1. Electrical conductivity and thermal expansion of neodymium–ytterbium zirconate ceramics
- Author
-
Liu, Zhan-Guo, Ouyang, Jia-Hu, Zhou, Yu, and Xia, Xiao-Liang
- Subjects
- *
CERAMICS , *ELECTRIC conductivity , *THERMAL expansion , *NEODYMIUM , *YTTERBIUM , *SINTERING , *BULK solids , *IMPEDANCE spectroscopy - Abstract
Abstract: (Nd1−x Yb x )2Zr2O7 (0≤ x ≤1) ceramics were prepared by pressureless-sintering to obtain dense bulk materials. The electrical conductivity of (Nd1−x Yb x )2Zr2O7 was investigated by complex impedance spectroscopy over a frequency range of 20Hz to 2MHz from 723 to 1173K in air. A high-temperature dilatometer was used to analyze thermal expansion coefficient of (Nd1−x Yb x )2Zr2O7 in the temperature range of 373–1523K. The measured electrical conductivity obeys the Arrhenius relation. The grain conductivity of each composition in (Nd1−x Yb x )2Zr2O7 gradually increases with increasing temperature. A decrease of about one order of magnitude in grain conductivity is found at all temperature levels when the Yb content increases from x =0.3 to x =0.5. The highest electrical conductivity value obtained in this work is 9.32×10−3 Scm−1 at 1173K for (Nd0.7Yb0.3)2Zr2O7 ceramic. (Nd1−x Yb x )2Zr2O7 ceramics are oxide-ion conductors in the oxygen partial pressure range from 1.0×10−4 to 1.0atm at all test temperature levels. Thermal expansion coefficients of (Nd1−x Yb x )2Zr2O7 gradually decrease with increasing ytterbium content at identical temperature levels. [Copyright &y& Elsevier]
- Published
- 2010
- Full Text
- View/download PDF