Search

Core-shell nanoparticles of Au@Pd with precise submonolayer, monolayer, or multilayer structure were synthesized using ligand-exchange reactions of palladate ions onto colloidal Au nanocrystals. Decoupling the palladate adsorption step from the subsequent reduction enables excellent precision, uniformity, and tunability in the Pd shell thickness. The redox properties of the surface Pd are directly correlated to the thickness of the Pd shell with a+200 mV shift in the PdO reduction potential for submonolayer Au@Pd nanoparticles compared to pure Pd. Using these precisely controlled core-shell materials, the oxygen reduction catalytic activity can be directly correlated to PdO reduction potential and Pd surface coverage on Au. When the Pd oxide reduction peak is shifted by +240 mV compared to pure Pd, a 50 mV reduction in overpotential and a 4-fold increase in kinetic current density for oxygen reduction are observed. Colloidal ligand-exchange synthesis may be particularly useful for noble metal core-shell catalysts as a strategy to subtly tune the electronic properties of surface atoms in order to lower overpotential and increase catalytic turnover.

Carbon dioxide reduction is an essential component of many prospective technologies for the renewable synthesis of carbon-containing fuels. Known catalysts for this reaction generally suffer from low energetic efficiency, poor product selectivity, and rapid deactivation. We show that the reduction of thick Au oxide films results in the formation of Au nanoparticles ("oxide-derived Au") that exhibit highly selective CO(2) reduction to CO in water at overpotentials as low as 140 mV and retain their activity for at least 8 h. Under identical conditions, polycrystalline Au electrodes and several other nanostructured Au electrodes prepared via alternative methods require at least 200 mV of additional overpotential to attain comparable CO(2) reduction activity and rapidly lose their activity. Electrokinetic studies indicate that the improved catalysis is linked to dramatically increased stabilization of the CO(2)(•-) intermediate on the surfaces of the oxide-derived Au electrodes.

Modified Cu electrodes were prepared by annealing Cu foil in air and electrochemically reducing the resulting Cu(2)O layers. The CO(2) reduction activities of these electrodes exhibited a strong dependence on the initial thickness of the Cu(2)O layer. Thin Cu(2)O layers formed by annealing at 130 °C resulted in electrodes whose activities were indistinguishable from those of polycrystalline Cu. In contrast, Cu(2)O layers formed at 500 °C that were ≥~3 μm thick resulted in electrodes that exhibited large roughness factors and required 0.5 V less overpotential than polycrystalline Cu to reduce CO(2) at a higher rate than H(2)O. The combination of these features resulted in CO(2) reduction geometric current densities1 mA/cm(2) at overpotentials0.4 V, a higher level of activity than all previously reported metal electrodes evaluated under comparable conditions. Moreover, the activity of the modified electrodes was stable over the course of several hours, whereas a polycrystalline Cu electrode exhibited deactivation within 1 h under identical conditions. The electrodes described here may be particularly useful for elucidating the structural properties of Cu that determine the distribution between CO(2) and H(2)O reduction and provide a promising lead for the development of practical catalysts for electrolytic fuel synthesis.