Search

In this work, PtCo nanoparticles (NPs) on hierarchically ordered mesoporous carbon (PtCo/OMC) are synthesized for polymer electrolyte membrane fuel cells (PEMFCs) aiming to improve the activity and durability of the Pt-based catalyst towards oxygen reduction reaction (ORR). Specifically, the OMC is prepared through a solvent evaporation-induced self-assembly (EISA) method by using a triblock copolymer PEO-PPO-PEO as the structure agent, followed by annealing in the nitrogen atmosphere to decompose the structure agent and to carbonize the carbon precursor. PtCo nanoparticles (NPs) are fabricated with an average diameter of 3.3 nm by H2 reduction and galvanic replacement in an acid solution, and then are uniformly dispersed onto the OMC via impregnation. The typical mesoporous structure of the OMC enhances the uniformly distribution and thermal stability of the small-sized PtCo NPs. The activity and the durability of the as-prepared PtCo/OMC catalyst are investigated by cyclic voltammetry (CV) and single-cell test. In the electrochemical tests, PtCo/OMC exhibits a high ECSA value of 88.56 m2g−1, and a ECSA retention of 77.5% after 5000 CV cycles. The results show that the PtCo/OMC catalyst is more active and more stable than the commercial-carbon-supported PtCo catalyst (PtCo/XC-72). PtCo nanoparticles (NPs) on hierarchically ordered mesoporous carbon (PtCo/OMC) are synthesized aiming to improve the activity and stability of the Pt-based catalyst for the oxygen reduction reaction (ORR). Due to the natural mesoporous and graphite-carbon nanostructure of the OMC, the as-prepared PtCo/OMC catalyst is more active and more stable than the PtCo NPs on the commercial Vulcan@ XC-72 support (PtCo/XC-72), showing great potential in proton exchange membrane fuel cells (PEMFCs).

A series of Ni-modified Mo2C catalysts with La2O3-stabilized ZrO2 supports were synthesized via template method coupled with incipient wetness impregnation and temperature-programmed carbonization. The catalyst was tested in dry reforming of methane (DRM) reaction at the temperature range from 973 to 1173 K in a fixed-bed quartz reactor under atmospheric pressure. XRD, Raman, BET, H2-TPD, SEM, EDS and TEM were conducted to characterize the phase constitution, the pore structure, the morphology and the crystal structure of the catalysts. Ni–Mo2C nanoparticles of ~ 3 nm diameter were obtained for these catalysts, and the La2O3–ZrO2 supports exhibited a cubic lattice structure with a sheet shape, which is believed to contain an abundant of oxygen vacancies. And the synergistic interaction between the oxygen vacancy in La–Zr–O solid solution and the Ni–Mo2C particles could decrease the apparent activation energy of CO2. Both of them are beneficial for accelerating DRM reaction. CH4 conversion of the best specimen catalyst reaches 94% at 1173 K, and the catalyst maintains its stability after 100-h reaction. The superior catalytic activity of NMLZ-7.5 is attributed to the improved BET surface area (33.2 m2/g), smaller crystallites, grain boundaries and oxidation–carbonization cycle of Ni–Mo2C.

This work offers an effective size-controlled synthesis of platinum nanoparticle (Pt NP) arrays for electrocatalyst through self-assembled nanopatterns of block copolymers on titanium (Ti) wafers. Size, spacing and uniformity of Pt NP with loading of Pt to a minimum were investigated to be controlled and adjusted in order to improve the electrochemically active surface area (ECSA) and ECSA stability, and Pt concentration in copolymer/chloroplatinic acid (H2PtCl6) solution was verified to be one of the most important factors to control the arrays’ structure. In our case, the Pt NPs with predictable size of 5–16.5 nm could be obtained when the Pt concentration is larger than 0.05 mg ml−1, which the dominant diameter is proved to be proportional to one-third power of the Pt concentration according to the linear relation of templates’ Pt/N mass ratio versus Pt concentration, and the Pt NPs remain highly ordered arrays with predictable spacing when the Pt concentration is larger than 0.125 mg ml−1. Decrease in Pt concentration from 2 to 0.125 mg ml−1 is an effective method to improve the ECSA and durability simultaneously. The Pt NP arrays exhibit not only a remarkable initial ECSA value of 106.2 m2 g−1, but also a pseudo-zero particle aggregation possibility during 3000-cycle voltammetry, which is attributed to the high Pt NP dispersion and the ordered arrays that improve the Pt utilization and lower the possibility of aggregation.

The spatial distribution of the eutectic M B borides in Fe-Cr-B cast irons was predicted using strain models. The spatial distribution of the eutectic M B borides was revealed by scanning electron microscopy (SEM) using deep-etched specimens. It was shown that the models are helpful for the prediction of mechanical properties, as well as interpretation of mechanical property difference of Fe-Cr-B cast irons. The results show that the models are successful in the prediction of the spatial distribution of the eutectic M B borides.