Search

Resin-based composites (RBCs) are commonly used in dental restorations. It is known that RBCs undergo volumetric shrinkage during photo-polymerization leading to a detrimental increased stress state at the RBC-tooth interface and potentially early restoration failure. The objectives of this in vitro study were: (1) to ascertain whether shrinkage strain could be measured using in-fibre Bragg grating (FBG) technology, without confounding effects of temperature; and (2) to ascertain whether FBGs can detect alteration in shrinkage strain with introduction of a surface condition change at the RBC-cavity analog interface. Aluminum cavity analogs with simulated cavity dimensions 3.5 mm height x 2 mm width x 8 mm length and 2 mm wall thickness were secured in a 3D printed experimental jig. Two FBGs were used in the RBC space, one that was covered with a polyimide tube and that measured only temperature, and another that was affected by both mechanical strain and temperature. Experiments to determine if the two FBG system could be used to compensate for thermal artefacts were contrived to verify that a tube-covered and bare FBG measure the same temperature effect (n = 5). In situ photo-polymerization experiments, which consisted of using controlled amounts of SureFil SDR Flow + RBC, were performed to study RBC shrinkage behavior. As-machined (n = 10) and micro-etched (n = 11) cavity analogs were used. Significant differences in FBG measurements, which could indicate the ability of FBGs to detect alterations in strain across surface preparations, were determined using one tail t-tests at 95% confidence. Finally, additional temperature experiments were conducted 5 h after initial light exposure using the same light irradiation regiment to investigate temperature effects within a cured RBC system (n = 3). For temperature measurement, the tubing-covered and bare FBGs measured temperature changes with time-lag of 3.7 ± 1.4 s (tubing-covered FBG relative to bare). For measurements in cured RBC, the bare FBG and tubing-covered FBG measured different strains, with the bare FBG measuring larger apparent strains because this FBG is affected by thermal volumetric expansion of the RBC and a temperature increase of the FBG itself. The tubing covered FBG, that is isolated from volumetric expansion effects, measured relatively less. The interpretation of these results is that thermally-compensated strain measures (in-situ) could require simultaneous use of two FBGs (one strain isolated). In situ measurements of the photo-polymerization procedure for as-machined analogs at two time-points, 500 and 1000 s, were determined to be −485.43 ± 131.06 μstrain and −524.96 ± 134.78 μstrain, respectively. For air-abraded surfaces measures were significantly lower at (p < 0.001) −211.36 ± 12.38 μstrain and −228.07 ± 49.08 μstrain, respectively. To measure shrinkage strain and compensate for associated thermal effects from photo-polymerization, systems employing two FBGs, one of them isolated from thermal volumetric expansion, may be required. The presented approach proved capable of detecting significant alteration in strain across two surface preparations. [ABSTRACT FROM AUTHOR]

CAD/CAM-generated resin-based composite crowns have been proposed as an inexpensive alternative to conventional crowns. However, concerns have been raised about crown loosening in clinical use. Therefore, the present in vitro study aimed to evaluate the influence of thermal and mechanical cycling (TC and MC) on retentive strength of CAD/CAM resin-based crowns in relation to microscale expansion and contraction caused by fatigue. Eighty standardized dies were produced using a resin-based composite material. Crowns were milled from resin-based composite (n = 40) and glass-ceramic blocks (n = 40; control) using a dental CAD/CAM system. The crowns bonded to the dies were subjected to TC (temperature: 5 and 55 °C, cycles: 50,000) and MC (load: 200 N, cycles: 1.2 million). After fatigue treatment, retentive strength of the crowns was evaluated by a crown pull-off test at a crosshead speed of 1 mm/min. Coefficient of thermal expansion (CTE) and modulus of elasticity (E-modulus) of each material were also analyzed to estimate the microscale expansion and contraction during TC and MC. TC and MC significantly reduced the retentive strength of the CAD/CAM resin-based crowns whereas that of the CAD/CAM ceramic crowns was only affected by TC. In addition, the resin-based crowns showed a higher number of crown loosening during TC than the ceramic crowns. Analyses of CTE and E-modulus indicated that the resin-based crowns would be more deformed during TC and MC than the ceramic crowns. The present study demonstrated that the resistance of crowns to microscale expansion and contraction caused by thermal and mechanical fatigue would play an important role in maintaining retentive strength. [ABSTRACT FROM AUTHOR]

The aim of the study was to investigate the retention behaviour (pull-off force include adhesive remnant index = ARI) as well as translucency of various temporary luting cements and use microstructure elucidation methods to formulate explanatory approaches to their mode of action. The retention force of the temporary luting cements Provicol QM Plus (P+), Provicol QM Aesthetic (Pae), Bifix Temp (BiT), and as a reference a glass ionomer cement Meron (M) with a direct (Structur 3/S3) or an indirect (Structure CAD/SCAD) resin-based composite restauration was investigated after accelerated aging (thermocycling). Additional investigation of the physical properties was performed regarding to translucency and surface free energy. The microstructure was evaluated by X-ray diffraction, thermogravimetric analysis, differential scanning calorimetry and micro X-ray computed tomography. All tested temporary luting cements showed different pull-off forces in the range between 3.0 and 16.8 N in combination with S3 or SCAD after thermocycling. Only BiT with S3 showed pull-off forces of 129.2 N and complete retention on the restoration (ARI = 0), which was significant (p <.001) to all other samples. High translucency (BiT > Pae > M > P+) was observed for materials with lower crystalline content and low residual mass (usally resulting from higher organic content). M showed the highest surface free energy with a predominantly polar fraction, while BiT had a predominantly dispersive fraction. The highest porosity was observed in the coronal region of the restoration. The results suggest that translucency of temporary luting cements can be increased with higher organic and lower cryristall content. All combinations of cements and temporary restorations (direct/indirect; with the exception of BiT/S3) showed pull-off forces below 17 N (equivalent to a weight force of ∼1.7 kg), which allows manual detachment of the restoration by the dentist. • Correlation between the organic/crystalline content and the translucency exists. • Luting composites cement and direct restauration showed higher pull-off forces. • The highest forces are not always achieved with glass ionomer cement. • Highest porosity in the cement gap was observed in the occlusal region. [ABSTRACT FROM AUTHOR]

This study evaluated the effect of using two different pre-heating methods on the three resin-based composite (RBCs). Three paste viscosity bulk-fill RBCs (VisCalor Bulk [VC]; VOCO; x-tra fil Caps [XF], VOCO; Filtek One Bulk Fill [FO], 3 M) were pre-heated using either a VisCalor Dispenser (VOCO) to 65 °C, or the Caps Warmer (VOCO) to 37 °C, 54 °C, or 68 °C. The temperature inside the capsules and cavity was monitored before and after insertion into the matrix. Within 30 s of inserting the RBC, they were light-activated using a VALO (Ultradent) curing light for 20 s. The post-gel shrinkage (Shr - %), Flexural Strength (FS - MPa), Elastic Modulus (E − MPa), degree of conversion (DC - %), Knoop Hardness (KH - N/mm2), diametral tensile strength (DTS – MPa), and compressive strength (CS - MPa) of the RBCs were measured (10 specimens per group). The shrinkage stress was calculated using three-dimensional finite element analysis. Data were analyzed using one-way, two-way ANOVA and Tukey's test (α = 0.05). The temperature fell rapidly after the RBC was inserted into the cavity. Pre-heating the RBCs did not affect the mechanical properties. FO had the lowest E, DC, and KH values, VC had intermediate values, and XF achieved the highest values. The DTS and CS values were not affected by the various pre-heating methods, the temperature, or RBC. Pre-heating methods at 37 °C produced higher shrinkage for all RBCs. VC pre-heated to 65 °C produced the lowest stress when measured at 10 min after light activation. [Display omitted] • Mechanical properties of bulk-fill RBCs are not affected by pre-heating to 68 °C. • Pre-heating bulk-fill RBCs to 68 °C can decrease shrinkage stress. • The gun-style VisCalor Dispenser can effectively heat RBCs in 60 s. • RBC VisCalor had good mechanical properties and low shrinkage stress. [ABSTRACT FROM AUTHOR]

This study: 1) measures the effect of sample thickness and high irradiance on the depth-dependent time delay before photopolymerization reaction onset; 2) determines if exposure reciprocity exists; 3) measures the conversion rate at four irradiance levels; 4) determines the time, t 0 , at which the maximum DC rate is reached for two bulk-fill and one conventional posterior resin-based composites (RBCs). Tetric PowerFill IVA shade (Ivoclar Vivadent) and Aura bulk-fill ultra universal restorative (SDI), and one conventional posterior resin-based composite (RBC), Heliomolar A3 (Ivoclar Vivadent), that were either 0.2 mm, 2 mm, or 4 mm thick were photocured using a modified Bluephase G4 (Ivoclar Vivadent) light-curing unit (LCU) that delivered a single emission band (wavelength centered at 449 nm). The same radiant exposure of 24 J/cm2 was delivered at irradiances ranging from 0.5 to 3 W/cm2 by adjusting the exposure time. PowerFill was also photocured for 3 s or 6 s using a Bluephase PowerCure LCU (Ivoclar Vivadent) on the 3 s mode setting. The degree of conversion (DC) was measured in real-time at a high temporal resolution at 30 °C using Attenuated Total Reflection (ATR) FTIR spectroscopy with a sampling rate of 13 DC data points per second. The DC data were analyzed using a phenomenological autocatalytic model. The RBC viscosity was measured at 21 °C and 30 °C. Light transmission through the RBC samples at 22 °C was monitored with time to calculate the extinction coefficients of the RBCs. The time delay before photopolymerization started increased as the RBC thickness increased and the irradiance decreased. An autocatalytic model described the DC data. The time t 0 was less than 77 ms for the 0.2 mm thick samples of PowerFill irradiated using the highest irradiance of 3 W/cm2. Among the three RBCs for each sample thickness and irradiance level, the PowerFill had the smallest time t 0. There was a time delay of 0.59 s and 1.25 s before the DC started to increase at the bottom of 4 mm thick samples for the PowerFill and Aura, respectively, when an irradiance of 1 W/cm2 was delivered. The time delay increased to 3.65 s for the Aura when an irradiance of 0.5 W/cm2 was delivered. The extinction coefficients near 449 nm were 0.78 mm−1, 0.76 mm−1, and 1.55 mm−1 during the first 2 s after the start of photocuring of PowerFill, Aura, and Heliomolar, respectively. Only PowerFill followed exposure reciprocity. At T = 30 °C, the viscosity was 3400, 17000, and 5200 Paˑs for PowerFill, Aura, and Heliomolar, respectively. The time delay between when photopolymerization starts at the top and bottom of 2- or 4-mm thick RBC restorations may affect the structural integrity of the bond between the tooth and the bottom of the restoration. Only PowerFill followed exposure reciprocity between irradiance levels of 0.5 to 3 W/cm2. Exposure reciprocity did not occur for Aura or Heliomolar, neither of which are optimized for short light exposure or high irradiance conditions. [Display omitted] • Sample depth, irradiance and RBC determine when photocuring starts. • A time delay as long as 3.65 s was measured. • Among the three RBCs investigated, only PowerFill followed exposure reciprocity. • A time t 0 at which the maximum DC rate is reached was less than 77 ms for PowerFill. [ABSTRACT FROM AUTHOR]

Abstract: The aim of the study was to verify the influence of surface sealants on the surface roughness of resin composite restorations before and after mechanical toothbrushing, and evaluate the superficial topography using atomic force microscope. Five surface sealers were used: Single Bond, Opti Bond Solo Plus, Fortify, Fortify Plus and control, without any sealer agent. The lowest values of surface roughness were obtained for control, Single Bond and Fortify groups before toothbrushing. Fortify and Fortify Plus were the sealer agents that support the abrasive action caused by the toothbrushing although Fortify Plus group remained with high values of surface roughness. The application of specific surface sealants could be a useful clinical procedure to maintain the quality of resin-based composite restorations. [Copyright &y& Elsevier]

The aim of the present laboratory study was to mechanically characterize the interface between two dental resin-based composite (RBC) increments, and to investigate if elevated temperatures have an influence on the quality of the interface mimicking clinical filling procedure. Four RBCs (CLEARFIL MAJESTY™ Posterior, Kuraray (CMP)/Filtek™ Supreme XTE, 3M (FSX)/Grandio®SO, VOCO (GSO)/VisCalor® bulk, VOCO (VCB)) were tested with a fracture toughness test using Chevron notched beams (K I,CNB) at 23, 37 and 54 °C. K I,CNB specimens (3 × 4x25mm) with a V-shaped notch at the incremental interface were loaded until failure in a 4-point bending set-up. Failure modes were characterized using light microscopy, microstructural interface was analyzed using SEM. Statistical analysis was performed using Kolmogorov-Smirnoff test, two-way ANOVA and Tukey Post-Hoc test (p = 0.05). Mean K I,CNB ranged between 0.73 ±0.14 MPam0.5 (VCB, 23 °C) and 1.11 ± 0.11 MPam0.5 (FSX, 23 °C). The tested conventional highly filled RBCs presented fracture toughness at the incremental interface comparable to the cohesive strength of the bulk materials. VCB showed reduced interfacial fracture toughness at 23 and 37 °C, but performed well at elevated temperature of 54 °C. - Incremental interface of dental composites can be as strong as their cohesive strength - Fracture toughness of VisCalor bulk is improved at elevated temperature - Scanning electron microscopy reveals defects at the incremental interface of dental composites [ABSTRACT FROM AUTHOR]

Using standardized aluminum tooth models, this study: 1) measured the deflection along the cusp wall of models with a Class II cavity restored using either bulk filling or horizontal incremental filling techniques, and 2) calculated the cusp deflection and built-in stress within the restored tooth models for both filling techniques using a finite element (FE) model. Standardized tooth models with Class II cavities 4 mm deep, 4 mm high and 6 mm wide were machined out of aluminum. The models were restored using Filtek Posterior Restorative A2 shade resin-based composite (RBC). Both bulk filling and horizontal incremental filling techniques were used to restore the tooth models. After photocuring for 20 s from a single peak wavelength light-curing unit (LCU) with a radiant exitance of 1.25 W/cm2, the deflection of the cusp wall surface was measured using a profilometer. A FE model was used to predict the cuspal deflection and built-in stress of the restored tooth models. The elastic modulus within the FE model was parameterized using cusp deflection data obtained on a bulk filled tooth model. An agreement was found between the measured and predicted cusp deflection only when considering partial stress relaxation within the first incremental layer for the two-layer incremental filling technique. The calculated built-in stress was significantly reduced within the RBC and along the cavity walls when the cavity was filled incrementally in a horizontal direction compared to when it was bulk filled, resulting in a significantly smaller cusp deflection. The FE model was first calibrated and then validated using measured cusp deflection data. Partial stress relaxation may play a significant role in the horizontal incremental filling technique. The model can be used to predict where the built-in stress within the tooth model occurs. This study explains why for a given RBC, a horizontal incremental filling and curing technique results in lower built-in stress within the restored tooth and lower cusp deflection compared to the bulk curing technique. Image 1 • Agreement between measured and predicted cuspal deflection along the model wall. • Bulk fill restoration led to greater cuspal deflection than for incremental filling. • Bulk fill restoration led to greatest built-in stress within the restored model. • Partial stress relaxation occurred within the first layer for incremental filling. [ABSTRACT FROM AUTHOR]

Objectives: This study aimed to investigate the effects of hydrothermal aging, thermal cycling, and water storage on the mechanical properties of a machinable resin-based composite containing nano-zirconia fillers., Materials and Methods: A machinable resin-based composite containing nano-zirconia fillers (Lava Ultimate, LU) and a resin-based composite with a similar resin matrix-to-filler ratio but without zirconia fillers (Tetric N-Ceram, TNC) were prepared into bars and assigned into four groups based on the type of aging treatment (hydrothermal aging, thermal cycling, water storage, or no aging). The phase transformations of the zirconia fillers in LU after aging were evaluated by X-ray diffraction. The flexural strength, Weibull modulus, flexural modulus, and Vickers hardness of each group were investigated. The fracture surface morphologies of both resin-based composites before and after aging were observed by a scanning electron microscopy (SEM)., Results: Only Tetragonal zirconia was detected in the LU samples. Both before and after aging, the flexural strength, flexural modulus, and Vickers hardness values of LU were significantly higher than those of TNC (p < 0.05) with the exception of the flexural modulus of LU, which showed no difference with that of TNC after water storage (p = 0.68). Hydrothermal aging, thermal cycling, and water storage had no significant effects on the surface Vickers hardnesses of LU or TNC (p > 0.05). Hydrothermal aging significantly improved the flexural strength of LU (p = 0.00). Thermal cycling (p = 0.00) and water storage (p = 0.00) significantly decreased the flexural strength of LU. The flexural strength of TNC was not decreased by hydrothermal aging (p = 0.82) or water storage (p = 0.36), while it was decreased by thermal cycling (p = 0.00). The hydrothermal aging group of LU exhibited the highest Weibull modulus., Conclusions: The machinable resin-based composite containing nano-zirconia fillers provides superior flexural strength, flexural modulus, and Vickers hardness compared to the direct-filling resin-based composite with a similar resin matrix-to-filler ratio, although it fails to provide better aging resistance., Competing Interests: Declaration of competing interest None., (Copyright © 2019 Elsevier Ltd. All rights reserved.)