Search

The present study evaluated the effect of glass application with and without silver-doped soda-lime glass on roughness, biofilm formation, cell viability and flexural strength of a zirconia. Samples of 3-YTZP (3 mol% yttria stabilized tetragonal zirconia polycrystals) were divided into: polished (P); glaze (G); glass infiltration (INF); 4% silver-doped soda-lime glass (Ag4); glass infiltration + 4% silver-doped soda-lime glass (INF-Ag4); 5% silver-doped soda-lime glass (Ag5); glass infiltration + 5% silver-doped soda-lime glass (INF-Ag5). Samples were submitted to the following analyses: roughness (Ra); free surface energy (FSE); colony-forming units count (log CFU/mL); scanning electron microscopy (SEM); cytotoxicity (MTT assay) and flexural strength. Ag5 had greater roughness and FSE, but less biofilm adherence. In the CFU, silver-doped soda-lime glass groups inhibited the growth of Candida albicans, while the Ag5 inhibited Streptococcus mutans and none of the groups was effective against Streptococcus sanguinis. In the qualitative evaluation, lower number of colonies in the Ag5 grew up, compared to the control groups (P; G and INF) for both C. albicans and S. mutans. Regarding the MTT assay, the Ag4, INF-Ag4 and INF-Ag5 obtained percentage of cell viability greater than 50%. Ag5 showed lower flexural strength when compared to the control groups, while the application of glass infiltration increased the flexural strength by formation of a graded region between zirconia-glass. In conclusion, Ag5 had the greatest antimicrobial effect, Ag4 and INF-Ag4 were the less cytotoxic and the INF was the most resistant to fracture. Therefore, INF-Ag4 conciliates the best performance in terms of antimicrobial and mechanical properties for a 3-YTZP.

Made available in DSpace on 2021-06-25T10:35:00Z (GMT). No. of bitstreams: 0 Previous issue date: 2021-01-01 Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) The need for improved mechanical properties in regions of higher masticatory loads led to the introduction of zirconia in dentistry. However, zirconia needs a characterization and glaze to have a more natural, tooth-like appearance. An experimental glass was produced based on the sol-gel method to exhibit a thermal expansion coefficient similar to that presented by zirconia. The experimental glass was used as glazing material on the previously sintered zirconia (vita YZ) surface. There was a significant reduction in the roughness and hardness of the material, caused by the formation of smooth, void-free and highly uniform glass coating. The glass infiltrated among superficial zirconia grains and caused the formation of monoclinic zirconia at the zirconia/glass interface. A consequent decrease in surface roughness and an increase in flexural strength and reliability was then observed in the experimental glass group. On the other hand, a significant decrease in the reliability of conventionally glazed group was observed. Therefore, the use of experimental glass instead of conventional glaze can improve the mechanical properties, smoothness, and mechanical reliability of fully sintered zirconia. Physics Department Aeronautics Technological Institute (ITA), 50 Marechal Eduardo Gomes Square, São José dos Campos, SP Department of Dental Materials and Prosthodontics São Paulo State University (UNESP) Institute of Science and Technology, São José dos Campos, São Paulo Department of Dental Materials and Prosthodontics São Paulo State University (UNESP) Institute of Science and Technology, São José dos Campos, São Paulo CAPES: 001 CNPq: 40983/2016-3