This study investigated changes in the crystal lattice, tribological properties and friction mechanism of AISI 316 steel irradiated with swift 160 MeV xenon ions. The irradiation process caused the increased roughness of the steel surface and the swelling of the material. The thickness of the irradiated layer increased by about 13 nm. Following irradiation with the fluences 2.5 × 1014 and 3.2 × 1014 (Xe24+/cm2), martensite formed in the surface layer. Fluctuating changes were also observed with respect to the coefficient of friction and the degree of wear of the AISI 316 steel samples. Irradiation also increased the microhardness of the steel.

This is the first study ever to show the impact of high-energy 160 MeV xenon ion irradiation on the properties of 100Cr6 bearing steel. The projected range (Rp) of xenon ions is 8.2 µm. Fluence-dependent variations in the coefficient of friction and wear of the 100Cr6 steel material have been observed. These changes correlate with shifts in the crystal lattice constant and variations in the oxygen, carbon, and iron content in the wear track. Fluence-dependent changes in these parameters have been observed for the first time. Irradiation reduces stresses in the crystal lattice, leading to crystallite size increase. The modifications in the properties of 100Cr6 steel result from radiation-induced defects caused by electronic ion stopping. The degree of these modifications depends on the applied irradiation fluence. Furthermore, the use of a higher irradiation fluence value appears to mitigate the effects produced by a lower fluence.