Search

Life extension of light water reactors requires robust models to predict the embrittlement of reactor pressure vessel (RPV) steels under long-term neutron irradiation. Embrittlement is due to nanoscale precipitation hardening by phases containing Cu, Mn, Ni, and Si, resulting in increases of the ductile to brittle transition temperature. Embrittlement data for low flux, high fluence extended life conditions, up to 80 years or more, are largely not available. Thus, higher flux, accelerated test reactor irradiations have been used to help develop models to predict low flux embrittlement at high fluence. Here flux, or dose rate, is expressed in units of displacements per atom per second (dpa/s). The dose rate can significantly influence precipitate evolution in a way that depends on fluence (dpa), temperature, and alloy composition, as well as flux itself. Here, we explore precipitation in surveillance steels with varying compositions at high fluxes (10−5–10−6 dpa/s) produced using 70 MeV Fe2+ ion irradiations. Atom probe tomography was used to characterize the dose dependence of precipitation at very high ion irradiation dose rates, and to evaluate corresponding similarities or differences compared to neutron irradiated steels at a much lower dose rate of ≈ 5 × 10−9 dpa/s. The data show that, on average, the ion irradiation precipitate volume fractions increase by factors of ∼ 1.5 to 2 between 0.3 dpa and 1.2 dpa. Limited data show that the major effect of neutron versus ion irradiation is the former has lower precipitate number densities and larger sizes. Otherwise, the precipitates are remarkably similar in composition and volume fraction. [ABSTRACT FROM AUTHOR]

F82H is the Japanese reference reduced-activation ferritic-martensitic (RAFM) steel for fusion blanket applications. The harsh environment of a fusion reactor, such as neutron irradiation and He/H damage, can result in significant degradation of F82H fracture toughness. Therefore, understanding the fracture toughness behavior of F82H in the fusion environment is critical to ensure the long-term safe operation of the fusion reactor. In this paper, we summarize seven irradiation campaigns of the High Flux Isotope Reactor (HFIR) at Oak Ridge National Laboratory (ORNL) covering five variants of F82H steels, including F82H IEA, F82H Mod3, F82H doped with 1.4% natural Ni, F82H doped with 1.4% 58Ni, and F82H doped with 1.4% 60Ni. The irradiation temperatures covered the range from 220 °C to 530 °C and the neutron irradiation dose spanned 4 dpa to 70 dpa. The effects of neutron irradiation temperature, dose, materials composition, Ni doping, and He production on F82H fracture toughness are discussed. Our results showed that irradiation embrittlement monotonically decreased with increasing irradiation temperature until 400 °C for F82H IEA and F82H Mod3. F82H Mod3 showed better fracture toughness than F82H IEA both before and after neutron irradiation. We determined that 1.4% Ni alloying can be applied to F82H for simulating He effect in a fission reactor without jeopardizing the fracture toughness of the material. However, more studies are needed to understand the effect of high dose (>20 dpa) and He production on F82H fracture toughness. [ABSTRACT FROM AUTHOR]

Nuclear reactor lifetimes may be limited by nano-scale Cu-Mn-Ni-Si precipitates (CRPs and MNSPs) that form under neutron irradiation (NI) of pressure vessel (RPV) steels, resulting in hardening and ductile to brittle transition temperature increases (embrittlement). Physical models of embrittlement must be based on characterization of precipitation as a function of the combination of metallurgical and irradiation variables. Here we focus on rapid and convenient charged particle irradiations (CPI) to both: a) compare to precipitates formed in NI; and, b) use CPI to efficiently explore precipitation in steels with a very wide range of compositions. Atom probe tomography (APT) comparisons show NI and CPI for similar bulk steel solute contents yield nearly the same precipitate compositions, albeit with some differences in their number density, size and volume fraction (f) dose (dpa) dependence. However, the overall precipitate evolutions are very similar. Advanced high Ni (>3 wt%) RPV steels, with superior unirradiated properties, were also investigated at high CPI dpa. For typical Mn contents, MNSPs have Ni 16 Mn 6 Si 7 or Ni 3 Mn 2 Si phase type compositions, with f values that are close to the equilibrium phase separated values. However, in steels with very low Mn and high Ni, Ni 2-3 Si silicide phase type precipitate compositions are observed; and when Ni is low, the precipitate compositions are close to the MnSi phase field. Low Mn significantly reduces, but does not eliminate, precipitation in high Ni steels. A comparison of dispersed barrier model predictions with measured hardening data suggests that the Ni-Si dominated precipitates are weaker dislocation obstacles than the G phase type MNSPs. • Nuclear reactor life times are limited by nano precipitates formed under irradiation. • Ion irradiations provide a rapid & affordable way to gain insight into precipitation. • Atom Probe data estimates hardening and embrittlement at lower service dose. • Advanced high Ni steels, with superior unirradiated properties, were investigated. • Simple thermodynamic models are able to predict volume fraction for alloys. [ABSTRACT FROM AUTHOR]