Search

Boron oxide/hydroxide supported on oxidized activated carbon (B/OAC) was shown to be an inexpensive catalyst for the oxidative dehydrogenation (ODH) of propane that offers activity and selectivity comparable to boron nitride. Here, we obtain an atomistic picture of the boron oxide/hydroxide layer in B/OAC by using 35.2 T

Hexagonal boron nitride (h-BN) and boron nitride nanotubes (BNNT) were recently reported as highly selective catalysts for the oxidative dehydrogenation (ODH) of alkanes to olefins in the gas phase. Previous studies revealed a substantial increase in surface oxygen content after exposure to ODH conditions (heating to ca. 500 °C under a flow of alkane and oxygen); however, the complexity of these materials has thus far precluded an in-depth understanding of the oxygenated surface species. In this contribution, we combine advanced NMR spectroscopy experiments with scanning electron microscopy and soft X-ray absorption spectroscopy to characterize the molecular structure of the oxygen functionalized phase that arises on h-BN and BNNT following catalytic testing for ODH of propane. The pristine BN materials are readily oxidized and hydrolyzed under ODH reaction conditions to yield a phase consisting of three-coordinate boron sites with variable numbers of hydroxyl and bridging oxide groups which is denoted B(OH)

Covalent organic framework (COF) represents an emerging class of porous materials that have exhibited great potential in various applications, particularly in catalysis. In this work, we report a newly designed 2D COF with incorporated Re complex, which exhibits intrinsic light absorption and charge separation (CS) properties. We show that this hybrid catalyst can efficiently reduce CO2 to form CO under visible light illumination with high electivity (98%) and better activity than its homogeneous Re counterpart. More importantly, using advanced transient optical and X-ray absorption spectroscopy and in situ diffuse reflectance spectroscopy, we unraveled three key intermediates that are responsible for CS, the induction period, and rate limiting step in catalysis. This work not only demonstrates the potential of COFs as next generation photocatalysts for solar fuel conversion but also provide unprecedented insight into the mechanistic origins for light-driven CO2 reduction.

Covalent organic framework (COF) represents an emerging class of porous materials that have exhibited great potential in various applications, particularly in catalysis. In this work, we report a newly designed 2D COF with incorporated Re complex, which exhibits intrinsic light absorption and charge separation (CS) properties. We show that this hybrid catalyst can efficiently reduce CO

We show that MoO(x)-promoted Au/SiO2 catalysts are active for reverse water-gas shift (RWGS) at 573 K. Results from reactivity measurements, CO FTIR studies, Raman spectroscopy, and X-ray absorption spectroscopy (XAS) indicate that the deposition of Mo onto Au nanoparticles occurs preferentially on under-coordinated Au sites, forming Au/MoO(x) interfacial sites active for reverse water-gas shift (RWGS). Au and AuMo sites are quantified from FTIR spectra of adsorbed CO collected at subambient temperatures (e.g., 150-270 K). Bands at 2111 and 2122 cm(-1) are attributed to CO adsorbed on under-coordinated Au(0) and Au(δ+) species, respectively. Clausius-Clapeyron analysis of FTIR data yields a heat of CO adsorption (ΔH(ads)) of -31 kJ mol(-1) for Au(0) and -64 kJ mol(-1) for Au(δ+) at 33% surface coverage. Correlations of RWGS reactivity with changes in FTIR spectra for samples containing different amounts of Mo indicate that interfacial sites are an order of magnitude more active than Au sites for RWGS. Raman spectra of Mo/SiO2 show a feature at 975 cm(-1), attributed to a dioxo (O═)2Mo(-O-Si)2 species not observed in spectra of AuMo/SiO2 catalysts, indicating preferential deposition of Mo on Au. XAS results indicate that Mo is in a +6 oxidation state, and therefore Au and Mo exist as a metal-metal oxide combination. Catalyst calcination increases the quantity of under-coordinated Au sites, increasing RWGS activity. This strategy for catalyst synthesis and characterization enables quantification of Au active sites and interfacial sites, and this approach may be extended to describe reactivity changes observed in other reactions on supported gold catalysts.

Acetone is known to be a key species in the chemistry of the Upper Troposphere and Lower Stratosphere. In this theoretical study, using amply validated methodologies, the hitherto overlooked reaction of acetone with HO2* radicals is found to lead to a fast equilibrium (CH3)2C=O + HO2* right harpoon over left harpoon (CH3)2C(OH)OO*. At room temperature, this is shifted entirely to the left and thus of no consequence. However, near the tropopause (T/= 220 K), the equilibrium is shown to shift to the right to such an extent that the subsequent reaction of (CH3)2C(OH)OO* with (partly air-traffic-generated) NO becomes an effective acetone sink. This process finally results in acetic acid, thus explaining the great abundance of this important organic acid observed near the tropopause.