Search

In imparting wetting properties, a fabrication process without the addition of new compounds and deposition of coating layers would be the most desirable because it does not introduce additional complexities. Hence, the ion beam irradiation technique is used as it enables the chemistry of materials to be modified through simple adjustments of irradiation parameters such as the type of accelerated particles, beam energy, and fluence. In this study, the hydrophilicity of alumina surfaces was weakened by irradiating He ion beams of different energy levels (200 keV and 20 MeV). These transitions become more pronounced as the total beam fluence increases. In low-energy irradiation, the effect of irradiation is predominant near the surface, and hydrophilicity is weakened by the increase in carbon adsorption and suppression of dissociative adsorption of water molecules owing to the introduction of oxygen vacancies. In contrast, nuclear transmutations are induced by irradiation with high-energy beams. Consequently, fluorine is generated, and hydrophobic functional groups are formed on the surface. By varying the beam conditions, the wetting properties of the target ceramic can be controlled to the desired level, which is required in various industries, via appropriate adjustments of the beam parameters. In addition, the beam irradiation technique may be applicable to all ceramic materials, including lattice oxygen and alumina.

We present an unprecedented and systematic route to controllably fabricate hexagonal non-close-packed (hncp) monolayer colloidal crystals and binary colloidal crystals (BCCs) based on plasma-electron coirradiation of polystyrene colloidal monolayers followed by thermal decomposition. Hncp colloidal crystals with tunable particle sizes and periods could be fabricated by changing the pristine colloidal particle size and the thermal decomposition time. In addition, BCCs and trimodal colloidal crystals that are composed of different-sized colloidal particles can also be fabricated by adding small particles on the prepared hncp colloidal crystals. Both the particle size ratio and the volume fraction of the BCCs can be widely tuned. These hncp colloidal crystals and BCCs have various potential applications as optical and photonic materials as well as in catalysis and sensors.

Polymer/ceramic composite films with micro- and nanocombined hierarchical structures are fabricated by electron irradiation of poly(methyl methacrylate) (PMMA) microspheres/silicone grease. Electron irradiation induces volume contraction of PMMA microspheres and simultaneously transforms silicone grease into a ceramic material of silicon oxycarbide with many nanobumps. As a result, highly porous structures that consist of micrometer-sized pores and microparticles decorated with nanobumps are created. The fabricated films with the porous hierarchical structure exhibit good superhydrophobicity with excellent self-cleaning and antiadhesion properties after surface treatment with fluorosilane. In addition, the porous hierarchical structures are covered with silicon oxycarbide, and thus the superhydrophobic coatings have high hardness and strong adhesion to the substrate. The presented technique provides a straightforward route to producing large-area, mechanically robust superhydrophobic films on various substrate materials.