Search

Oxygen-containing carbon materials such as graphene oxide have been extensively studied because of their high dispersibility. However, the oxygen-containing functional groups in most carbon materials are not controlled. Uncontrollability of the synthesis is also one of factors that prevent industrialization. Carbon materials derived from phloroglucinol (PG), which show high solubility/dispersibility and controllability of functional groups, have been developed recently by our group. The high performance of carbonized PG originates from the thermally stable backbone structure of the benzene ring with hydroxy groups of PG. However, the degree of carbonization was low. In this study, five heteropoly acids (HPAs), which are thermally stable homogeneous strong acid catalysts, were used to promote carbonization of PG without losing the controllability of functional groups and the dispersibility. HPAs promoted etherification of hydroxy groups followed by C=C coupling reactions (furan cyclization) at 523 K. Furthermore, it was confirmed that particularly furan structures, which contribute to solubility/dispersibility in solvents, and thermal stability in air, could be maintained at 673 K as suggested by spectroscopies and thermogravimetric-differential thermal analysis. Among five HPAs, phosphotungstic acid worked as the excellent catalyst to promote carbonization of PG containing furan structures, exhibiting high solubility/dispersibility and high thermal stability in air.

Pentagons in carbon materials have attracted attentions because of the potential high chemical reactivity, band gap control, and electrochemical activity. However, it is challenging to prepare a carbon film with high pentagon density because of the curvature and the high reactivity caused by the presence of pentagons, and it is also challenging to estimate the percentage of pentagons in carbon materials because of the limitation of current analytical techniques. In this work, the percentage of pentagons in carbon materials was experimentally estimated for the first time using experimental and calculated C1s X-ray photoelectron spectroscopy and elemental analysis. Carbon films with 7% of pentagons (40% of pentagons compared to the raw material) with electrical resistivity of 1.1 × 104 Ω meter were prepared by heat treatment of corannulene at 873 K. On the other hand, fluoranthene and fullerene remained as non-film solid and powder without forming films at 873 K. Experimental and calculated Raman and IR spectra revealed the peaks of different types of pentagons. Decrement of pentagons in corannulene and fluoranthene heated at high temperatures can be explained mainly by the scission of C=C bond in pentagons, as suggested by the results of reactive molecular dynamics simulation (ReaxFF).

Oxygen-containing carbon materials such as graphene oxide have been studied intensively for a decade because of the high oxygen content, which is beneficial to disperse carbon materials in solutions and to support either metals or metal oxides on carbon materials. However, various oxygen-containing functional groups exist on carbon materials and controlling the structures is almost impossible. In this work, phloroglucinol (PG), which has a symmetrical structure with three hydroxyl groups relative to six aromatic carbon atoms, was found to be the best precursor among PG, cyanuric acid, trimesic acid, and melamine because of the high yield (63 wt%) at 573 K even in an open system which is essential for mass production. The materials synthesized from PG also showed the high dispersibility and/or solubility in solvents (N-methyl-2-pyrrolidone and N,N-dimethylformamide) and the low temperature to form carbon materials (573 K), which can be explained from (002) and (10) in X-ray diffraction pattern. X-ray photoelectron spectroscopy, Fourier transform infrared spectrometer, carbon-13 nuclear magnetic resonance with the aid of calculation of both spectra and carbonization mechanisms revealed that the high solubility of carbonized PG originates from the presence of ether and cyclic ether, which were formed from dehydration of hydroxy groups, and also some remained hydroxyl groups in carbonized PG. Oxygen-containing groups in carbonized PG were effective as an antioxidant. In addition, the coating of carbonized PG on silica nanoparticles imparted conductivity and lubricity to silica nanoparticles.