The compressive strength parallel to grain of earlywood and latewood from the yellow pine sapwood and heartwood areas was examined in the study. The structure of the basic structural elements of wood - tracheids, which conduct water and/or perform the mechanical function - was also characterized. The compressive strength parallel to grain of latewood in the sapwood area was found to be twice as high as the compressive strength parallel to grain of earlywood. The compressive strength parallel to grain of latewood in the heartwood area, on the other hand, was found to be 2,5 times higher than the compressive strength parallel to grain of earlywood. This was due to the density of particular areas of wood and the dimensions of structural elements - tracheids. In the sapwood area, the density of latewood was ca. twice as high as the density of earlywood. Similar relationships were found for heartwood. The thickness of latewood tracheids was found to be 1,5 times greater than the thickness of earlywood tracheids. These relationships were observed in sapwood and heartwood. The diameter of earlywood tracheids in radial direction was twice as large as the diameter of latewood tracheids. These relationships were observed in yellow pine sapwood and heartwood.

The present work regards an attempt to obtain particles from the post-industrial pine plywood in a single-shaft shredder. A screen mesh size determines the wood particles characteristics. In the work 10–, 14–, 25– and 38–mm mesh size screens were used. The urea-formaldehyde (UF) and phenol-formaldehyde (PF) bonded plywood were shredded separately, so that the effect of the binder type could be analyzed. The determined fractional composition, bulk density, dimensions and surface area of the particles were compared to the industrial virgin pine particles dedicated to the core layer of particleboards. The results showed that the particles obtained from a 14–mm mesh screen exhibited properties closest to those found for the virgin particles.

The study examined the influence of ultraviolet radiation on the colour of thermo-mechanically modified beech (Fagus sylvatica ) and oak (Quercus robur). The wood colour parameters were measured using the mathematical CIE L*a*b* and L*C*h colour space models. The higher the temperature of thermo-mechanical treatment, the least susceptible beech and oak wood was to a change in L*, a* and b* under the influence of light irradiation. The greatest changes in the colour of non-densified and densified beech and oak wood occurred after 20 h of light irradiation. The higher the temperature of thermo-mechanical treatment, the smaller were the total changes in the colour of beech and oak wood under the influence of ultraviolet radiation. The total changes in the colour of beech densified at temperatures of 100°C and 150°C that took place under the influence of ultraviolet radiation were twice as high as in the case of densified oak wood. The colour of oak wood modified at a temperature of 200°C did not change significantly in 300 h of light irradiation.