Search

A new platinum group metal (PGM)-free proton exchange membrane fuel cell (PEMFC) cathode catalyst materials, synthesized using the VariPore™ method by Pajarito Powder, LLC, are characterized for their structure and activity. The physico-chemical analysis of the iron-nitrogen-carbon (Fe-N-C) electrocatalysts show mesoporous carbon material effectively doped with iron and nitrogen. The materials have an average pore size of 7–8 nm and high specific surface area. The Fe-N-C catalysts exhibit good oxygen reduction reaction (ORR) activity in 0.5 M H 2 SO 4 electrolyte with high half-wave potential and sustainable electrochemical stability over 10,000 repeated potential cycles with insignificant losses in their activities. As cathode catalysts in a PEMFC, the Fe-N-C materials deliver remarkably good fuel cell performance at low overpotential approaching that of the commercial Pt catalyst. The high ORR electrocatalytic activity of these Fe-N-C catalysts is credited to the synergy between nitrogen-moieties, specifically pyrrolic-N, pyridinic-N, and graphitic-N, and iron in addition to the high mesoporosity that facilitate an effective reaction path in boosting the electrocatalytic activity and stability. [Display omitted] • State-of-the-art commercial PGM-free catalysts for ORR were characterized and evaluated. • Was shown that active centres are atomically dispersed. • Performance of electrocatalysts was evaluated in industrially manufactured MEA form-factor. • The fuel cell performance is close to the state-of-the-art R&D PGM-free catalysts. [ABSTRACT FROM AUTHOR]

Abstract: The influence of ammonium ions on the catalysis of hydrogen oxidation and oxygen reduction is studied by means of rotating ring-disk electrode experiments on polycrystalline platinum in perchloric acid. While ammonium does not affect the hydrogen oxidation reaction, the oxygen reduction reaction is severely poisoned. Poisoning at the cathode explains the majority of the losses observed in polymer electrolyte membrane fuel cells contaminated with ammonia. Voltammetry in deaerated solution suggest that the poisoning can be attributed to either ammonium oxidation or increased binding to OH species. [Copyright &y& Elsevier]

Abstract: In this study, a novel core–shell structured Pd3Fe@Pt/C electrocatalyst, which is based on Pt deposited onto carbon supported Pd3Fe nanoparticles, is prepared for the oxygen reduction reaction (ORR) in proton exchange membrane fuel cells (PEMFCs). The carbon supported Pd3Fe nanoparticles act as seeds to guide the growth of Pt. The formation of the core–shell structured Pd3Fe@Pt/C is confirmed by transmission electron microscopy (TEM), X-ray diffraction (XRD) and electrochemical characterization. The higher surface area of the synthesized catalyst suggests that the utilization of Pt in the Pd3Fe@Pt/C catalyst is higher than that in Pt/C. Furthermore, better electrocatalytic performance than that of Pt/C and Pd3Fe/C catalyst is observed in the ORR which follows a four-electron path. Consequently, the results indicate that the Pd3Fe@Pt/C catalyst could be used as a more economically viable alternative for the ORR of PEMFCs. [Copyright &y& Elsevier]

Abstract: A solution-phase synthesis method was studied to prepare carbon supported Pt-Co alloy catalysts. The organic precursors of Pt acetylacetonate and Co acetylacetonate were reduced in a high boiling point solvent of octyl ether in the presence of oleic acid (OAc) and oleylamine (OAm) to produce fine Pt-Co nanoparticles, which were subsequently deposited on carbon support to obtain Pt-Co/C catalysts. Thermogravimetric analysis suggests that the stabilizers (OAc and OAm) can be removed by copious ethanol washing and subsequent moderate temperature heat-treatment (250°C, under Argon atmosphere). X-ray diffraction patterns indicate that the average particle size is around 2.3nm, and the lattice parameter is 3.868Å for the heat-treated Pt-Co/C (40wt%). Transmission electron microscopy images show very small Pt-Co alloy nanoparticles homogeneously dispersed on the carbon support with a particle size distribution of 2–4nm for all Pt-Co/C samples. The elements composition of Pt and Co in the final Pt-Co/C catalyst can be well controlled, as evidenced by inductively coupled plasma atomic emission spectroscopy and energy dispersive spectroscopy analyses. Proton exchange membrane fuel cell tests show the heat-treated Pt-Co/C cathode catalyst has higher mass activity of oxygen reduction reaction than Pt/C at an operation voltage of 0.9V, this can be attributed to its smaller particle size and reduced lattice parameter. [Copyright &y& Elsevier]

Ceria coated carbon nanotubes (CeO 2 @CNTs) were prepared as a versatile support material to improve both the activity and stability of platinum (Pt)-based catalysts. We demonstrated that the CeO 2 nanoparticles (NPs) had an extrinsically remote functionalization effect on the Pt electrocatalysis. The CeO 2 modulated the electronic structure, and facilitated the O 2 adsorption property of Pt without any intrinsic chemical doping or Pt-alloying. This led to d -band electron filling in Pt, and delivery of active oxygens (O−) to the Pt surface via oxygen spillover at the Pt-CeO x interface, thus enhancing the ORR activity. Furthermore, due to the unique redox behavior between Ce3+ and Ce4+, the dissolved Ce ions could also participate in the radical scavenge reaction, which prevents the chemical degradation of polymeric components in the cell. A single cell using the Pt NPs supported on CeO 2 @CNT as a cathode catalyst delivered a superior electrochemical performance and a retained durability compared to the cells with pristine CNT supported Pt NPs. • The ceria functionalized Pt/CNT (Pt@CeO 2 @CNT) was used as PEM fuel cell catalysts. • Ceria improves the ORR activity of adjacent Pt nanoparticles catalyst. • Dissolved Ce ions effectively scavenge the oxidative free radicals. • Pt@CeO 2 @CNT exhibits outstanding activity and stability in PEM fuel cells.. [ABSTRACT FROM AUTHOR]