Search

The present study aimed to evaluate the impact of the existence of an abutment screw-access hole and the filling effects on the fatigue mechanical behavior of a luted lithium-disilicate glass-ceramic. Seventy-two discs (Ø = 10 mm, 1.0 mm in thickness) of lithium disilicate (IPS e.max CAD, Ivoclar AG) were obtained from prefabricated blocks. Thirty-six abutment specimens of an opaque zirconia (Yz - IPS e.max ZirCAD, Ivoclar AG) and titanium (Ti - Luminesse Ti-Cam discs, Talladium Inc.) were confectioned, and allocated according to 6 groups: Yz and Ti rigid (without screw access hole); Yz unfilled, Yz filled, Ti unfilled and Ti filled (with the screw access (Ø = 2.5 mm) in the center). For the unfilled groups, only a polytetrafluoroethylene tape was used. Resin composite (Tetric N-Ceram, Ivoclar AG) was applied to the screw access hole for the filled groups (Yz and Ti). A cyclic fatigue test was carried out (load of 200 N, 10,000 cycles each; 20 Hz of frequency, step size of 100 N until failure detection (radial/cone crack). The fatigue failure load (FFL) and number of cycles until failure (CFF) were recorded for statistical purposes. The stress distribution (MPa) was evaluated by finite element analysis. A statistically positive effect of the abutment material and the presence of the screw access hole was observed (p ≤ 0.05). The rigid groups (without screw access holes) depicted almost 100% of survival after the fatigue tests. Among the other groups, the Yz-filled group showed the best performance (p ≤ 0.05), followed by the Yz unfilled group. The Ti groups depicted lower values of FFL and CFF, with the Ti unfilled group showing the most unfavorable fatigue behavior (p ≤ 0.05). The lowest tensile stress concentration in the restorative material was observed with the use of rigid abutments, the filled groups depicted intermediate values, while unfilled groups showed the highest stress concentration (Yz rigid = 306.3 MPa; Ti rigid = 310.4 MPa < Yz filled = 490.7 MPa; Ti filled = 498.9 MPa < Yz unfilled = 707.6 MPa; Ti unfilled = 719.7 MPa). Therefore, the presence of a screw-access hole decreases the mechanical performance of a lithium disilicate ceramic regardless of the abutment material. In the presence of a screw-access hole, zirconia abutments depicted a higher fatigue failure load when compared with titanium. The filling of the abutment screw-access hole with resin composite increased the mechanical performance of the simulated restoration., Competing Interests: Declaration of competing interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper., (Copyright © 2023 The Authors. Published by Elsevier Ltd.. All rights reserved.)

This study aimed to evaluate the effect of low and high viscosities of dual-cured resin cement on the mechanical fatigue behavior of yttria tetragonal zirconia polycrystals (3Y-TZP) and yttria-stabilized zirconia (4YSZ) adhesively luted to a dentin analogue (glass fiber-reinforced epoxy resin). Ceramic discs were randomly divided into four groups (n = 20) based on the following study factors: dual-cured resin cement viscosities (low and high) and zirconia microstructure (3Y-TZP and 4YSZ). The discs were treated by air abrasion with aluminum oxide particles (50 μm), followed by the application of primer, and then luted with high or low viscosity resin cement to the dentin analogue. Subsequently, the luted sets underwent a step-stress fatigue test, which involved an initial load of 200 N, step increments of 100 N, 10,000 cycles per step, and a frequency of 20 Hz. Data on fatigue failure load (FFL) and the number of cycles for failure (CFF) were collected and analyzed using survival tests, including Kaplan-Meier and Mantel-Cox analyses, as well as Weibull analysis. Additionally, topography analysis, fractographic features, bonding interface analysis, and Raman spectroscopy were performed. The results revealed that 3Y-TZP exhibited superior fatigue behavior compared to 4YSZ, regardless of the viscosity of the resin cement used for luting. Among all groups, 3Y-Low exhibited the best fatigue performance, while 4YSZ luted with low or high viscosity resin cements yielded the lowest fatigue behavior (FFL). There were no significant differences in Weibull modulus among the groups. After air abrasion, both ceramics showed similar topography. Raman analysis indicated that the surface of 3Y-TZP ceramics prior to sintering had a monoclinic phase, which transitioned predominantly to tetragonal phase peaks after sintering. A similar transition was observed in 4YSZ ceramics. In summary, 3Y-TZP exhibited superior mechanical fatigue behavior compared to 4YSZ. The influence of resin cement viscosity on fatigue behavior was more pronounced in 3Y-TZP, with low-viscosity resin cement enhancing its performance. However, the mechanical fatigue behavior of 4YSZ was less affected by the viscosity of the dual-cured resin cement, showing similar results with both low and high viscosities. In conclusion, 3Y-TZP demonstrated superior mechanical fatigue behavior compared to 4YSZ. The impact of resin cement viscosity on fatigue behavior was more pronounced in 3Y-TZP, with low-viscosity resin cement enhancing its performance. Conversely, the mechanical fatigue behavior of 4YSZ was less sensitive to the viscosity of the dual-cured resin cement, resulting in similar outcomes with both low and high viscosities., Competing Interests: Declaration of competing interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper., (Copyright © 2023 Elsevier Ltd. All rights reserved.)

The purpose of the present study was to characterize the elastic modulus and Poisson's ratio of a resin cement with distinct viscosities, and to evaluate their impact on the static and fatigue strength of a translucent zirconia (4Y-PSZ) after air-abrasion surface treatment. Bar-shaped specimens of two different viscosities of resin cement (high and low) were obtained (25 × 10 × 3 mm). Sonelastic and Maxwell principles tests were performed to determine the elastic modulus and Poisson's ratio of each resin cement. Disc-shaped specimens of 4Y-PSZ were made (Ø = 15 mm, 1.2 mm in thickness) for the mechanical tests and allocated into groups according to two factors: surface treatment (presence or absence of air-abrasion with alumina particles; 45 μm grain-size); cement (absence, low or high viscosity). The static (n = 10) and cyclical (n = 15) biaxial flexural strength tests were performed by piston-on-three-balls geometry. A fatigue strength test was executed (20 Hz, initial stress of 60 MPa [12% of the mean static biaxial flexural strength], followed by increments of 25 MPa [5% of the mean static biaxial flexural strength] at each step of 10,000 cycles until the failure). The obtained data were analyzed by Weibull analysis. Survival rates were tabulated by the Kaplan-Meier test. Complementary analyses of surface roughness, topography, cross-sectional interfacial zone, fractography, and zirconia crystalline content (X-ray diffraction) were also performed. The evaluated resin cements with high and low viscosity presented similar elastic modulus (13.63 GPa; 12.74 GPa) and Poisson's ratio (0.32; 0.30), respectively. The air-abraded groups depicted higher mechanical strength of the zirconia ceramics than non-abraded groups (p˂ 0.05), regardless of the resin cement. 4Y-PSZ adhesively bonded to a high or low viscosity resin cement have statistically similar behavior (p˃ 0.05). The mechanical structural reliability of the 4Y-PSZ was not affected by the factors. Therefore, resin cement with high and low viscosity presented similar properties and potential to fill the zirconia surface, and did not affect the mechanical behavior of 4Y-PSZ. However, the air-abrasion surface treatment increased the static and fatigue flexural strength of the translucent zirconia., Competing Interests: Declaration of competing interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper., (Copyright © 2023 Elsevier Ltd. All rights reserved.)

This study aims to characterize the effect of pre- and/or post-sintering pigmentation techniques on the fatigue behavior of a 4YSZ ceramic (4 mol% yttrium stabilized zirconia). First, 4YSZ ceramic discs (IPS e.max ZirCAD, 15 mm diameter, and 1.2 mm thickness) were obtained and allocated according to the 'pigmentation technique' factor into 5 groups: Ctrl - unshaded ceramic disc (IPS e.max ZirCAD BL); Manuf - ceramic discs shaded by the manufacturer at block formation (IPS e.max ZirCAD MT A2); Brush - unshaded ceramic disc pigmented in the pre-sintered stage using a brush; Stain - unshaded ceramic disc pigmented in the post-sintering stage using a stain glaze (shade A2); Brush + Stain - combination of Brush and Stain techniques. The specimens were sintered and analyzed by a spectrophotometer (VITA Easyshade) for color differences (ΔE 00 calculated according to CIEDE, 2000) to ensure that they present the same perceived color (ΔE 00  ≤ 1.77, acceptability threshold). The specimens (n = 15) were submitted to biaxial flexural fatigue testing using a cyclic fatigue method (frequency of 20 Hz; 10,000 cycles per step; initial stress of 200 MPa; and step-size of 25 MPa) until specimen fracture. Fatigue strength (FS) and number of cycles until failure (CFF) were recorded with statistical purposes. Fractographic, complementary topography, elemental and roughness analyses were performed. The Ctrl shown the highest FS, CFF, and survival rates compared to the other conditions (p < 0.05), being only statistically similar to Brush. Stain showed the lowest FS, CFF and survival rates (p < 0.05). The Manuf and Brush + Stain shown intermediary performance. In regards of Weibull moduli, Brush shown the lowest values (lowest structural reliability), for both FS and CFF, being only statistically similar to Manuf. Topography analysis shown a uniform size of zirconia crystals in Ctrl, Manuf and Brush. In addition, a smooth glassy surface with some spots of impregnated pigment was observed in the groups where glaze was applied (Stain and Brush + Stain). This finding was corroborated by elemental analysis. Despite that, Stain and Brush + Stain presented the roughest surface (p < 0.05). In summary, the pigmentation techniques used to provide a Vita classical A2 color shade have a detrimental effect on the mechanical fatigue properties of a 4YSZ ceramic, except for the technique performed with the brush in the block pre-sintering stage. Despite this, the brush technique presents great variability in mechanical performance, resulting in lower structural reliability., Competing Interests: Declaration of competing interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper., (Copyright © 2022 Elsevier Ltd. All rights reserved.)

The fatigue behavior and FEA analysis of different ceramic materials cemented over distinct substrates for implant-supported crowns were evaluated in this study. Discs of 10 mm in diameter of both restorative and substrate materials were made and randomly allocated into pairs (n = 15) considering the two study factors: 'restorative ceramic material' (1 mm thickness) - polymer-infiltrated ceramic network (PICN), lithium disilicate (LD), zirconia-reinforced lithium silicate (ZLS), or translucent zirconia (TZ); and 'foundation substrate' (2 mm thickness) - polyetheretherketone (Peek) or yttrium-stabilized zirconia (YZ). Adhesive cementation was made with a dual cure resin cement. Fatigue testing was run using the step-stress methodology: initial load of 200 N for 5000 cycles, followed by steps of 10,000 cycles starting at 400 N up to 2800 N or until failure, step size of 200 N, frequency of 20 Hz. Data were analyzed by the Kaplan Meier and log-rank post-hoc tests. Fractography analysis (stereomicroscope and SEM) and FEA were also performed. Both factors under study and their interaction statistically influenced the fatigue failure load (FFL), cycles for failure (CFF) and survival rates (p < 0.001). The restorative materials bonded to YZ had higher FFL and CFF than when adhering to Peek, while restorative materials with more crystalline content (TZ and ZLS) showed higher FFL and CFF than LD and PICN. The fractography analysis showed that all materials bonded to YZ resulted in failures starting at the occlusal surface (Hertzian cone cracks), while materials bonded to Peek had radial cracks from the ceramic-cement intaglio surface. FEA analysis showed that tensile stress concentration decreased in the intaglio surface when testing the restorative material over a stiffer (YZ) foundation substrate. In addition, the higher the restorative material's crystalline content, the more the stress is concentrated within the material (TZ > ZLS ≥ LD > PICN) when bonded to the same foundation substrate. Thus, it concluded that a stiffer foundation substrate (YZ) enhances the load-bearing capacity under fatigue of the restorative set; that restorative materials with higher crystalline content results in higher fatigue performance of the set, regardless of the foundation used; and that the foundation material influences the failure pattern of the restorative set., (Copyright © 2021 Elsevier Ltd. All rights reserved.)