electropolishing was carried out under a constant voltage (10–15 V) with a specified current density. The electrolyte used contained methanol and sulfuric acid. The modified surface was subjected to a thorough analysis regarding its surface morphology, chemical composition, and physicochemical properties. Scanning electron microscope images and profilometer tests of roughness confirmed significantly smoother surfaces after electropolishing. The surface profile analysis of processed samples also yielded satisfactory results, showing less imperfections than before modification. The EDX spectra showed that electropolishing does not have significant influence on the chemical composition of the samples. [ABSTRACT FROM AUTHOR]

To perform quality assessments of both metal alloys and many other engineering materials, measurements of the volume fractions of phases or microstructure components are utilized. For this purpose, quantitative analysis of the evaluated components' distribution on metallographic specimens is often employed. Phases or components of the microstructure are identified based on the variation in signal received in the band of light seen. Problems with the correct identification of measurement results in this spectral band can be caused by the inhomogeneity of the etching when the alloy components are segregated. Additional uncertainty arises when the analyzed image pixel contains a boundary between grains of different phases. This article attempts to use the results of local chemical composition measurements as a source signal for quantitative evaluation of phase composition. For this purpose, quantitative maps of elemental concentration distributions, obtained with a Tescan Mira GMU high-resolution scanning electron microscope in QuantMap mode, were used as input data for the phase composition evaluation of an EN AC 46000 alloy sample. The X-ray microanalysis signal generation area may contain grains of more than one phase. Therefore, evaluation of the phase fractions in areas of individual measurements were calculated by looking for the minimum of the objective function, calculated as the sum of the squares of the deviations of the results of measurements of the concentration of individual elements from the weighted average values of solubilities of these elements in the phases. [ABSTRACT FROM AUTHOR]

Due to the poor activation performance and kinetics of Ti50V25Cr25 alloys, the element Zr was added to improve the phase structure of the alloy and achieve a high-performance hydrogen storage alloy. The Ti50−xV25Cr25Zrx (x = 0, 5, 7, and 9) system alloys were prepared by arc melting. The alloys were analyzed using an X-ray diffractometer (XRD), scanning electron microscope (SEM), and differential scanning calorimeter (DSC). The hydrogen storage capabilities of the alloys were also obtained by the Sievert volumetric method. The results indicated that the alloy with Zr added had a combination of the C15 Laves phase and the BCC phase, whereas the Zr-free alloy had a BCC single phase. The partial replacement of Zr with Ti resulted in an increase in the lattice parameters of the main phase. The hydrogen storage kinetic performance and activation of the alloys both significantly improved with an increasing Zr concentration. The time to reach 90% of the maximum hydrogen storage capacity decreased to 2946 s, 230 s, and 120 s, respectively, with the increases in Zr concentration. The initial hydrogen absorption content of the alloys increased and then decreased after the addition of the element Zr. The second phase expanded with an increasing Zr concentration, which in turn decreased the abundance of the BCC main phase. The Ti43V25Cr25Zr7 alloy showed good cycle stability and hydrogen-desorption performance, and it could absorb 90% of the maximum hydrogen storage capacity in around 230 s. The maximum hydrogen-absorption capacity of the alloy was 2.7 wt%. The diffusion activation energy of hydrogen desorption dropped from 102.67 kJ/mol to 92.62 kJ/mol. [ABSTRACT FROM AUTHOR]

The deformation aspects associated with the micro-mechanical properties of the powder laser bed fusion (P-LBF) additively manufactured stainless steel 316L were investigated in the present work. Toward that, micro-pillars were fabricated on different planes of the stainless steel 316L specimen with respect to build direction, and an in situ compression was carried out inside the chamber of the scanning electron microscope (SEM). The results were compared against the compositionally similar stainless steel 316L, which was fabricated by a conventional method, that is, casting. The post-deformed micro-pillars on the both materials were examined by electron microscopy. The P-LBF processed steel exhibits equiaxed as well as elongated grains of different orientation with the characteristics of the melt-pool type arrangements. In contrast, the cast alloy shows typical circular-type grains in the presence of micro-twins. The yield stress and ultimate compressive stress of P-LBF fabricated steel were about 431.02 ± 15.51 − 474.44 ± 23.49 MPa and 547.78 ± 29.58 − 682.59 ± 21.59 MPa, respectively. Whereas for the cast alloy, it was about 322.38 ± 19.78 MPa and 477.11 ± 25.31 MPa, respectively. Thus, the outcome of this study signifies that the AM-processed samples possess higher mechanical properties than conventionally processed alloy of similar composition. Irrespective of the processing method, both specimens exhibit ductile-type deformation, which is typical for metallic alloys. [ABSTRACT FROM AUTHOR]

Hot-dip aluminum alloy is widely used in the engineering fields. However, during the aluminum plating process, Fe inevitably enters and reaches a saturation state, which has a significant impact on the corrosion resistance and microstructure of the coating. Currently, adding Si during the hot-dip aluminum process can effectively improve the quality of the coating and inhibit the Fe-Al reaction. To understand the effect of Si content on the microstructure and electrochemical performance of Al-xSi-3.5Fe coating alloys, the microstructure and post-corrosion morphology of the alloys were analyzed using SEM (Scanning Electron Microscope) and XRD (X-ray Diffraction). Through electrochemical tests and complete immersion corrosion experiments, the corrosion resistance of the coating alloys in 3.5 wt.% NaCl was tested and analyzed. The results show that the Al-3.5Fe coating alloy mainly comprises α-Al, Al3Fe, and Al6Fe. With the increase in Si addition, the iron-rich phase changes from Al3Fe and Al6Fe to Al8Fe2Si. When the Si content reaches 4 wt.%, the iron-rich phase is Al9Fe2Si2, and the excess Si forms the eutectic Si phase with the aluminum matrix. Through SKPFM (Scanning Kelvin Probe Force Microscopy) testing, it was determined that the electrode potentials of the alloy phases Al3Fe, Al6Fe, Al8Fe2Si, Al9Fe2Si2, and eutectic Si phase were higher than that of α-Al, acting as cathode phases to the micro-galvanic cell with the aluminum matrix, and the corrosion form of alloys was mainly galvanic corrosion. With the addition of silicon, the electrode potential of the alloy increased first and then decreased, and the corrosion resistance results were synchronous with it. When the Si content is 10 wt.%, the alloy has the lowest electrode potential and the highest electrochemical activity. [ABSTRACT FROM AUTHOR]

The low strength caused by the single FCC structure of the CrMnFeCoNi high entropy alloy (HEA) limits its application in the field of coating. Here, we prepared high-entropy alloy coatings of CrMnFeCoNi with different ZrC contents on Q235 steel by a plasma transferred arc process. The effects of ZrC on the microstructure and properties of the CrMnFeCoNi HEA coating were investigated by optical microscopy, scanning electron microscope, and X-ray diffraction and by employing a potensiostat/galvanostat. The results showed that ZrC mainly existed in the coatings as a second phase, having little influence on the main crystal structure and micromorphology of the CrMnFeCoNi HEA coating. The hardness of the CrMnFeCoNi HEA coating increased with the ZrC content. ZrC can effectively improve the corrosion resistance of the CrMnFeCoNi HEA coating. In a 1 mol/L NaCl solution with 4 wt% ZrC, the annual corrosion rate was only 5.997% of that of the HEA coating. Nevertheless, the improvement in the wear resistance of CrMnFeCoNi high-entropy alloy coatings was not apparent with the addition of ZrC. Consequently, the addition of ZrC to the FeCoCrNiMn high-entropy alloy coating holds promise for applications in corrosion resistance, particularly in oceanic environments. [ABSTRACT FROM AUTHOR]

Cu additions notably strengthen Al-Mg-Si and Al-Si-Mg alloys due to the dense precipitation of quaternary nano precipitates during ageing. However, the chemical evolution and mechanical behaviors of the quaternary micro-scale Q constituent phase occurring in cast and homogenized states have rarely been studied. Meanwhile, there exists a type of AlCuMgSi cluster in the cast state, which has been regarded as Q particles. The accurate identification of phase constituents is the basis for the future design of alloys with better performance. In our work, this type of cluster was revealed to consist of α-Al, θ-Al2Cu, Q, and Si phases through micro-to-atomic scale studies using scanning and transmission electron microscopes. The skeleton of the dendrite was θ phase. The second phases in the dendritic eutectic cluster dissolved quickly during a 4 h homogenization at 550 °C. The Q phase was found to effectively absorb the Fe impurities during casting and homogenization. As a result, the formation of other harmful Fe-rich intermetallics was suppressed. These Q constituent particles were observed to break into separate pieces in an intermediately brittle manner when compressed in situ in a scanning electron microscope. These findings provide insights into the thermodynamic modeling of the Al-Mg-Si-Cu system and alloy design. [ABSTRACT FROM AUTHOR]

Chloride ions play an important role in the corrosion of bronze through their active reactivity to copper alloys. The corrosion behavior of bronze alloys in NaCl solution was investigated by using X-ray diffraction (XRD), a scanning electron microscope (SEM), and electrochemical tests, with a special emphasis on the corrosion resistance of the α and δ phases in Cu-20 wt%Sn bronze alloys. The experimental results show that the corrosion current density of Cu-20 wt%Sn bronze alloys increases from 1.1 × 10−7 A/cm2 to 2.7 × 10−6 A/cm2 with the increase in the chloride ion concentration from 10−3 mol/L to 1 mol/L. After a soaking duration of 30 days, the matrix corrosion depth reaches 50 μm. The α phase of the alloys is easily corroded in NaCl solution, while the δ phase with high Sn content has strong corrosion resistance. This study provides relevant data for the analysis and protection of ancient bronze alloys. [ABSTRACT FROM AUTHOR]

Mg-3Sn-1Mn-xLa alloy bars were prepared using backward extrusion, and the effects of the La content on the microstructures and mechanical properties of the alloy were systematically studied using an optical microscope (OM), X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), and tensile tests. The results of this research show that the Mg2Sn phases were mainly formed at the α-Mg grain boundaries and within the grains in the Mg-3Sn-1Mn alloy. After adding a certain amount of La, the plate-shaped MgSnLa compounds consisting of Mg17La2, Mg2Sn, and La5Sn3 gradually disappeared in the α-Mg matrix and grain boundaries. With an increase in La content, the Mg2Sn phase in the crystal was gradually refined and spheroidized. When the content of La reached 1.5%, the tensile strength of the alloy reached 300 Mpa and the elongation reached 12.6%, i.e., 25% and 85% increases, respectively, compared to the Mg-3Sn-1Mn alloy. The plate-shaped compound of Mg-3Sn-1Mn-1.5La had an average length of 3000 ± 50 nm, while the width was 350 ± 10 nm. Meanwhile, the extruded alloy's grain size was significantly refined, and there were many small cleavage steps and dimples in the fracture surface of the alloy. When the La content reached 2%, the alloy performance showed a downward trend due to the coarsening of the grains. The formed plate-shaped MgSnLa compounds and Mg2Sn phases were consistent with the α-Mg matrix. They effectively pinned the dislocations and grain boundaries, which is the main reason for strengthening the mechanical properties of extrusion alloys. [ABSTRACT FROM AUTHOR]

Mg77+xNi20−xLa3 (x = 0, 5, 10, 15) alloys were successfully prepared by the vacuum induction melting method. The structural characterizations of the alloys were performed by using X-ray diffraction and scanning electron microscope. The effects of nickel content on the microstructure and hydrogen storage kinetic of the as-cast alloys were investigated. The results showed that the alloys are composed of a primary phase of Mg2Ni, lamella eutectic composites of Mg + Mg2Ni, and some amount of LaMg12 and La2Mg17. Nickel addition significantly improved the hydrogen-absorption kinetic performance of the alloy. At 683 K, Mg77Ni20La3 alloy and Mg82Ni15La3 alloy underwent hydrogen absorption and desorption reactions for 2 h, respectively, and their hydrogen absorption and desorption capacities were 4.16 wt.% and 4.1 wt.%, and 4.92 wt.% and 4.69 wt.%, respectively. Using the Kissinger equation, it was calculated that the activation energy values of Mg77Ni20La3, Mg82Ni15La3, Mg87Ni10La3 and Mg92Ni5La3 alloys were in the range of 68.5~75.2 kJ/mol, much lower than 150~160 kJ/mol of MgH2. [ABSTRACT FROM AUTHOR]

Cu–9Ni–6Sn alloys have received widespread attention due to their good mechanical properties and resistance to stress relaxation in the electronic and electrical industries. The hot compression deformation behaviors of the Cu–9Ni–6Sn–0.3Mn–0.2Zn alloy were investigated using the Gleeble-3500 thermal simulator at a temperature range of 700–900 °C and a strain rate range of 0.001–1 s−1. The microstructural evolution of the Cu–9Ni–6Sn alloy during hot compression was studied by means of an optical microscope and a scanning electron microscope. The constitutive equation of hot compression of the alloy was constructed by peak flow stress, and the corresponding 3D hot processing maps were plotted. The results showed that the peak flow stress decreased with the increase in the compression temperature and the decrease in the strain rate. The hot deformation activation energy was calculated as 243.67 kJ/mol by the Arrhenius equation, and the optimum deformation parameters for the alloy were 740–760 °C and 840–900 °C with a strain rate of 0.001~0.01 s−1. According to Deform-3D finite element simulation results, the distribution of the equivalent strain field in the hot deformation samples was inhomogeneous. The alloy was more sensitive to the deformation rate than to the temperature. The simulation results can provide a guideline for the optimization of the microstructure and hot deformation parameters of the Cu–9Ni–6Sn–0.3Mn–0.2Zn alloy. [ABSTRACT FROM AUTHOR]

Ti-15%Zr alloy and Ti-15%Zr-2%Ta alloy were fabricated to be used in biomedical applications. The corrosion of these two alloys after being immersed in simulated body fluid for 1 h and 72 h was investigated. Different electrochemical methods, including polarization, impedance, and chronoamperometric current with time at 400 mV were employed. Also, the surface morphology and the compositions of its formed film were reported by the use of scanning electron microscope and energy dispersive X-ray. Based on the collected results, the presence of 2%Ta in the Ti-Zr alloy passivated its corrosion by minimizing its corrosion rate. The polarization curves revealed that adding Ta within the alloy increases the corrosion resistance as was confirmed by the impedance spectroscopy and current time data. The change of current versus time proved that the addition of Ta reduces the absolute current even at high anodic potential, 400 mV. The results of both electrochemical and spectroscopic methods indicated that pitting corrosion does not occur for both Ti-Zr and Ti-Zr-Ta alloys, even after their immersion in SBF solutions for 72 h. [ABSTRACT FROM AUTHOR]

Metal matrix composites (MMCs) are a special class of materials carrying combined properties that belongs to alloys and metals according to market demands. Therefore, they are used in different areas of industry, and the properties of this type of material are useful in engineering applications. Machining of such composites is of great importance to finalize the fabrication process with improved part quality. However, the process implies several challenges due to the complexity of the cutting processes and random material structure. The current study aims to examine machinability characteristics. Effects of turning a metal matrix composite built of Al2O3 sinter, saturated with an EN AC-44000 AC-AlSi11 alloy, are presented in this paper. In the present study, a turning process of new metal matrix composites was carried out to determine the state-of-the-art material for various engineering applications. During the turning process, the cutting forces, a tool's wear, and surface roughness were investigated. Further, the SEM (scanning electron microscope) analysis of cutting inserts was performed. The influence of MMC structure on the machining process and surface roughness was studied. The Al2O3 reinforcements were used in different graininess. Effects of conventional turning of the metal matrix composite with Al2O3 sinter of FEPA (Federation of European Producers of Abrasives) 046 and FEPA 100 grade were compared. Results analysis of these tests showed the necessity of continuing research on turning metal matrix composites built of an AlSi alloy and Al2O3 ceramic reinforcement. The study showed the properties of MMCs that influenced machinability. In this paper, the influence of feed rate's value on surface roughness was carried out. The significant tool wear during the turning of the MMC was proved. [ABSTRACT FROM AUTHOR]

High entropy alloys (HEA) are one of the modern-era alloys accelerating with greater velocity because of their excellent properties and different applications. In the present paper, we have successfully fabricated HEA (23Fe-21Cr-18Ni-20Ti-18Mn) powders by ball milling the elemental Fe, Cr, Ni, Ti, and Mn powders for 15 h. The advancement of the milling process and phase transformation of HEAs were studied by using X-ray diffraction (XRD) and scanning electron microscope (SEM). The crystallite size and the lattice strain of the HEA were calculated by using the Williamson-Hall (W-H) equation and the values were found to be 7 nm and 0.0176%, respectively. Similarly, the true lattice parameter was calculated using the Nelson–Riley (N-R) extrapolation method, and the value was found to be 3.544 Å. We have successfully investigated the electrochemical response of 15 h ball milled 23Fe-21Cr-18Ni-20Ti-18Mn HEA powders to determine the ascorbic acid (AA) using cyclic voltammetry. We have modified the carbon paste electrode with ball milled HEA of concentrations 0, 2, 4, 6, 8, and 10 mg, and among them, 8 mg HEA modified carbon paste electrode (HEA-MCPE) depicted the highest current sensitivity. We reported the effect of modifier concentration, analyte concentration, scan rate, and pH on the oxidation peak of AA. The electrochemical active surface area of carbon paste and MCPE was calculated using the Nernst equation and the values were found to be 0.0014 cm2 and 0.0027 cm2, respectively. The fabricated HEA-MCPE showed excellent current sensitivity, stability, anti-fouling, and selectivity. [ABSTRACT FROM AUTHOR]

In this study, low-iron Zn–Fe alloy coatings and pure Zn coatings, with or without trivalent chromium passivation treatment, were electrodeposited onto a sintered NdFeB magnet from a weak acid chloride bath. The surface morphology and structure of the coatings were then examined using the X-ray diffraction, a scanning electron microscope and 3D white-light interfering surface analysis. Meanwhile, the electrodeposition behavior and anti-corrosive properties of the coatings were investigated using cyclic voltammetry, potentiodynamic polarization, electrochemical impedance spectroscopy, and natural salt spray tests. The results indicate that a passivated Zn–Fe alloy coating with a 0.9 wt.% Fe content provided much better corrosion resistance than a pure Zn coating and could provide both anodic protection and physical barrier function in the NdFeB substrates. The Fe element in Zn–Fe alloy coating was predominantly in solid solution in η-phase and small amounts in elemental form, which was beneficial to acquire a compact coating and passivation film. Finally, the passivated Zn–Fe alloy coating withstood 210 h against a neutral 3.5 wt.% NaCl salt spray without any white rust, which was 3–4 times longer than the pure Zn coating. [ABSTRACT FROM AUTHOR]

The effects of La and Y on the microstructure and mechanical properties of cast Al-Si-Cu alloys were investigated by X-ray diffractometer (XRD), optical microscope (OM), and scanning electron microscope (SEM). The results indicated that the addition of La and Y had a great effect on the refinement of α-Al grains, the modification of eutectic Si phase, and the reduction of β-Al5FeSi length in Al-Si-Cu alloys. The A380 + 0.6 wt.% La/Y alloy exhibited the best microstructure and mechanical properties. The UTS and EI of the A380 + 0.6 wt.% La/Y alloy were 215.3 MPa and 5.1%, which were 22.9% and 37.8% higher than those of the matrix alloy, respectively. In addition, neither Al11La3 nor Al3Y generated by the addition of La and Y could not serve as the nucleation core of α-Al grains, so the grain refinement of α-Al originated from the growth limitation and constitutional supercooling. Since La and Y promote twinning generation and constitutional supercooling, the eutectic Si phase also changed from stripe-like to short fibrous or even granular and was significantly refined. Furthermore, thermodynamic calculations indicated that the Al11La3 phase was formed first and the Al3Y phase was generated on the Al11La3 phase. [ABSTRACT FROM AUTHOR]

High-cycle fatigue (HCF) is a critical property of metastable β Ti alloys in aerospace applications. In this work, the HCF behavior and corresponding microscale deformation mechanisms of a metastable Ti-5Al-5Mo-5V-1Cr-1Fe (Ti55511) alloy with a basket-weave structure were investigated. HCF and its deformation mechanisms of a Ti55511 alloy were systematically studied in the deformed condition by using a scanning electron microscope (SEM), a transmission electron microscope (TEM), and electron backscatter diffraction (EBSD). It was found that the Ti55511 alloy exhibited an excellent HCF strength (107 cycles, Kt = 1, R = 0.06) of 738 MPa. The fractographic investigation demonstrated that fatigue striations and secondary cracks were the main features in the crack initiation zone. Dislocation analyses indicated that the HCF deformation of the basket-weave microstructure was mainly affected by the dislocation slipping of the primary α (αp) phase. In addition, the dislocation pile-up at the αp/βtrans interface led to crack initiation. EBSD analyses indicated that the prismatic type slip system of the αp phase was preferentially activated during the HCF deformation process of the Ti55511 alloy, followed by the basal type and pyramid type systems. [ABSTRACT FROM AUTHOR]

In order to investigate the effect of Si content on the microstructures and properties of directionally solidified (DS) Fe-B alloy, a scanning electron microscope (SEM) with an energy dispersive spectrum (EDS), and X-ray diffraction have been employed to investigate the as-cast microstructures of DS Fe-B alloy. The results show that Si can strongly refine the columnar microstructures of the DS Fe-B alloy, and the columnar grain thickness of the oriented Fe2B is reduced with the increase of Si addition. In addition, Si is mainly distributed in the ferrite matrix, almost does not dissolve in boride, and seems to segregate in the center of the columnar ferrite to cause a strong solid solution strengthening and refinement effect on the matrix, thus raising the microhardness of the matrix and bulk hardness of the DS Fe-B alloy. [ABSTRACT FROM AUTHOR]

A complex concentrated noble alloy (CCNA) of equiatomic composition (Ag20Pd20Pt20Cu20Ni20–20 at. %) was studied as a potential high—performance material. The equiatomic composition was used so that this alloy could be classified in the subgroup of high—entropy alloys (HEA). The alloy was prepared by induction melting at atmospheric pressure, using high purity elements. The degree of metastability of the cast state was estimated on the basis of changes in the microstructure during annealing at high temperatures in a protective atmosphere of argon. Characterisation of the metallographically prepared samples was performed using a scanning electron microscope (SEM) equipped with an energy dispersive spectrometer (EDS), differential scanning calorimetry (DSC), and X–ray diffraction (XRD). Observation shows that the microstructure of the CCNA is in a very metastable state and multiphase, consisting of a continuous base of dendritic solidification—a matrix with an interdendritic region without other microstructural components and complex spheres. A model of the probable flow of metastable solidification of the studied alloy was proposed, based on the separation of L—melts into L1 (rich in Ni) and L2 (rich in Ag). The phenomenon of liquid phase separation in the considered CCNA is based on the monotectic reaction in the Ag−Ni system. [ABSTRACT FROM AUTHOR]

The phase structure and microstructure of Sm12Co88−xCux (x = 0, 2, 4, 6, 8, 10; at.%) as-cast alloys and melt-spun ribbons prepared via the arc-melting method and melt-spun technology were studied experimentally by X-ray diffraction (XRD) and scanning electron microscope (SEM) with energy dispersive spectroscopy (EDS). The results reveal that the Sm12Co88−xCux (x = 0) as-cast alloy contains Sm2Co17 and Sm5Co19 phases, while the Sm12Co88−xCux (x = 2) as-cast alloy is composed of Sm2Co17, Sm2Co7 and Sm(Co, Cu)5 phases. Sm2Co17 and Sm(Co, Cu)5 phases are detected in Sm12Co88−xCux (x = 4, 6, 8, 10) as-cast alloys. Meanwhile, Sm12Co88−xCux ribbons show a single SmCo7 phase, which is still formed in the ribbons annealed at 1023 K for one hour. After annealed at 1123 K for two hours, cooled slowly down to 673 K at 0.5 K/min and then kept for four hours, the ribbons are composed of Sm2Co17 and Sm(Co, Cu)5 phases. The magnetic measurements of Sm12Co88−xCux ribbons were performed by vibrating sample magnetometer (VSM). The results exhibit that the maximum magnetic energy product ((BH)max), the coercivity (Hcj) and the remanence (Br) of the Sm12Co88−xCux ribbons increase generally with the increase in Cu substitution. In particular, the magnetic properties of the ribbons annealed at 1123 K and 673 K increase significantly with the increase in Cu substitution, resulting from the increase in the volume fraction of the formed Sm(Co, Cu)5 phase after heat treatment. [ABSTRACT FROM AUTHOR]

High-entropy alloys are a new generation of materials that have attracted the interest of numerous scientists because of their unusual properties. It seems interesting to use these alloys in biomedical applications. However, for this purpose, the basic condition of corrosion resistance must be fulfilled. In this article, selected corrosion properties of self-composed high-entropy alloys are investigated and compared with conventional biomedical alloys, that is titanium alloys and stainless steels. Corrosive parameters were determined using the potentiodynamic method. X-ray diffraction studies were performed to characterize the crystal structures. Microstructures of the prepared materials were examined using a scanning electron microscope, and surface hardness was measured by the Vickers method. The results show that investigated high-entropy alloys are characterized by simple structures. Three out of four tested high-entropy alloys had better corrosion properties than conventional implant alloys used in medicine. The Al0.7CoCrFeNi alloy was characterized by a corrosion potential of −224 mV and a corrosion current density of 0.9 μA/cm2; CoCrFeNiCu by −210 mV and 1.1 μA/cm2; TiAlFeCoNi by −435 mV and 4.6 μA/cm2; and Mn0.5TiCuAlCr by −253 mV and 1.3 μA/cm2, respectively. Therefore, the proposed high-entropy alloys can be considered as potential materials for biomedical applications, but this requires more studies to confirm their biocompatibility. [ABSTRACT FROM AUTHOR]

With the development and wide application of nickel-based single-crystal superalloys, the effect of Ru on the microstructure stability and high-temperature properties of superalloys is becoming increasingly important. In this study, the effect of Ru on the evolution of the γ′ phase in Ni-Al-Ru ternary alloys during aging treatment was analyzed, using a scanning electron microscope and transmission electron microscope, combined with energy-dispersive spectroscopy. The relationship between chemical partition behavior and γ/γ′ lattice misfit was investigated in detail. During the aging process, Ru addition suppressed the growth rate and rafting process of γ′ precipitates, while the effect of Ru on hindering γ′ phase growth was reduced when the Ru content was over 3 at%. Ru preferentially partitioned to the γ phase, and its partitioning ratio to the γ phase increased with a variation in Ru content from 1 at% to 3 at% and decreased for the NiAl6Ru alloy. Additionally, the lattice misfit of all alloys was positive and reduced with the increase in Ru content, which hindered the Ru atoms to diffuse into the γ phase and promoted the shape of γ′ precipitates to change from cubic to spherical. [ABSTRACT FROM AUTHOR]

The improvement of the surface qualities and surface hardening of precipitation hardened martensitic stainless steel 17-4PH was achieved by the plasma-transferred arc welding (PTAW) process deposited with Co-based alloy. The microstructure of the heat affected zone (HAZ) and base metal were characterized by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that there are obvious microstructural differences between the base metal and HAZ. For example, base material is transformed from lath martensite to austenite due to the heateffect of the welding process. On the other hand, the precipitate in the matrix (bar-like shape Cr7C3 phase with a width of about one hundred nanometres and a length of hundreds of nanometres) grows to a rectangular appearance with a width of about two hundred nanometres and a length of about one micron. Stacking fault could also be observed in the Cr7C3 after PTAW. The above means that welding can obviously improve the surface qualities. [ABSTRACT FROM AUTHOR]

In this study, a Mg-9Gd-4Y-2Zn-0.5Zr (wt.%) alloy was subjected, after solution treatment, to hot compression deformation at different temperatures (350 °C, 400 °C and 450 °C) and different strain rates (0.001 s−1, 0.01 s−1, 0.1 s−1 and 0.5 s−1) on a Gleeble-3800 thermal simulator. The evolution of the stress–strain curves under different conditions was compared. The changes in microstructure caused by the different deformation parameters and the change law of the long-period stacking-ordered (LPSO) phase during compression were observed and analyzed by optical microscope (OM) and scanning electron microscope (SEM). The results show that with the increase in the deformation temperature and the decrease in the strain rate, the degree of dynamic recrystallization (DRX) gradually increased, and the morphology of the phase also changed through, for example, twist fracture. The continuous dynamic recrystallization (CDRX) and discontinuous dynamic recrystallization (DDRX) mechanisms activated during the thermal deformation process can effectively refine the grains and weaken the texture in the alloy. [ABSTRACT FROM AUTHOR]

The effect of initial Fe content on the iron removal efficiency, morphology evolution of the Fe-rich phase and the mechanical properties of the recycled Al-7Si-xFe-1.2xMn alloy during melt holding was studied using an optical microscope (OM), scanning electron microscope (SEM) and tensile testing. The results show that with the increase of the initial Fe content, the residual Fe concentration of the alloys gradually increased, and the corresponding removal efficiency of Fe gradually was increased to 77.67%. The type of Fe-rich phase in the alloys changes from α-Al15(FeMn)3Si2 to a mixture of α-Al15(FeMn)3Si2 and β-Al5FeSi, and its morphological evolution is as follows: coarse Chinese-script + polygon → dense Chinese-script + polygon → polygonal + dense Chinese-script + plate-like. Furthermore, the morphology of the Fe-rich phase in the slag changes from a polygonal shape to an irregular shape with a two-layer structure. The formation and increase of the inner layer with high Mn-content in the irregular-shape phase is the main reason for the increasing residual Fe content. The plasticity of the alloy increases obviously with the increase of the initial Fe content, but the formation of the β-Al5FeSi with plate-like morphology in higher Fe-containing alloy may hinder further improvement of the plasticity. [ABSTRACT FROM AUTHOR]

High strength and toughness are achieved in the Mg-4.96Gd-2.44Y-0.43Zr alloy by multidirectional impact forging (MDIF). The forged sample has a fine-grained microstructure with an average grain size of ~5.7 µm and a weak non-basal texture, and it was characterized by an optical microscope (OM), scanning electron microscope (SEM), and electron back-scattering diffraction (EBSD). Tensile results exhibit the tensile yield strength (TYS) and static toughness (ST) of as-homogenized alloy dramatically increased after forging and aging, i.e., the TYS increased from 135 − 5 + 4 MPa to 337 − 2 + 2 MPa, and the ST enhanced from 22. 0 − 0.5 + 0.3 MJ/m3 to 50. 4 − 5.4 + 5.3 MJ/m3. Specifically, the forged Mg-Gd-Y-Zr alloy owns higher TYS than that of commercial rolled WE54 (Mg-5.25Y-3.5Nd-0.5Zr) and WE43 (Mg-4.0Y-3.0Nd-0.5Zr) alloys. [ABSTRACT FROM AUTHOR]

Titanium (Ti)-based alloys (e.g., Ti6Al4V) are widely used in orthopedic implant applications owing to their excellent mechanical properties and biocompatibility. However, their corrosion resistance needs to be optimized. In addition, the presence of aluminum and vanadium cause alzheimer and cancer, respectively. Therefore, in this study, titanium-based alloys were developed via powder metallurgy route. In these alloys, the Al and V were replaced with tin (Sn) which was the main aim of this study. Four sets of samples were prepared by varying Sn contents, i.e., 5 to 20 wt. %. This was followed by characterization techniques including laser particle analyzer (LPA), X-ray diffractometer (XRD), scanning electron microscope (SEM), computerized potentiostate, vicker hardness tester, and nanoindenter. Results demonstrate the powder sizes between 50 and 55 µm exhibiting very good densification after sintering. The alloy contained alpha at all concentrations of Sn. However, as Sn content in the alloy exceeded from 10 wt. %, the formation of intermetallic compounds was significant. Thus, the presence of such intermetallic phases are attributed to enhanced elastic modulus. In particular, when Sn content was between 15 and 20 wt. % a drastic increase in elastic modulus was observed thereby surpassing the standard/reference alloy (Ti6Al4V). However, at 10 wt. % of Sn, the elastic modulus is more or less comparable to reference counterpart. Similarly, hardness was also increased in an ascending order upon Sn addition, i.e., 250 to 310 HV. Specifically, at 10 wt. % Sn, the hardness was observed to be 250 HV which is quite near to reference alloy, i.e., 210 HV. Moreover, tensile strength (TS) of the alloys were calculated using hardness values since it was very difficult to prepare the test coupons using powders. The TS values were in the range of 975 to 1524 MPa at all concentrations of Sn. In particular, the TS at 10 wt. % Sn is 1149 MPa which is comparable to reference counterpart (1168 MPa). The corrosion rate of Titanium-Sn alloys (as of this study) and reference alloy, i.e., Ti6Al4V were also compared. Incorporation of Sn reduced the corrosion rate at large than that of reference counterpart. In particular, the trend was in decreasing order as Sn content increased from 5 to 20 wt. %. The minimum corrosion rate of 3.65 × 10−9 mm/year was noticed at 20 wt. % than that of 0.03 mm/year of reference alloy. This shows the excellent corrosion resistance upon addition of Sn at all concentrations. [ABSTRACT FROM AUTHOR]

The AlSi10Mg alloy is characterized by a high strength-to-weight ratio, good formability, and satisfying corrosion resistance; thus, it is very often used in automotive and aerospace applications. However, the main limitation of using this alloy is its low yield strength and ductility. The equal-channel angular pressing is a processing tool that allows one to obtain ultrafine-grained or nanomaterials, with exceptional mechanical and physical properties. The purpose of the paper was to analyze the influence of the ECAP process on the structure and hardness of the AlSi10Mg alloy, obtained by the selective laser melting process. Four types of samples were examined: as-fabricated, heat-treated, and subjected to one and two ECAP passes. The microstructure analysis was performed using light and electron microscope systems (scanning electron microscope and transmission electron microscope). To evaluate the effect of ECAP on the mechanical properties, hardness measurements were performed. We found that the samples that underwent the ECAP process were characterized by a higher hardness than the heat-treated sample. It was also found that the ECAP processing promoted the formation of structures with semicircular patterns and multiple melt pool boundaries with a mean grain size of 0.24 μm. [ABSTRACT FROM AUTHOR]

In the present paper, the Mg-11Gd-2Y-1Zn alloys with different Al addition were fabricated by the gravity permanent mold method. The effect of Al content on microstructure evolution and mechanical properties of as-cast Mg-11Gd-2Y-1Zn alloy was studied by metallographic microscope, scanning electron microscope, XRD and tensile testing. The experimental results showed that the microstructure of as-cast Mg-11Gd-2Y-1Zn alloy consisted of α-Mg phase and island-shaped Mg3 (RE, Zn) phase. When Al element was added, Al2RE phase and lamellar Mg12REZn (LPSO) phase were formed in the Mg-11Gd-2Y-1Zn alloy. With increasing Al content, LPSO phase and Mg3 (RE, Zn) phase gradually decreased, while Al2RE phase gradually increased. There were only α-Mg and Al2RE phases in the Mg-11Gd-2Y-1Zn-5Al alloy. With the increase of Al content, the grain size decreased firstly and then increased. When the Al content was 1 wt.%, the grain size of the alloy was the minimum value (28.9 μm). The ultimate tensile strength and elongation increased firstly and then decreased with increasing Al addition. And the fracture mode changed from intergranular fracture to transgranular fracture with increasing addition. When Al addition was 1 wt.%, the maximum ultimate tensile strength reached 225.6 MPa, and the elongation was 7.8%. When the content of Al element was 3 wt.%, the maximum elongation reached 10.2% and the ultimate tensile strength was 207.7 MPa. [ABSTRACT FROM AUTHOR]

The refining performance of Al-Ti-C master alloys is substantially compromised by the inferior wettability between graphite and molten aluminum. In this paper, the Al-5Ti-0.25C master alloy was successfully prepared by reacting Ti machining chips, graphite, and molten aluminum. In order to determine a simple method of improving the wettability, the optimal preparation process and phase transformation of the Al-5Ti-0.25C master alloy were investigated using an optical microscope, X-ray diffractometer, and scanning electron microscope equipped with an energy dispersive spectrometer. The results show that the feeding method using a prefabricated block made from Ti chips, Al chips, and graphite effectively improves the wettability between graphite and molten aluminum and increases the recovery rate of graphite. When the reaction temperature is low (1223 K), the agglomeration of TiAl3 is caused. When the reaction temperature is high (1373 K), the morphology of TiAl3 changes from block-like to needle-like and increases its size. Further, a short reaction time (30 min) results in the incomplete dissolution of the Ti chips, while a long reaction time (90 min) causes the TiAl3 to transform into needle-like morphologies. The microstructural observation of undissolved Ti chips shows that TiAl3 and TiC are formed around it, which proves the transformation of Ti chips to TiAl3 and TiC. In addition, the enrichment of TiC and Al4C3 was observed in the vicinity of TiAl3, and a reaction model for the formation of TiC from the reaction of Al4C3 and TiAl3 was presented. [ABSTRACT FROM AUTHOR]

The microstructural and wear properties of laser-cladding WC/Ni-based layer on Al–Si alloy were investigated by scanning electron microscope (SEM), X-ray diffraction (XRD), energy dispersive spectrometer (EDS) and wear-testing. The results show that, compared with the original specimen, the microhardness and wear resistance of the cladding layer on an Al–Si alloy were remarkably improved, wherein the microhardness of the layer achieved 1100 HV and the average friction coefficient of the layer was barely 0.14. The mainly contributor to such significant improvement was the generation of a WC/Ni-composite layer of Al–Si alloy during laser cladding. Two types of carbides, identified as M7C3 and M23C6, were found in the layer. The wear rate of the layer first increased and then decreased with the increase in load; when the load was 20 N, 60 N and 80 N, the wear rate of layer was1.89 × 10−3 mm3·m−1, 3.73 × 10−3 mm3·m−1 and 2.63 × 10−3 mm3·m−1, respectively, and the average friction coefficient (0.14) was the smallest when the load was 60 N. [ABSTRACT FROM AUTHOR]

Newly developed Zn-Mn-Mg alloys can be invoked as biomedical materials because of their excellent mechanical properties. However, the corrosion behavior of Zn-Mn-Mg alloys was still lacking in research. It had grown to be a hot research topic to improve the corrosion behavior of Zn alloys by surface treatment to meet the application of degradable Zn alloys in biomedical applications. Micro arc oxidation (MAO) is a simple and effective method to improve the corrosion behavior of the alloy. MAO coatings were successfully prepared on the surface of Zn-Mn-Mg alloys by MAO in silicate-based solutions with different NaF concentrations. The microstructure and phase composition of MAO coatings prepared on Zn-Mn-Mg alloys with different NaF concentrations in the electrolyte was examined by a scanning electron microscope and X-ray diffraction. The results showed that the MAO coatings are porous and mainly composed of ZnO. With the increasing NaF concentration in the electrolyte, the average thickness increases. The distribution of the micro/nanopores was uniform, and the pore size ranged from the submicron scale to several micrometers after MAO treatment in the electrolyte containing different concentrations of NaF. Potential dynamic polarization curves and electrochemical impedance spectroscopy were employed to assess the corrosion behavior of MAO coatings in Hank's solution. The highest corrosion rate can be achieved after MAO treatment, with an electrolyte concentration of 1.5 g/L NaF in Hank's solution. These results indicated that MAO coating can accelerate the corrosion resistance of a Zn-Mn-Mg alloy. [ABSTRACT FROM AUTHOR]

The paper presents a comparison of the results of the corrosion resistance for three Fe-B-Co-Si-based newly developed alloys with the addition of Nb and V. The corrosion performance differences and microstructure variations were systematically studied using scanning electron microscope, electric corrosion equipment, X-ray diffractometer, and differential calorimeter. It has been shown that each alloying addition increased the corrosion resistance. The highest corrosion resistance obtained by potentiodynamic polarization was found for the alloy with both Nb and V addons (Fe57Co10B20Si5Nb4V4) and lowest in the case of the basic four-element Fe62Co15B14Si9 material. This shows that the proper choice of additions is of significant influence on the final performance of the alloy and allows tailoring of the material for specific applications. [ABSTRACT FROM AUTHOR]

To enhance the mechanical properties (e.g., strength and elongation) of the face-centered cubic (fcc) α-phase in the Au-Cu-Al system, this study focused on the introduction of the martensite phase (doubled B19 (DB19) crystal structure of Au2CuAl) via the manipulation of alloy compositions. Fundamental evaluations, such as microstructure observations, phase identifications, thermal analysis, tensile behavior examinations, and reflectance analysis, have been conducted. The presence of fcc annealing twins was observed in both the optical microscope (OM) and the scanning electron microscope (SEM) images. Both strength and elongation of the alloys were greatly promoted while the DB19 martensite phase was introduced into the alloys. Amongst all the prepared specimens, the 47Au41Cu12Al and the 44Au44Cu12Al alloys performed the optimized mechanical properties. The enhancement of strength and ductility in these two alloys was achieved while the stress plateau was observed during the tensile deformation. A plot of the ultimate tensile strength (UTS) against fracture strain was constructed to illustrate the effects of the introduction of the DB19 martensite phase on the mechanical properties of the alloys. Regardless of the manipulation of the alloy compositions and the introduction of the DB19 martensite phase, the reflectance stayed almost identical to pure Au. [ABSTRACT FROM AUTHOR]

In this investigation, the extensive wear behaviour of materials was studied using SiC reinforced magnesium alloy composites fabricated through the stir casting process. The wear properties of AZ91 alloy composites with a small variation (i.e., 3%, 6%, 9% and 12%) of SiC particulates were evaluated by varying the normal load with sliding velocity and sliding distance. The worn surfaces were examined by scanning electron microscope to predict the different wear mechanisms on the pin while sliding on the hard disk in the dry sliding wear test condition. The microhardness of the SiC reinforced AZ91 composites was found to be more than the un-reinforced AZ91 alloy. Pins tested at load 19.62 N, and 2.6 m/s exhibited a series of short cracks nearly perpendicular to the sliding direction. At higher speed and load, the oxidation and delamination were observed to be fully converted into adhesion wear. Abrasion, oxidation, and delamination wear mechanisms were generally dominant in lower sliding velocity and lower load region, while adhesion and thermal softening/melting were dominant in higher sliding velocity and loads. The wear rate and coefficient of friction of the SiC reinforced composites were lower than that of the unreinforced alloy. This is due to the fact of higher hardness exhibited by the composites. The wear behaviour at the velocity of 1.39 m/s was dominated by oxidation and delamination wear, whereas at the velocity of 2.6 m/s the wear behaviour was dominated by abrasion and adhesion wear. It was also found that the plastic deformation and smearing occurred at higher load and sliding velocity. [ABSTRACT FROM AUTHOR]

In this study, the influence of alloying elements on the mechanical properties of iron borides FeB and Fe2B formed in Fe-B-X (X = C, Cr, Mn, V, W, Mn + V) alloys were evaluated using instrumented indentation measurement. The microstructural characterization of the alloys was performed by means of X-ray diffraction and scanning electron microscope equipped with an energy dispersive X-ray analyzer. The fraction of the phases present in the alloys was determined either by the lever rule or by image analysis. The hardest and stiffest FeB formed in Fe-B-X (X = C, Cr, Mn) alloys was observed in the Fe-B-Cr alloys, where indentation hardness of HIT = 26.9 ± 1.4 GPa and indentation modulus of EIT = 486 ± 22 GPa were determined. The highest hardness of Fe2B was determined in the presence of tungsten as an alloying element, HIT = 20.8 ± 0.9 GPa. The lowest indentation hardness is measured in manganese alloyed FeB and Fe2B. In both FeB and Fe2B, an indentation size effect was observed, showing a decrease of hardness with increasing indentation depth. [ABSTRACT FROM AUTHOR]

Serration behavior is a kind of plastic instability phenomenon of materials, which widely exists in the high-entropy alloys and has influence on microstructure and mechanical properties. In this work, the microstructure and mechanical properties of a NiCrFeCoMn high-entropy alloy (HEA) were studied under high-speed impact. The microstructure of a NiCrFeCoMn HEA were investigated by optical microscope (OM), scanning electron microscope (SEM), electron backscatter diffraction (EBSD), and transmission electron microscope (TEM). The dislocation density increased with the true strain at high-strain-rate deformation, and the dislocations can be hindered and released continually by the twin layers, resulting in serration on the true stress—true strain curve. When values of the strain rates are 1250, 2000 and 4800 s−1, the yield strength of the deformed NiCrFeCoMn HEA are 510, 525 and 680 MPa, respectively. Moreover, the fluctuation of the serration became more serious with the increasing of the strain rate. Compared with the as-cast NiCrFeCoMn HEA, the true stress—true strain curve of the deformed NiCrFeCoMn HEAwas smoother. [ABSTRACT FROM AUTHOR]

Micro-turning is a micro-mechanical cutting method used to produce small diameter cylindrical parts. Since the diameter of the part is usually small, it may be a little difficult to improve the surface quality by a second operation, such as grinding. Therefore, it is important to obtain the good surface finish in micro turning process using the ideal cutting parameters. Here, the multi-objective optimization of micro-turning process parameters such as cutting speed, feed rate and depth of cut were performed by response surface method (RSM). Two important machining indices, such as surface roughness and material removal rate, were simultaneously optimized in the micro-turning of a Ti6Al4V alloy. Further, the scanning electron microscope (SEM) analysis was done on the cutting tools. The overall results depict that the feed rate is the prominent factor that significantly affects the responses in micro-turning operation. Moreover, the SEM results confirmed that abrasion and crater wear mechanism were observed during the micro-turning of a Ti6Al4V alloy. [ABSTRACT FROM AUTHOR]

The effects of solute element content and cooling rate on the morphology of Al6Mn phase in suction casting Al–Mn alloys were investigated by transmission electron microscope, scanning electron microscope, and X-ray diffractometer. Results show that Al6Mn dendrite morphology with different degrees of development can occur in the microstructure of as-cast Al–Mn alloys. For the Al–4 wt.% Mn alloy, there are small amounts of block Al6Mn crystals at the center of sample, while we see a block Al6Mn phase and a feathery Al6Mn phase in the sample of Al–6 wt.% Mn alloy. Moreover, the block Al6Mn phases in the Al–8 wt.% Mn alloy disappear, and only snowflake-like Al6Mn phases play a dominant role in the microstructure. However, with an increase in Mn content to 10 wt.%, more dendritic trunks are formed, and secondary dendrite arms are degraded more seriously due to the formation of an icosahedral quasicrystal in suction casting. In addition to the effect of Mn content on Al6Mn morphology, with the increase in cooling rate from the center to the edge of samples, the outline diameter of equiaxed dendrite decreases. The evolution of Al6Mn dendrite morphology and the formation of quasicrystal are further discussed. [ABSTRACT FROM AUTHOR]

A deleterious Laves phase forms in the solidified structure of Inconel 718 (IN718) alloy during laser cladding. However, effective removal methods have not yet been identified. In this study, we first added the IN718 alloy cladding layers with a trace amount of vanadium (V, 0.066 wt.%). Then, we studied the solidification structure of cladding layers using a confocal laser scanning microscope and scanning electron microscopy. The microstructure and Laves phase morphology were investigated. The distribution of niobium (Nb) was observed by experiment as well. We found that V is evenly distributed in dendrites and interdendritic zones. A more refined dendrite structure, reduced second dendrite arm spacing and lower volume fraction of Laves phase were observed in the solidification structure. The results of linear energy-dispersive X-ray spectroscopy (EDS) indicate that the concentration of Nb decreases with an increasing of the distance from the Laves phase. The V-containing sample displayed a relatively slower decreasing tendency. The IN718 alloy sample was harder with the addition of V. In addition, the porosity of the sample decreased compared with the blank sample. The presented findings outline a new method to inhibit the Nb segregation in IN718 alloy during laser cladding, providing reference significance for improving the performance of IN718 alloy samples during actual processing. [ABSTRACT FROM AUTHOR]

According to the stoichiometric ratios of Mo-10Si-7B, Mo-12Si-8.5B, Mo-14Si-9.8B, and Mo-25Si-8.5B, some new Mo-Si-B alloys doped with 0.3 wt % lanthanum (III) oxide (La2O3) were prepared via liquid-liquid (L-L) doping, mechanical alloying (MA), and hot-pressing (HP) sintering technology. The phase-composition and microstructure were investigated by X-ray diffraction (XRD) and scanning electron microscope (SEM). The worn surfaces of the plate specimens were studied by confocal laser scanning microscopy (CLSM). Then, the tribological properties of Mo-Si-B alloy doped with sliding plate specimens of 0.3 wt % La2O3 were investigated against the Si3N4 ball specimens. The friction coefficients of Mo-Si-B alloys decreased and the wear rates of the alloys increased with test load. The high-temperature friction and wear behavior of Mo-Si-B alloy are related to the surface-oxidation and contact-deformation of the alloy at a high temperature. The low friction coefficients and the reduced wear rates are thought to be due to the formation of low friction MoO3 films. MoO3 changed the contact state of the friction pairs and behaved as lubricating films. [ABSTRACT FROM AUTHOR]