In this study, the strength properties of NHL based mortar with blending basalt fiber were investigated. In the first step, it was evaluated that physical properties of NHL based mortar according to mixing method of four types of basalt fiber and then mixing method of one type was selected. As a result of assessment, it showed that the physical properties with mixing method of dry blending were better than that of wet blending and mixing method that basalt fiber pre-mixed with NHL for 5 min in a blender was selected and water and aggregate were finally added. Secondly, the investigation of blending fiber length on the compressive and flexural strength for basalt fiber reinforced NHL based mortars was carried out. The compressive strength was decreased with adding fiber, and the flexural strength was increased more than plain mortar. In the case of adding 6 mm fiber, the compressive and flexural strength were improved more than that of others.

This study investigated a utilization technology of light burned dolomite. light burned dolomite () generated in furnace (steel manufacturer) is an alternative to quick lime. Using light burned dolomite has an effect on reducing the consumption of fluorite slag MgO concentration in supersaturated solution by prolonging the life of softening effect. Armophous MgO, not containing periclase is formed by firing dolomite under . It has larger surface area and higher reactivity than periclase, and also shows better expansion effect than quicklime. Due to those effects, therefore, armophous MgO produced from light burned dolomite is used as an alternative expansion agent in mortar. In the experiment, characteristics of light burned dolomite were compared to those of existing expansion agents such as anhydrite and quicklime. Then, each expansion and shrinkage rates were measured over a period of about 3 months in both of 1m Jis mold at labscale and apartment mortar flooring at field scale. In the result, it was observed that light burned dolomite in mortar flooring more compensates for the expansion and shrinkage rates than the existing expansion agents, showing low expansion rate of below 0.05% and also decreases the crack.

Current, Registration fields of CDM projects are being conducted in a variety of parts such as mostly energy, chemical processing and manufacturing processes. However, there are not many CDM project registrations by recycling of inorganic waste. In this paper, analysis abroad CDM project and applications in order to review possibility of CDM project registration through the recycling of domestic inorganic waste were investigated. As a results, registered case of CDM project by inorganic waste recycling was researched to registrate in raw material alternative field of cement industry that inorganic waste can be used in large quantities. Application prospects of CDM project in Korea will be possible to analysis industrial scale, industry using inorganic raw materials, green house gas emissions and inorganic waste generated in large quantities.