Search

Functional, hierarchically mesostructured nonwovens are of fundamental importance because complex fiber morphologies increase the active surface area and functionality allowing for the effective immobilization of metal nanoparticles. Such complex functional fiber morphologies clearly widen the property profile and enable the preparation of more efficient and selective filter media. Here, we demonstrate the realization of hierarchically mesostructured nonwovens with barbed wire-like morphology by combining electrospun polystyrene fibers, decorated with patchy worm-like micelles, with solution-processed supramolecular short fibers composed of 1,3,5-benzenetricarboxamides with peripheral N,N-diisopropylaminoethyl substituents. The worm-like micelles with a patchy microphase-separated corona were prepared by crystallization-driven self-assembly of a polyethylene based triblock terpolymer and deposited on top of the polystyrene fibers by coaxial electrospinning. The micelles were designed in a way that their patches promote the directed self-assembly of the 1,3,5-benzenetricarboxamide and the fixation of the supramolecular nanofibers on the supporting polystyrene fibers. Functionality of the mesostructured nonwoven is provided by the peripheral N,N-diisopropylaminoethyl substituents of the 1,3,5-benzenetricarboxamide and proven by the effective immobilization of individual palladium nanoparticles on the supramolecular nanofibers. The preparation of hierarchically mesostructured nonwovens and their shown functionality demonstrate that such systems are attractive candidates to be used for example in filtration, selective separation and heterogenous catalysis.

Gold nanoparticles (AuNP) with pyridyl end-capped polystyrenes (PS-4VP) as "quasi-monodentate" ligands self-assemble into ordered PS-4VP/AuNP nanostructures with 3D hexagonal spatial order in the dried solid state. The key for the formation of these ordered structures is the modulation of the ratio AuNP versus ligands, which proves the importance of ligand design and quantity for the preparation of novel ordered polymer/metal nanoparticle conjugates. Although the assemblies of PS-4VP/AuNP in dispersion lack in high dimensional order, strong plasmonic interactions are observed due to close contact of AuNP. Applying temperature as an external stimulus allows the reversible distortion of plasmonic interactions within the AuNP nanocomposite structures, which can be observed directly by naked eye. The modulation of the macroscopic optical properties accompanied by this structural distortion of plasmonic interaction opens up very interesting sensoric applications.

In this paper, preparation method and actuation properties of an innovative composite membrane composed of thermo- and pH-responsive poly(N-isopropylacrylamide-co-acrylic acid) fibers (average diameter ≈ 905 nm) embedded within a passive thermoplastic polyurethane (TPU) matrix at different angles with degree of alignment as high as 98% are presented. The composite membrane has a gradient of TPU along the thickness. It has the capability of temperature- and pH-dependent direction-, and size-controlled actuation in few minutes. The stresses generated at the responsive fiber and nonresponsive matrix provide actuation, whereas the angle at which fibers are embedded in the matrix controls the actuation direction and size. The temperature has no effect on actuation and actuated forms at pH 7 and above, whereas the size of the actuated forms can be controlled by the temperature at lower pH. The membranes are strong enough to reversibly lift and release ≈426 times weight of their own mass (2.47 g metal ring is lifted by a 5.8 mg membrane). Soft actuators are of interest as smart scaffolds, robotics, catalysis, drug release, energy storage, electrodes, and metamaterials.

We present a facile access route to hydroxy-functional narrow disperse microspheres of well-defined grafting density (GD). Ethylene oxide has been grafted from highly crosslinked poly(divinyl benzene) microspheres by anionic ring-opening polymerization using sec-butyllithium as activator together with the phosphazene base t-BuP(4) . Initially, core microspheres have been prepared by precipitation polymerization utilizing divinyl benzene (DVB, 80 wt.-%). The grafting of poly(ethylene oxide) (PEO) from the surface resulted in the formation of functional core-shell microspheres with hydroxy-terminal end groups. The number average particle diameter of the grafted microspheres was 3.6 µm and the particle weight increased by 5.7%. The microspheres were characterized by SEM, FT-IR spectroscopy, elemental analysis, and fluorescence microscopy. The surface GD (determined via two methods) was 1.65 ± 0.06 and 2.09 ± 0.08 chains · nm(-2) , respectively.