In this work, porous Al alloy-based composites with varying Ti-coated diamond contents (0, 4, 6, 12 and 15 wt.%) were prepared, employing the powder metallurgy route and using a fixed amount (25 wt.%) of polymethylmethacrylate (PMMA) as a space holder. The effects of the varying wt.% of diamond particles on the microstructure, porosities, densities and compressive behaviors were systematically evaluated. The microstructure study revealed that the porous composites exhibited a well-defined and uniform porous structure with good interfacial bonding between the Al alloy matrix and diamond particles. The porosities ranged from 18% to 35%, with an increase in the diamond content. The maximum value of plateau stress of 31.51 MPa and an energy absorption capacity of 7.46 MJ/m3 were acquired for a composite with 12 wt.% of Ti-coated diamond content; beyond this wt.%, the properties declined. Thus, the presence of diamond particles, especially in the cell walls of porous composites, strengthened their cell walls and improved their compressive properties.

The compressive properties of powder metallurgy (PM)-based porous aluminum (Al) composites were optimized at three levels based on the following parameters: titanium (Ti)-coated diamond content, polymethylmethacrylate (PMMA) particle content, and PMMA particle size. A 3 × 3 matrix was used in the experimental design of an L9 orthogonal array to get nine sets of combinations. These nine compositions were then tested and analyzed for density, porosity, plateau stress, and energy absorption capacity. The effect of individual input parameters was assessed using the Taguchi-based means ratio and analysis of variance (ANOVA). The main effect plots articulated the optimal parameter levels for achieving maximum compressive property values (plateau stress and energy absorption capacity). The findings show that diamond content and PMMA particle size have a major impact on compressive properties. The ANOVA analysis yielded similar results, with diamond content accounting for the greatest value. Further, the response optimization of compressive properties revealed that maximum values could be obtained at optimum parameters: diamond content of 12 wt.%, PMMA particle size of 150 μm, and PMMA particle content of 25 wt.%. Confirmation tests on the optimal parameters revealed improved results as well as some minor errors and deviations, indicating that the chosen parameters are critical for controlling the compressive properties of Al composites.