A simple way to synthesize PbS nanocrystals with the ability to tune their morphology at room temperature is reported. The preparation utilizes an amine-catalyzed decomposition of a precursor and the amine was found to play dual roles as both the catalyst and the capping agent. Spherical PbS nanocrystals of diameters 5 to 10 nm were obtained when long chain alkylamines were used in the pot. When difunctional ethylenediamine was used instead, exclusively PbS dendrites can be isolated from the same precursor at room temperature. Uniform six- and four-armed dendrites are observed, with regular branches of approximately 20 nm in diameter growing in a parallel order. In a further step, morphology tuning of the dendrites to induce 1D growth into nanorods is achievable through the addition of a trace amount of stronger capping dodecanethiol molecules. Thus, PbS nanorods with aspect ratios of approximately 20 to 30 could be successfully obtained and illustrated. A possible formation mechanism is discussed and the initial step of the reaction mechanism was modeled with DFT calculations as a nucleophilic attack.

Dodecanethiol-protected copper/silver bimetallic nanoclusters were prepared by a liquid-phase method using different copper to silver feed ratios. The morphology and size of the prepared nanoclusters were analyzed with X-ray diffraction (XRD) and transmission electron microscopy (TEM), while their spectroscopic and surface properties were characterized by infrared (IR) and X-ray photoelectron spectroscopy (XPS), thermal gravimetric analysis (TGA), differential scanning calorimetry (DSC), and 13C cross-polarization magic angle spinning NMR (13C CPMAS NMR). TEM analysis indicated that all the bimetallic clusters prepared are approximately 4-6 nm in size. On the other hand, the results of XRD, XPS, and Fourier transform infrared (FTIR) spectroscopy suggested that the surfaces of the alloy nanoclusters are mostly enriched with the less noble metal copper atoms. This surface enrichment of copper may be attributed to a galvanic exchange process during preparation, and the extent of enrichment is directly related to the copper feed ratio used. Interestingly, DSC studies showed two melting transitions in some of these alloy samples, suggesting different packing behavior of the dodecanethiol chains onto the heterogeneously intercalated silver- and copper-rich surfaces.