Search

The electrochemical reduction of nitrate (NO 3 - ) and nitrite (NO 2 - ) enables sustainable, carbon-neutral, and decentralized routes to produce ammonia (NH 3 ). Copper-based materials are promising electrocatalysts for NO x - conversion to NH 3 . However, the underlying reaction mechanisms and the role of different Cu species during the catalytic process are still poorly understood. Herein, by combining quasi in situ X-ray photoelectron spectroscopy (XPS) and operando X-ray absorption spectroscopy (XAS), we unveiled that Cu is mostly in metallic form during the highly selective reduction of NO 3 - /NO 2 - to NH 3 . On the contrary, Cu(I) species are predominant in a potential region where the two-electron reduction of NO 3 - to NO 2 - is the major reaction. Electrokinetic analysis and in situ Raman spectroscopy was also used to propose possible steps and intermediates leading to NO 2 - and NH 3 , respectively. This work establishes a correlation between the catalytic performance and the dynamic changes of the chemical state of Cu, and provides crucial mechanistic insights into the pathways for NO 3 - /NO 2 - electrocatalytic reduction.

Spinel-type catalysts are promising anode materials for the alkaline oxygen evolution reaction (OER), exhibiting low overpotentials and providing long-term stability. In this study, we compared two structurally equal Co 2 FeO 4 spinels with nominally identical stoichiometry and substantially different OER activities. In particular, one of the samples, characterized by a metastable precatalyst state, was found to quickly achieve its steady-state optimum operation, while the other, which was initially closer to the ideal crystallographic spinel structure, never reached such a state and required 168 mV higher potential to achieve 1 mA/cm 2 . In addition, the enhanced OER activity was accompanied by a larger resistance to corrosion. More specifically, using various ex situ , quasi in situ , and operando methods, we could identify a correlation between the catalytic activity and compositional inhomogeneities resulting in an X-ray amorphous Co 2+ -rich minority phase linking the crystalline spinel domains in the as-prepared state. Operando X-ray absorption spectroscopy revealed that these Co 2+ -rich domains transform during OER to structurally different Co 3+ -rich domains. These domains appear to be crucial for enhancing OER kinetics while exhibiting distinctly different redox properties. Our work emphasizes the necessity of the operando methodology to gain fundamental insight into the activity-determining properties of OER catalysts and presents a promising catalyst concept in which a stable, crystalline structure hosts the disordered and active catalyst phase.

In this study, we have taken advantage of a pulsed CO 2 electroreduction reaction (CO 2 RR) approach to tune the product distribution at industrially relevant current densities in a gas-fed flow cell. We compared the CO 2 RR selectivity of Cu catalysts subjected to either potentiostatic conditions (fixed applied potential of -0.7 V RHE ) or pulsed electrolysis conditions (1 s pulses at oxidative potentials ranging from E an = 0.6 to 1.5 V RHE , followed by 1 s pulses at -0.7 V RHE ) and identified the main parameters responsible for the enhanced product selectivity observed in the latter case. Herein, two distinct regimes were observed: (i) for E an = 0.9 V RHE we obtained 10% enhanced C 2 product selectivity (FE C 2 H 4 = 43.6% and FE C 2 H 5 OH = 19.8%) in comparison to the potentiostatic CO 2 RR at -0.7 V RHE (FE C 2 H 4 = 40.9% and FE C 2 H 5 OH = 11%), (ii) while for E an = 1.2 V RHE , high CH 4 selectivity (FE CH 4 = 48.3% vs 0.1% at constant -0.7 V RHE ) was observed. Operando spectroscopy (XAS, SERS) and ex situ microscopy (SEM and TEM) measurements revealed that these differences in catalyst selectivity can be ascribed to structural modifications and local pH effects. The morphological reconstruction of the catalyst observed after pulsed electrolysis with E an = 0.9 V RHE , including the presence of highly defective interfaces and grain boundaries, was found to play a key role in the enhancement of the C 2 product formation. In turn, pulsed electrolysis with E an = 1.2 V RHE caused the consumption of OH - species near the catalyst surface, leading to an OH-poor environment favorable for CH 4 production.

Bimetallic CuZn catalysts have been recently proposed as alternatives in order to achieve selectivity control during the electrochemical reduction of CO 2 (CO 2 RR). However, fundamental understanding of the underlying reaction mechanism and parameters determining the CO 2 RR performance is still missing. In this study, we have employed size-controlled (∼5 nm) Cu 100- x Zn x nanoparticles (NPs) supported on carbon to investigate the correlation between their structure and composition and catalytic performance. By tuning the concentration of Zn, a drastic increase in CH 4 selectivity [∼70% Faradaic efficiency (F.E.)] could be achieved for Zn contents from 10 to 50, which was accompanied by a suppression of the H 2 production. Samples containing a higher Zn concentration displayed significantly lower CH 4 production and an abrupt switch in the selectivity to CO. Lack of metal leaching was observed based on quasi in situ X-ray photoelectron spectroscopy (XPS). Operando X-ray absorption fine structure (XAFS) spectroscopy measurements revealed that the alloying of Cu atoms with Zn atoms takes place under reaction conditions and plays a determining role in the product selectivity. Time-dependent XAFS analysis showed that the local structure and chemical environment around the Cu atoms continuously evolve during CO 2 RR for several hours. In particular, cationic Zn species initially present were found to get reduced as the reaction proceeded, leading to the formation of a CuZn alloy (brass). The evolution of the Cu-Zn interaction with time during CO 2 RR was found to be responsible for the change in the selectivity from CH 4 over Cu-ZnO NPs to CO over CuZn alloy NPs. This study highlights the importance of having access to in depth information on the interplay between the different atomic species in bimetallic NP electrocatalysts under operando reaction conditions in order to understand and ultimately tune their reactivity.